The purpose of this study was to precisely measure the 10-year polyethylene wear rate of primary total hips using Radiostereometric analysis (RSA) comparing Oxidized Zirconium (OxZi) to cobalt chrome (CoCr) femoral heads articulating with highly cross-linked polyethylene (XLPE).

RSA was performed on 46 patients who underwent total hip arthroplasty − 23 who received OxZi femoral heads and 23 who received CoCr heads in combination with XLPE at a minimum of 10 years follow-up. All patients had identical THR systems implanted except for the femoral head utilized. The Centre Index method was utilised to assess total wear rates (from index surgery until final evaluation) using a dedicated RSA Software program (UmRSA Digital Measure v.2.2.1). In addition, the Martell technique was used to subtract head penetration occurring in the first 1–2 years (i.e. bedding-in phase) to allow calculation of the ‘steady state’ wear rates.

There were no significant differences in demographics (i.e age, BMI, gender) between the groups. The average time from surgery of the RSA examinations was 11.7 and 12.6 years for the CoCr and OxZi groups respectively. Using the Centre Index Method to calculate total head penetration, wear rates were slightly higher in the OxZi group (0.048 +/− 0.021mm/year) compared to the CoCr group (0.035 +/− 0.017mm/year) with no statistical difference between the groups (p= 0.02). After correction for the bedding-in period, there was no statistically significant difference in mean ‘steady-state’ wear rate between OxZi (0.031 +/− 0.021mm/year) and CoCr (0.024 +/− 0.019mm/year) at 10 year follow up (p= 0.24). A comparison of preoperative and postoperative SF12, HHS, and WOMAC scores showed no statistical difference between the groups.

RSA demonstrated the 10 year in-vivo wear rates of both bearing combinations to be well below the threshold for osteolysis. There was no significant difference between either the total or ‘steady-state’ wear rates of the OxZi and CoCr groups at 10 years.

Background

There has been a trend in the evolution of total hip arthroplasty towards increased modularity, with this increase in modularity come some potentially harmful consequences. Modularity at the neck shaft junction has been linked to corrosion, adverse reaction to metal debris and pseudotumor formation.

The aim of this retrieval study is to assess whether the surface integrity of the polyethylene (PE) liner is affected by metal wear debris in a single implant design series of THA revised for trunnionosis.

Lewinnek's safe zone recommendation to minimise dislocations was a target of 5–25° for anteversion angle and 30–50° for inclination angle. Subsequently, it was demonstrated that mal-positioning of the acetabular cup can also lead to edge loading, liner fracture, and greater conventional polyethylene wear. The purpose of this study was to measure the effect of acetabular cup position on highly crosslinked polyethylene wear in total hip arthroplasty (THA) at long-term follow-up.

We identified all patients that underwent primary THA with a minimum of 10 years follow-up using an institutional database in London, Ontario, Canada. Patients with a single implant design consisting of a 28 mm cobalt chromium head and highly crosslinked polyethylene liner (ram extruded, GUR 1050, 100 kGy gamma irradiated, remelted, ethylene oxide sterilised) were selected for inclusion. In total, 85 hips from 79 recruited patients were analysed. Patients underwent a supine radiostereometric analysis (RSA) exam in which the x-ray sources and detectors were positioned to obtain an anterior-posterior and cross-table lateral radiograph. Acetabular cup anteversion angle, inclination angle, and 3D penetration rate (including wear and creep) were measured from the stereo radiograph pairs.

At a mean follow-up of 13 years (range, 10–17 years) the mean penetration rate was 0.059 mm/year (95% CI: 0.045 to 0.073 mm/year). Mean anteversion angle was 18.2° (range, −14 to 40°) and mean inclination angle was 43.6° (range, 27 to 61°). With respect to the Lewinnek safe zone, 67% hips met the target for anteversion angle, 77% met the target for inclination angle, and 51% met the target for both. There was no correlation between anteversion angle and penetration rate (r = −0.14, p = 0.72) or between inclination angle and penetration rate (r = 0.11, p = 0.35). There was also no difference (p = 0.07) in penetration rate between hips located within the Lewinnek safe zone for both anteversion angle and inclination angle (mean 0.057 mm/year, 95% CI: 0.036 to 0.079 mm/year) and those outside the safe zone (mean 0.062 mm/year, 95% CI: 0.042 to 0.083 mm/year).

Acetabular cup position had no effect on the wear rate of highly crosslinked polyethylene at long-term follow-up. Although care should still be taken to correctly position the acetabular cup for stability, highly crosslinked polyethylene is a forgiving bearing material that can withstand a wide range of cup positions without negatively impacting longevity due to wear.