This study reports the ten-year wear rates, incidence of osteolysis, clinical outcomes, and complications of a multicentre randomized controlled trial comparing oxidized zirconium (OxZr) versus cobalt-chrome (CoCr) femoral heads with ultra-high molecular weight polyethylene (UHMWPE) and highly cross-linked polyethylene (XLPE) liners in total hip arthroplasty (THA).

This study reports the ten-year polyethylene liner wear rates, incidence of osteolysis, clinical outcomes and complications of a three-arm, multicentre randomised controlled trial comparing Cobalt-Chrome (CoCr) and Oxidised Zirconium (OxZr) femoral heads with ultra-high molecular weight polyethylene (UHMWPE) versus highly cross-linked polyethylene (XLPE) liners in total hip arthroplasty (THA).

Patients undergoing THA from four institutions were prospectively randomised into three groups. Group A received a CoCr femoral head and XLPE liner; Group B received an OxZr femoral head and XLPE liner; and Group C received an OxZr femoral head and UHMWPE liner. Blinded observers recorded predefined outcomes in 262 study patients at regular intervals for ten years following THA.

At ten years follow-up, increased linear wear rates were recorded in group C compared to group A (0.133 ± 0.21 mm/yr vs 0.031 ± 0.07 mm/yr respectively, p<0.001) and group B (0.133 ± 0.21 mm/yr vs 0.022 ± 0.05 mm/yr respectively, p<0.001). Patients in group C were associated with increased risk of osteolysis and aseptic loosening requiring revision surgery compared with group A (7/133 vs 0/133 respectively, p=0.007) and group B (7/133 vs 0/135 respectively, p=0.007). There was a non-significant trend towards increased liner wear rates in group A compared to group B (0.031 ± 0.07 mm/yr vs 0.022 ± 0.05 mm/yr respectively, p=0.128). All three groups were statistically comparable preoperatively and at ten years follow-up when measuring normalised Western Ontario and McMaster Universities Osteoarthritis Index(p=0.410), short-form-36 (p = 0.465 mental, p = 0.713 physical), and pain scale scores (p=0.451).

The use of UHMWPE was associated with progressively increased annual liner wear rates after THA. At ten years follow-up, this translated to UHMWPE leading to an increased incidence of osteolysis and aseptic loosening requiring revision THA, compared with XLPE. Femoral heads composed of OxZr were associated with a non-significant trend towards reduced wear rates compared to CoCr, but this did not translate to any differences in osteolysis, functional outcomes, or revision surgery between the two treatments groups.

This study reports the ten-year outcomes of a three-arm, multicentre randomised controlled trial comparing Cobalt-Chrome (CoCr) and Oxidised Zirconium (OxZr) femoral heads with ultra-high molecular weight polyethylene (UHMWPE) versus highly cross-linked polyethylene (XLPE) liners in total hip arthroplasty (THA).

Patients undergoing THA from four institutions were prospectively randomised into three groups. Group A received a CoCr femoral head and XLPE liner; Group B received an OxZr femoral head and XLPE liner; and Group C received an OxZr femoral head and UHMWPE liner. The outcomes of 262 study patients were analysed at ten years follow-up.

At ten years, increased linear wear rates were recorded in group C compared to group A (0.133 ± 0.21 mm/yr vs 0.031 ± 0.07 mm/yr respectively, p<0.001) and group B (0.133 ± 0.21 mm/yr vs 0.022 ± 0.05 mm/yr respectively, p<0.001). Patients in group C had increased risk of osteolysis and aseptic loosening requiring revision surgery compared with group A (7/133 vs 0/133 respectively, p=0.007) and group B (7/133 vs 0/135 respectively, p=0.007). There was a non- significant trend towards increased liner wear rates in group A compared to group B (0.031 ± 0.07 mm/yr vs 0.022 ± 0.05 mm/yr respectively, p=0.128). All three groups were statistically comparable preoperatively and at ten years follow-up from a clinical score perspective.

The use of UHMWPE was associated with progressively increased annual liner wear rates. At ten years follow-up, this translated to an increased incidence of osteolysis and aseptic loosening requiring revision, compared with XLPE. Femoral heads composed of OxZr were associated with a non-significant trend towards reduced wear rates compared to CoCr, but this did not translate to any differences in osteolysis, functional outcomes, or revision surgery between the two treatments groups.

Oxidised zirconium (OxZi) has been developed as an alternative bearing surface for femoral heads in total hip arthroplasty (THA). This study has investigated polyethylene wear, functional outcomes and complications, comparing OxZi and cobalt–chrome (CoCr) as part of a three-arm, multicentre randomised controlled trial. Patients undergoing THA from four institutions were prospectively randomised into three groups. Group A received a CoCr femoral head and highly cross-linked polyethylene (XLPE) liner; Group B received an OxZi femoral head and XLPE liner; Group C received an OxZi femoral head and ultra-high molecular weight polyethylene (UHMWPE) liner. At five years, 368 patients had no statistically significant differences in short-form-36 (p = 0.176 mental, p = 0.756 physical), Western Ontario and McMaster Universities Osteoarthritis Index (p = 0.847), pain scores (p = 0.458) or complications. The mean rate of linear wear was 0.028 mm/year (standard deviation (sd) 0.010) for Group A, 0.023 mm/year (sd 0.010) for Group B, and 0.09 mm/year (sd 0.045) for Group C. Penetration was significantly higher in the UHMWPE liner group compared with both XLPE liner groups (p < 0.001) but no significant difference was noted between CoCr and OxZi when articulating with XLPE (p = 0.153). In this, the largest randomised study of this bearing surface, it appears that using a XLPE acetabular liner is more important in reducing THA component wear than the choice of femoral head bearing, at mid-term follow-up. There is a non-significant trend towards lower wear, coupling OxZi rather than CoCr with XLPE but long-term analysis is required to see if this observation changes with time and becomes significant.