Femoral neck narrowing (NN) following Metal-on-Metal Hip Resurfacing Arthroplasty (MoMHRA) is a well-recognised clinical phenomenon. The incidence of resurfaced hips with NN > 10% is reported to be up to 27%. Its pathogenesis is thought to be multi-factorial secondary to stress shielding, impingement, osteolysis secondary to wear/ion particles and as a result of reduced vascularity and pressure effect on cancellous bone secondary to the presence of a soft-tissue mass around the resurfaced hip. Recognised risk factors for its development include: female gender and the presence of a pseudotumour. Serum Chromium (Cr) and Cobalt (Co) are recognised surrogate markers of in-vivo wear of MoMHRA. The aims of this study were to establish whether NN is associated with increased wear. A cohort of 214 patients with unilateral MoMHRA (139M: 75F) was included in this study. Primary osteoarthritis was the diagnosis leading to surgery for the majority of patients (208). The average age at surgery was 54.1 years old (13–73). Six different implants were used; BHR (116), Conserve plus (92), Recap (2), ASR (2), Adept (1) and Cormet (1). The average femoral component size was 49.2mm (range: 38–59). The average follow up was 4.3 years (range: 2–10). Patients were subdivided into 3 groups as per implant size. Small size component group had implants <45mm, average size group had components 45–51mm and large component size group had components >51mm. All patients had Prosthesis-Junction-Ratio (PJR) measured from postoperative (PJRpost) and at latest follow up (PJRfollow) radiographs. Measurements were made using the method described by Lilikakis1. Metal ion levels (Cr/Co) were measured at last follow-up for all patients. Cr level >5.1g/ml and Co levels >4.4 g/ml were considered high2 and patients with such levels formed the high ion group.INTRODUCTION
METHODS
Although simulation studies have shown superior wear properties of metal-on-metal articulations, increased concern exists regarding the excess in-vivo wear of a small number of Metal-on-Metal-Hip-Resurfacing (MoMHRA) implants. Serum ion levels of Chromium (Cr) and Cobalt (Co) are surrogate markers of wear. Risk factors associated with increased wear include female gender, small components, dysplasia, cup orientation outside safe zone and femoral head downsize during surgery with an associated decrease in Head-Neck-Ratio (HNR). However, these factors are interlinked. This study aims to identify the factors that are most important for subsequent wear of MoMHRA, by performing a multivariate analysis. 206 patients (124M: 82F) with unilateral MoMHRA were included in this study. The average follow up was 3.3 years. All patients had Cr/Co levels measured at follow up. Inclination and anteversion of each cup were measured using EBRA. Cups were analysed as being within or outside the previously defined optimum-zone. HNR measurements were made from pre-operative (HNRpre) and post-operative (HNRpost) radiographs. The immediate changes in HNR (downsize/upsize of femoral head) as a result of the operation were expressed as: HNRprepost=HNRpost–HNRpre Multivariate linear regression modelling was used to explore the association between measures of ions with the following predictor variables (gender, age, diagnosis, femoral component size, orientation of the acetabular component, head/neck ratio and position of femoral stem). Analyses were carried out separately for each outcome (Cr and Co). Classification and Regression Tree (CART) models were fitted as a complimentary approach to regression modelling.INTRODUCTION
METHODS