There is considerable interest in the orthopaedic community in understanding the multifactorial process of taper fretting corrosion in total hip arthroplasty (THA). Previous studies have identified some patient and device factors associated with taper damage, including length of implantation, stem flexural rigidity, and head offset. Due to the complexity of this phenomenon, we approached the topic by developing a series of matched cohort studies, each attempting to isolate a single implant design variable, while controlling for confounding factors to the extent possible. We also developed a validated method for measuring material loss in retrieved orthopaedic tapers, which contributed to the creation of a new international standard (ASTM F3129-16). Based on our implant retrieval collection of over 3,000 THAs, we developed independent matched cohort studies to examine (1) the effect of femoral head material (metal vs. ceramic, n=50 per cohort) and (2) stem taper surface finish (smooth vs. microgrooved, n=60 per cohort). Within each individual study, we adjusted for confounding factors by balancing implantation time, stem taper flexural rigidity, offset, and, when possible, head size. We evaluated fretting and corrosion using a four-point semiquantitative score. We also used an out-of-roundness machine (Talyrond 585) to quantify the material loss from the tapers. This method was validated in a series of experiments of controlled material removal on never-implanted components.Introduction
Methods
Previous studies of long-term CoCr alloy femoral components for TKA have identified 3rd body abrasive wear and inflammatory cell induced corrosion (ICIC). The extent of femoral condyle surface damage in contemporary CoCr femoral components is currently unclear. The purpose of this study was to investigate the prevalence and morphology of damage (3rd body scratches and ICIC) at the bearing surface in retrieved TKA femoral components from contemporary designs. 308 CoCr femoral TKA components were collected as part of an ongoing, multi-institutional orthopedic implant retrieval program. The collection included contemporary designs from Stryker (Triathlon n=48, NRG n=10, Scorpio n=31), Depuy Synthes (PFC n=27) and Zimmer (NexGen n=140, Persona n=1) and Biomet (Vanguard n=51). Hinged knee designs and unicondylar knee designs were excluded. Components were split into groups based on implantation time: short-term (1–3y, n=134), intermediate-term (3–5y, n=73) and long-term (6–15y, n=101). Each grouping was mainly revised for instability, infection and loosening. Third-body abrasive wear of CoCr was evaluated using a semi-quantitative scoring method similar to the Hood method (Figure 1). A score of 1 had minimal damage and a score of 4 corresponded to damage covering more than 50% of the evaluated area. ICIC damage was reported as location of affected area. A white light interferometer (Zygo New View 5000) was also used to analyze the topography of severe damage of the bearing surface. For this analysis, three representative components from each cohort were selected and analyzed in three locations on the apex of the bearing surface. We analyzed the following roughness parameters: Ra, Rsk, and Rku.Introduction
Methods
In total joint replacement devices, material loss from the taper junctions is a clinical concern. Previous studies of explanted orthopedic devices have relied on visual scoring methods to quantify the fretting-corrosion damage on the component interfaces. Previous research has shown that visual fretting-corrosion evaluation is correlated to the volume of material loss [1], but scoring is semi-qualitative and does not provide a quantitative measure of the amount of material removed from the surface. The purpose of this study was to develop and validate a quantitative method for measuring the volume of material lost from the surfaces of explanted devices at the taper-trunnion junction. 10 new exemplar taper adapter sleeves (Ceramtec, Plochingen, Germany) were used for method validation. By using exemplar devices we were able to create clinically realistic taper damage in a controlled and repeatable manner using machining tools. Taper surfaces were measured before and after in vitro material removal using a roundness machine (Talyrond 585, Taylor Hobson, UK). Axial traces were measured on each taper surface using a diamond stylus. The mass of artificially removed material was also measured gravimetrically using a microgram balance (Sartorius, CPA225D, accuracy = ± 0.00003g). Surface profiles were analyzed using a custom MatLab script and Talymap software was used to provide 3D visualizations of the pattern of material loss. Calculated volumetric material loss was compared to the gravimetric value. A sensitivity analysis was conducted to determine the optimum number of traces to characterize the material loss from taper junctions.Introduction
Methods
Recent implant design trends have renewed concerns regarding metal wear debris release from modular connections in THA. Previous studies regarding modular head-neck taper corrosion were largely based on cobalt chrome (CoCr) alloy femoral heads. Comparatively little is known about head-neck taper corrosion with ceramic femoral heads or about how taper angle clearance influences taper corrosion. This study addressed the following research questions: 1) Could ceramic heads mitigate electrochemical processes of taper corrosion compared to CoCr heads? 2) Which factors influence stem taper corrosion with ceramic heads? 3) What is the influence of taper angle clearance on taper corrosion in THA? 100 femoral head-stem pairs were analyzed for evidence of fretting and corrosion. A matched cohort design was employed in which 50 ceramic head-stem pairs were matched with 50 CoCr head-stem pairs based on implantation time, lateral offset, stem design and flexural rigidity. Fretting corrosion was assessed using a semi-quantitative scoring scale where a score of 1 was given for little to no damage and a score of 4 was given for severe fretting corrosion. The head and trunnion taper angles were measured using a roundness machine (Talyrond 585, Taylor Hobson, UK). Taper angle clearance is defined as the difference between the head and trunnion taper angles.Introduction
Methods
The release of metal debris and ions has raised concerns in joint arthroplasty. In THA metal debris and ions can be generated by wear of metal-on-metal bearing surfaces and corrosion at modular taper interfaces, currently understood to be mechanically assisted crevice corrosion (MACC) [1]. More recently, inflammatory-cell induced corrosion (ICIC) has been identified as a possible source of metal debris and/or ions [2]. Although MACC has been shown to occur at modular junctions in TKA, little is known about the prevalence of other sources. The purpose of this study was to determine the sources of metallic debris and ion release in long-term implanted (in vivo > 15y) TKA femoral components. Specific attention was paid to instances of ICIC as well as damage at the implant-bone interface. 1873 retrieved TKA components were collected from 2002–2013 as part of a multi-center, IRB-approved retrieval program. Of these, 52 CoCr femoral condyles were identified as long term TKA (Average: 17.9±2.8y). These components were predominantly revised for loosening, PE wear and instability. 40/52 of the components were primary surgeries. Components were examined using optical microscopy to confirm the presence of 5 damage mechanisms (polyethylene failure, MACC corrosion of modular tapers, corrosion damage between cement and backside, third-body wear, and ICIC). Third-body wear was evaluated using a semi-quantitative scoring method based on the percentage of damaged area. A score of 1 had minimal damage and a score of 4 corresponded to severe damage. Polyethylene components were scored using the Hood method and CoCr components were scored similarly to quantify metal wear. The total area damaged by ICIC was quantified using photogrammetry. Images were taken using a digital SLR with a calibrated ruler in the same focal plane. Using known pixel dimensions, the ICIC damaged area was calculated.Introduction
Methods
Previous studies regarding modular head-neck taper corrosion were largely based on cobalt chrome (CoCr) alloy femoral heads. Less is known about head-neck taper corrosion with ceramic femoral heads. We asked (1) whether ceramic heads resulted in less taper corrosion than CoCr heads; (2) what device and patient factors influence taper fretting corrosion; and (3) whether the mechanism of taper fretting corrosion in ceramic heads differs from that in CoCr heads.Background:
Questions/purposes:
Sequentially annealed highly crosslinked polyethylenes (HXLPEs) were introduced in total knee replacement (TKR) starting in 2005 to reduce wear and particle-induced osteolysis. Few studies have reported on the clinical performance of HXLPE knees. In this study, we hypothesized that due to the reduced free radicals, sequentially annealed HXLPE would have lower oxidation levels than gamma inert-sterilized controls. 145 tibial components were retrieved at consecutive revision surgeries at 7 different surgical centers. 74 components were identified as sequentially annealed HXLPE (X3, Stryker) while the remainder (n = 71) were conventional gamma inert sterilized polyethylene. The sterilization method was confirmed by tracing the lot numbers by the manufacturer. The conventional inserts were implanted for 1.7 years (Range: 0.0–9.3 years), while the X3 components were implanted 1.1 years (Range: 0.0–4.5 years). Surface damage was assessed using the Hood method. Oxidation analysis was performed in accordance with ASTM 2102 following submersion in boiling heptane for 6 hours to remove absorbed lipids. 30 of the conventional and 29 of the HXLPE inserts were available for oxidation analysis.Introduction
Methods