The optimal bearing for hip arthroplasty is still a matter of debate. in younger and more active patients ceramic-on-polyethylene (CoP) bearings are frequently chosen over metal-on-polyethylene (MoP) bearings to reduce wear and increase biocompatibility. However, the fracture risk of ceramic heads is higher than that of metal heads. This can cause serious issue, as ceramic fractures pose a serious complication often necessitating major revision surgery – a complication more frequently seen in ceramic-on-ceramic bearings. To date, there are no long-term data (> 20 years of follow-up) reporting fracture rates of the ceramic femoral heads in CoP bearings. We retrospectively evaluated the clinical and radiographic results of 348 cementless THAs treated with 2nd generation Biolox® Al2O3 Ceramic-on-Polyethylene (CoP) bearings, which had been consecutively implanted between January 1985 and December 1989. At implantation the mean patient age was 57 years. The cohort was subsequently followed for a minimum of 20 years. At the final follow-up 111 patients had died, and 5 were lost to follow-up (Fig. 1). A Kaplan-Meier survivorship analysis was used to estimate the cumulative incidence of ceramic head fractures over the long-term.Introduction
Patients and Methods
Corrosion in modular taper connections of total joint replacement has become a hot topic in the orthopaedic community and failures of modular systems have been reported. The objective of the present study was to determine in vivo titanium ion levels following cementless total hip arthroplasty (THA) using a modular neck system. A consecutive series of 173 patients who underwent cementless modular neck THA and a ceramic on polyethylene bearing was evaluated retrospectively. According to a standardized protocol, titanium ion measurements were performed on 67 patients using high-resolution inductively coupled plasma-mass spectrometry. Ion levels were compared to a control group comprising patients with non-modular titanium implants and to individuals without implants. Although there was a higher range, modular-neck THA (unilateral THA: 3.0 μg/L (0.8–21.0); bilateral THA: 6.0 μg/L (2.0–20.0)) did not result in significant elevated titanium ion levels compared to non-modular THA (unilateral THA: 2.7 μg/L (1.1–7.0), p = 0.821; bilateral THA: 6.2 μg/L, (2.3–8.0), p = 0.638). In the modular-neck THA group, patients with bilateral implants had significantly higher titanium ion levels than patients with an unilateral implant (p < 0.001). Compared to healthy controls (0.9 μg/L (0.1–4.5)), both modular THA (unilateral: p = 0.029; bilateral p = 0.003) and non-modular THA (unilateral: p < 0.001; bilateral: p < 0.001) showed elevated titanium ion levels. The data suggest that the present modular stem system does not result in elevated systemic titanium ion levels in the medium term when compared to non-modular stems. However, more outliner were seen in modular-neck THA. Further longitudinal studies are needed to evaluate the use of systemic titanium ion levels as an objective diagnostic tool to identify THA failure and to monitor patients following revision surgery.