Osteoarthritis (OA) occurs due to a multi-scale degradation of articular cartilage (AC) surface which aggravates the disease condition. Investigating the micro-scale structural alterations and mechano-tribological properties facilitates comprehension of disease-mechanisms to improve future injectable-therapies. This study aims to analyze these properties using various experimental and analytical methods to establish correlations between their morpho-physiological features. In this study, Raman-spectroscopy was used to investigate microscale changes in AC constituents and categorize OA damage regions in knee-joint samples from joint replacement patients (Samples = 5 and Regions = 40). Following, microscale indentation and sliding tests were performed on these regions to evaluate variations in aggregate-modulus (AM) and elastic-modulus (EM), with coefficient of friction (COF). Finally, scanning electron microscopy (SEM) was employed to analyze these morphological variations.Introduction
Method
It is believed that wear of replacement joints A five active degree of freedom (DOF) spine simulator was used to compare the effects of varying the kinematic and loading input parameters on a ProDisc-L TDR (Synthes Spine). A four DOF standard ISO (ISO18192-1) test was followed by a five DOF test which included the AP shear force. The standard ISO test was repeated on a second simulator (of identical design) but with the phasing of the lateral bend (LB) and flexion extension (FE) motions changed to be in-phase, creating a low cross-shear motion pattern. The standard ISO test was then modified to give half the ISO standard axial loading. All tests conducted were based on the ISO18192-1 standard for lumbar implants with 15 g/l protein lubricant and modified as described. Gravimetric wear measurements were taken every million cycles (mc) in units of milligrams (mg). Six discs were tested to give statistically significant results.Introduction
Methods
The direction of wear in the acetabular socket has implications for the amount of debris that is generated during movement, for the magnitude of eccentric loading and for the incidence of impingement of the neck. We observed the direction of penetration with respect to a global co-ordinate system in 84 acetabular components retrieved at reoperation. The mean direction of wear relative to the open face of the sockets was found to be 37° with a range from 0° to 87°. For those values determined using the inclination of the socket on the prerevision radiograph, the mean direction of penetration in the coronal plane had a lateral, rather than a medial, component. The mean angle was 84° (SD 17°) with respect to the horizontal. The angle of penetration was found to correlate significantly with the depth, in that the lateral component became larger as the wear progressed. There was also a significant correlation between the rate of penetration and the direction of wear. Despite the theoretical advantage of penetration in the superolateral direction, i.e., along the margin of the socket, in reducing the probability of impingement of the neck, no significant correlation was seen between the angle of penetration and the period of use in vivo. This may suggest that impingement of the femoral neck on the rim of the socket may not be the dominant factor in loosening of the socket but can still be important in a few cases.