Favourable results for collarless polished tapered stems have been reported, and cement creep due to taper slip may be a contributing factor. However, the ideal cement thickness around polished stems remains unknown. We investigated the influence of cement thickness on stem subsidence and cement creep. We cemented six collarless polished tapered (CPT) stems (two stems each of small, medium and large sizes) into composite femurs that had been reamed with a large CPT rasp to achieve various thicknesses of the cement mantle. Two or three tantalum balls were implanted in the proximal cement in each femur. A cyclic loading test was then performed for each stem. The migration of the balls was measured three-dimensionally, using a micro-computed tomography (CT) scanner, before and after loading. A digital displacement gauge was positioned at the stem shoulder, and stem subsidence was measured continuously by the gauge. Final stem subsidence was measured at the balls at the end of each stem.Objectives
Methods
The French paradox regarding cemented femoral components has not been resolved, so we compared the mechanical behavior of a French stem, the CMK stem (Biomet, Warsaw, IN, USA), with a collarless, polished, tapered stem (CPT, Zimmer, Warsaw, IN, USA) using an original biomechanical instrument. Two size-3 CPT stems and two size-302 CMK stems stems were fixed with bone cement into a composite femur soaked in vegetable oil to simulate wet condition. The composite femur was attached to a biomechanical testing instrument after stem implantation, and a 1-Hz dynamic sine wave load (3000 N) was applied to the stems for a total of 1 million cycles. An 8-hour unload period was set after every 16 hours of load. Femur temperature was maintained at 37°C during testing. The femoral canal was prepared for the CPT stems by standard rasping; for the CMK stems, however, the French method was used, in which cancellous bone was removed with a reamer. One CMK stem (CMK-1) was inserted into a femur without collar contact (>2 mm above the calcar), and the other (CMK-2) was inserted into a femur with collar contact. Stem subsidence was measured at the stem shoulder. Compressive force and horizontal cement movement were measured via rods set at the cement–bone interface on the medial, lateral, anterior, and posterior sides of the proximal and distal portions of the composite femurs.Introduction
Materials and Methods
In cemented total hip arthroplasty (THA), proper cement mantle thickness in the femoral canal is still controversial subject. It is widely accepted that the cement mantle around a femoral stem should be at least 2 mm in thickness. But articles from France reported good long-term result with thin cement mantle. It is so called “The French paradox”. We have already reported that the greater compressive force at the cement-bone interface was seen in collarless polished tapered (CPT, Zimmer, USA) stem with thick cement mantle than that with thin cement mantle. However, the stem with thick cement mantle subsided more than with thin mantle. It may have a possibility to cause an early mechanical failure of cemented THA. We compared to stem and cement subsidence in various cement mantles using tantalum ball into cement in this study. A cemented stem model was used for this study with a CPT stem into composite femur. Three sizes of CPT stems (No. 1, No. 2 and No. 3) and one size composite femur were prepared for this study. We inserted two stems for each size, for a total of six stems. Composite femurs were reamed with a No. 3 rasp, and various size of stem was fixed with cement in each composite femur to make a various thicknesses of cement mantle. Two to three tantalum marker balls were injected into the cement in each femur before cement was hardened. 1-Hz dynamic load applied to the stems for half a-million cycles. Each 16 hours of loading was followed by 8 hours without loading. We used micro-CT before and after loading to measure the movement of the tantalum balls in three dimensions. And we analyzed occupation ratio of stem in the femoral canal by computed reconstructed three dimensional model of bone cement and stem.Introduction
Methods
To prevent excessive tension on the posterior cruciate ligament (PCL) in cruciate-retaining total knee arthroplasty (CR-TKA), some knee prosthesis-systems offer the option of creating a posterior slope for the tibial polyethylene insert. Vanguard® Complete Knee System offers two different types of tibial bearing for CR -TKA. CR Lipped Bearing (LB) has a slightly raised posterior lip, whereas CR Standard Bearing (SB) is recessed downward at the posterior margin and has 3° posterior slope. The objective of this study was to investigate the effect of the tibial bearing slope on PCL load using the original devise in vivo conditions. Twenty osteoarthritic varus knees were included in this study. After implantation of the trial components, PCL stiffness was measured using the original tension analyzer intra-operatively. Elastic modulus of PCL was calculated at 90 and 120 degrees knee flexion on two types of bearing surface.Background
Material and Methods