In total hip arthroplasty ceramic on ceramic bearing couples are used more and more frequently and on a wordwide basis. The main reason of this choice is reduction of wear debris and osteolysis. The tribological properties and the mechanical behaviour of the implanted ceramic must remain the same throughout the patient's life. The aim of this study was to evaluate the resistance of Alumina Matrix Composite to environmental degradation. The alumina matrix composite or BIOLOX ® delta is manufactured in Germany by CeramTec. It is made up of 80 vol.% Al2O3, 17 vol.% Yttria Stabilized ZrO2 and 3vol.% strontium aluminate platelets. The zirconia grains account for 1.3 mol.% of the Yttria content. Accelerated aging tests in water steam at 142°C, 134°C, 121°C, and 105°C were performed to evaluate the aging kinetics of the composite. X-ray diffraction was used to determine the monoclinic phase content on the material surface. Phase transformation is associated with weakness and increase in roughness of zirconia ceramic implants.Introduction
Material and method