Wear debris generated by total hip replacements (THRs) may cause mechanical instability, inflammation, osteolysis and ultimately implant loosening, thus limiting the lifetime of such devices [1]. This has led to the development of biocompatible coatings for prostheses. Silicon nitride (SiN) coatings are highly wear resistant and any resultant wear debris are soluble, reducing the possibility of a chronic inflammatory reaction [2]. SiN wear debris produced from coatings have not been characterized Commercial silicon nitride particles of <50nm (Sigma Aldrich) were incubated with formalin fixed sheep synovium at a volume of 0.01mm3 /g of tissue (n=3). The tissue was digested with papain (1.56mg/ml) for 6h and subsequently proteinase K (1mg/ml) overnight. Proteinase K digestion was repeated for 6h and again overnight, after which samples appeared visibly homogeneous [Figure 1]. Samples were then subjected to density gradient ultracentrifugation using sodium polytungstate (SPT) [3]. The resulting protein band was removed from the pellet of particles. Control tissue samples, to which no particles were added, were also subjected to the procedure. Particles were washed with filtered water to remove residual SPT using ultracentrifugation and filtered onto 15nm polycarbonate filters. The filtered particles were imaged by cold field emission scanning electron microscopy (CFE-SEM) and positively identified by elemental analysis before and after the isolation procedure. To validate whether the isolation method affected particle size or morphology, imaging software (imageJ) was used to determine size distributions and morphological parameters of the particles. A Kolmogorov-Smirnov test was used to statistically analyse the particle morphology.Introduction
Methods