Previous studies have highlighted differences in the risk of periprosthetic fracture between tapered slip (TS) and composite beam (CB) stems. This biomechanical study explored periprosthetic fractures around these stems and the effect of adding a 16-gauge calcar or diaphyseal wire to TS stems on their resistance to torque.

A power analysis determined a sample size of 7 specimens per group, assuming a standard deviation of 14.8 Nm in peak torque, to provide 90% power to detect a difference of at least 30 Nm between groups. Twenty-one TS stems (eight alone, six with calcar wiring, seven with diaphyseal wiring placed 2 cm distal to the lesser trochanter) and seven CB stems were cemented into standard Sawbones. A servo-hydraulic test machine applied a 1000 N load with a 1-degree rotation per second until failure. The peak torque at failure was measured, and the fracture location recorded. Comparisons were performed using two-sample t-tests.

CB stems exhibited a significantly higher peak torque at failure (205.3 Nm) than TS stems (159.5 Nm, p=0.020). Calcar-wire-TS (148.2 Nm, p=0.036) and diaphyseal-wire-TS (164.9 Nm, p=0.036) were both weaker than CB stems. Wired-TS stems showed no significant difference from non-wired-TS stems. Additionally, the study could not conclude that calcar wiring is stronger than diaphyseal wiring. All TS fractures occurred at the mid-stem, simulating a B-type fracture, while the addition of the diaphyseal wire shifted the fracture location more distally in four of seven stems (p=0.0699).

This biomechanical study supports the clinical evidence that CB stems have stronger resistance to torque than TS stems and may explain lower risk of periprosthetic fracture. The addition of calcar or diaphyseal wires to TS stems resulted in no significant changes in peak torque to fracture. In patients at high risk of periprosthetic fracture, CB cemented stems should be considered.