A longitudinal study was done assessing the latest radiographs available in a series of collarless Corail uncemented stems which have reported survival rates of 95% at 20 years. Parameters scored included the degree of “Ghosting” or delamination, the Gruen, the stem fit in the femoral canal and the degree of calcar resorption. Patient and implant demographics were noted.

At 3 years the loosening rate was 23% reaching 64% at 6 years after the index procedure. It was present in all age groups, with a peak in the 24 to 49 year age group. Males and females had the same occurrence. When it was present this was always in zone 1. It was present in 6% of patients in zone 7, but then always associated with zone 1 changes. High and standard off-set stems had the same loosening rates. The looser fit of the stem the higher the incidence of loosening. There was no correlation to the type of bearing surface or the degree of calcar resorption. Those patients with a BMI of 25 – 35 had lower loosening rates compared to those with higher or lower BMI's.

We postulate that cancellous bone on-growth onto the hydroxyapatite coating associated with loading flexural micro-motion leads to hydroxyapatite being pulled off the smooth stem substrate in zone 1. Progressive delamination of the hydroxyapatite then occurs. The triple-tapered design though imparts continued stability.

We report high loosening rates in the Corail stem and suggest a mechanism for its development.

This study reports on ceramic-on-metal (CoM) bearings in total hip replacement. Whole blood metal ion levels were measured. The median increase in chromium and cobalt at 12 months was 0.08 μg/1 and 0.22 μg/1, respectively, in CoM bearings. Comparable values for metal-on-metal (MoM) were 0.48 μg/1 and 0.32 μg/1. The chromium levels were significantly lower in CoM than in MoM bearings (p = 0.02). The cobalt levels were lower, but the difference was not significant. Examination of two explanted ceramic heads revealed areas of thin metal transfer. CoM bearings (one explanted head and acetabular component, one explanted head and new acetabular component, and three new heads and acetabular components) were tested in a hip joint simulator. The explanted head and acetabular component had higher bedding-in. However, after one million cycles all the wear rates were the same and an order of magnitude less than that reported for MoM bearings. There were four outliers in each clinical group, primarily related to component malposition.