Materials and Methods

Medial compartmental osteoarthrosis (OA) patients (13 female and 7 male) were evaluated. Average age, BMI, and Varus deformity were 72.1 years, 26.9, and 12 degrees, respectively.

The newly developed center paddle balancer consists of a built-in spring (Fig. 1). Figure 2 shows the sequence of surgery and measurements. In the surgery, we measured the balance (degrees in Figure 1, A) and distance (mm in Figure 1, B) in extension with a load (Figure 1,C) at transition zone of toe region to linear region. Then, applying the load until flexion gap was the same as that in extension with a patella reduction, we measured the femoral component rotation from the balancer (degrees in Figure 1, A). The anterior and posterior femoral cuts were performed according to measured femoral component rotation which angle is parallel to tibial cut surface.

Materials and Methods

Six acetabulum of 3 matured crossbred pig (average weight: 36 +/− 3.6kg) was retrieved. Animal experiment was performed under the rules of ethical committee of animal experiment. Average diameter of pig acetabulum was 26.3 +/− 0.6 mm. Just after sacrifice, mechanical loading using Instron testing machine with 26mm diameter of Co-Cr in right hip and Ceramic heads in left hip was performed in culture media. Ten thousand cycles of cyclic compression and rotation load (1.5kN to 0.15kN of compression and 12 degrees of rotation) to cartilage was applied at 1Hz (Figure 1).

Culture media was analyzed for protein levels of inflammation related cytokines and amount of HA. Relative quantitative reverse transcriptase-polymerase chain reaction (RT-PCR) from acetabular cartilage was performed as previously reported using specific primer sets for type II collagen, aggrecan, TNF-alpha, Interleukine-1 and 6, and MMP-1, 3, 13.

Materials and methods

The FerVID family (Fujitsu Co. Ltd., Tokyo, Japan) was prepared as the RFID tag. It was radio-resistant below the dose of 50kGy, which allowed gamma sterilization. The RFID tags were embedded into the anterior side of GUR 1050 UHMWPE inserts and 0.3wt% vitamin E blended UHMWPE. The UHMWPE inserts were manufactured by thecompression molding method at the maximum temperature of 220°C and the maximum compressive force of 245kgf/cm². The manufactured inserts were implanted in fresh cadaveric knees. The tibial base plate was made of Ti6Al4V. The femoral components were made of Co-Cr-Mo or Ti-6Al-4V. Communication Performance was measured with the interrogator (DOTR-920 MHz-band, Tohoku Systems Support Co. Ltd., Miyagi, Japan). The transmission output was up to 1W. Received Signal Strength Indicator (RSSI) was measured 500 times at 15 mm away from the surface of skin in the extension and 90° flexion of the knee (Fig1).

Study design

From 1988 to 1991, 122 knees were replaced by Y/SII TKA in 81 patients with rheumatoid arthritis (RA). Among them, 24 joints in 12 patients were examined directly. The average age of follow-up was 19.5 years. The survival rate was investigated according to medical records.

Methods

Clinical outocome of revision TEA that underwent between 2005 and 2013 were evaluated. Causes of revision, implanted revised prosthesis, a clinical score (the Japanese Orthopaedic Association (JOA) elbow assessment score), the arc of motion and complications were investigated. Totally, 6 patients underwent revision TEA. The patients were females with a mean age of 60.4 years (range, 32 to 72).

Materials and Methods

Peek and bioactive PEEK discs (24 mm in diameter and 2 mm in thickness) were prepared. Bioactive PEEk was produced by the combination of 80 vol% Peek powder and 20 vol% CaO-SiO₂ particles (30CaO · 70SiO₂). Discs were sterilized with ethylene oxide gas. The study was approved by the ethics committee in Chiba University. Human osteoblast-like cells were used in the study. The cells at passage 3–5 were used in the experiments. 2 × 10⁵cells /disc were culture at 37°C in a humidified atmosphere with 5% CO₂, and the media was replaced every 3 days. At days 3, 7, 21, the culture media, cells and discs were collected respectively. Cell attachment assay was performed. Cells were seeded at a density of 4 × 10⁵ cells /well and incubated for 2 hours at 37 C in a humidified atmosphere with 5% CO₂. The cells on the discs were evaluated by DNA content. The real-time PCR was performed with regard to type I collagen (COLI), osteocalcin (OC), osteonectin (ON), osteopontin (OPN), and GAPDH. The alkaline phosphatase activity (ALP) was measeured at 3, 7, and 21 days, which samples as used in the DNA-content assay. Alizalin Red Staining was performed at day 21 to quantify calcification deposits in discs. Results were analyzed using Student's t-test with at least three samples. The level of siginificance was set at p=0.05.

Results

The content of DNA showed similar increases on PEEK and bioactive PEEK in the course of day 3, 7, 21. The cell attachment of bioactive PEEK was two times larger than that of PEEK. Real-time PCR results of human osteoblast-like cells cultured on PEEK and bioactive PEEK discs were shown in Fig. 1. There were no significant differences between cells on PEEK and bioactive PEEK with respect to COL I and ON mRNA expression. However, human osteoblast-like cells on bioactive PEEK presented higher expression of OPN and OCN mRNA at day 21. No significant differences were found in ALP activity of both discs. Calcification deposits were observed only on bioactive PEEK at day 21

EXPERIMENTAL METHODS

Three kinds of culture dishes coated with three diffrent fibroin aqueous solutions were prepared: 1 wild-type, 2 transgenic and 3 mixed. The wild-type aqueous solution was prepared from Bombyx mori silkworm cocoons. The transgenic aqueous solution was prepared from Bombyx mori silkworm cocoons in which RGD was interfused in the fibroin light chain³⁾. The mixed aqueous solution was prepared simply by blending RGD peptides with the wild-type fibroin aqueous solution. Chondrocytes were asepically harvested from the joints of 4-week-old Japanese white rabbits and then subcultured on T-flasks and seeded at 2.0 × 10⁵ cells/dish. LIPUS stimulation, with spatial and temporal average intensity of 30 mW/cm² and a frequency of 1.71 MHz with a 200 ms tone burst repeated at 1.0 kHz, was applied to the chondrocytes at 12, 36, 60 hours and administered for 20 minutes each time. GAG production and the number of chondrocytes were measured by the Dimethylmethylene blue (DMMB) method⁴⁾ and the LDH method⁵⁾, respectively. Extracted mRNA from the chondrocytes was analyzed by using the Syber Green method, where the primers were designed for glyceraldehyde-3-phosphate dehydrogenase (GAPDH) as the house-keeping gene, aggrecan and Sox 9. This data was analyzed using the two-sided Student's t-test.