Cobalt-Chromium-Molybdenum (CoCr) and Titanium-Aluminium-Vanadium (Ti) alloys are the most commonly used alloys used for Total Hip Replacement due to their excellent biocompatibility and mechanical properties. However, both are susceptible to fretting corrosion In-vivo. The objective of this study was to understand the damage mechanism of both combinations through a sub-surface damage assessment of the alloys at various fretting amplitudes using the Transmission Electron Microscopy (TEM – CM200 FEGTEM). The TEM was used to attain a cross sectional view of the alloys in orderto see the effect of high shear stress on the grain structure. The two combinations were fretted at a maximum contact pressure of 1 GPa in a Ball – on – Plate configuration for displacement amplitudes of 10μm, 25μm, 50μm and 150μm. The contact was lubricated with 25% v/v Foetal Bovine Serum (FBS), diluted with Phosphate Buffered Saline (PBS). The material loss through wear and corrosion from the fretting contact were quantified using the Visual Scanning Interferometry (VSI). The TEM samples were obtained using the Focused Ion Beam (FIB – FEA Nova 200 Nanolab). Samples were obtained from regions of high stress (shaded in red) [Fig. 1] for both CoCr and Ti flat of the CoCr–CoCr and CoCr–Ti couples respectively.Introduction
Methods