Four highly cross-linked UHWMPEs except vitamin E-stabilised explants The development of both first and second generation highly cross-linked material focused on stabilizing radiation-induced free radicals as the sole precursor to oxidative degradation; however, secondary in vivo oxidation mechanisms have been identified in both conventional and highly cross-linked UHMWPE, induced by absorbed lipids and cyclic mechanical load. Retrieval studies are reporting in vivo oxidation highly cross-linked retrievals with up to ten year in vivo durations. Preclinical aging tests did not predict these in vivo material changes. With only a decade of these materials in clinical use, retrieval studies are limited to mid-term follow-up. In vitro studies face a challenge in effectively replicating the precise in vivo conditions that lead to this loss of oxidation resistance. In this study, we bypass replicating these in vivo variables by examining surgically-retrieved components, thereby testing material that has been affectively “pre-conditioned” by their in vivo service. After a preliminary post-operative analysis, we subjected retrievals to accelerated aging tests in order to predict the extent to which their oxidative stability had been uniquely compromised in vivo.Summary
Introduction
We analysed impaction bone grafting used together with cemented or uncemented fixation in acetabular revision surgery. The overall risk for re-revision did not differ between the cemented and uncemented group. However, aseptic loosening was more common in the cemented group. Several surgical techniques address bone defects in cup revision surgery. Bone impaction grafting, introduced more than thirty years ago, is a biologically and mechanically appealing method. The primary aim of this study was to evaluate the effect of bone impaction grafting when used with uncemented and cemented fixation in cup revision surgery. Uncemented cups resting on more than 50% host bone were used as controls.Summary Statement
Background
Sequentially irradiated and annealed UHMWPE hip and knee retrievals showed subsurface Highly cross-linked polyethylene was developed to improve the wear resistance of UHMWPE bearing surfaces in total hip arthroplasty. First generation irradiated and annealed polyethylene showed high oxidation Summary
Introduction
We revised 24 consecutive hips with loosening of the femoral stem using impaction allograft and a cemented stem with an unpolished proximal surface. Repeated radiostereometric examinations for up to two years showed a slow rate of subsidence with a mean of 0.32 mm (−2.0 to +0.31). Fifteen cases followed for a further year showed the same mean subsidence after three years, indicating stabilisation. A tendency to retroversion of the stems was noted between the operation and the last follow-up. Retroversion was also recorded when displacement of the stem was studied in ten of the patients after two years. Repeated determination of bone mineral density showed an initial loss after six months, followed by recovery to the postoperative level at two years. Defects in the cement mantle and malalignment of the stem were often noted on postoperative radiographs, but did not correlate with the degrees of migration or displacement. After one year, increasing frequency of trabecular remodelling or resorption of the graft was observed in the greater trochanter and distal to the tip of the stem. Cortical repair was noted distally and medially (Gruen regions 3, 5 and 6). Migration of the stems was the lowest reported to date, which we attribute to the improved grafting technique and to the hardness of the graft.