Surgeons have commonly used modular femoral heads and stems from
different manufacturers, although this is not recommended by orthopaedic
companies due to the different manufacturing processes. We compared the rate of corrosion and rate of wear at the trunnion/head
taper junction in two groups of retrieved hips; those with mixed
manufacturers (MM) and those from the same manufacturer (SM). We identified 151 retrieved hips with large-diameter cobalt-chromium
heads; 51 of two designs that had been paired with stems from different
manufacturers (MM) and 100 of seven designs paired with stems from
the same manufacturer (SM). We determined the severity of corrosion
with the Goldberg corrosion score and the volume of material loss
at the head/stem junction. We used multivariable statistical analysis
to determine if there was a significant difference between the two
groups. Aims
Materials and Methods
The long term biological effects of wear products
following total hip arthroplasty (THA) are unclear. However, the indications
for THA are expanding, with increasingly younger patients undergoing
the procedure. This prospective, randomised study compared two groups of patients
undergoing THA after being randomised to receive one of two different
bearing surfaces: metal-on-polyethylene (MoP) n = 22 and metal-on-metal
(MoM) n = 23. We investigated the relationship between three variables:
bearing surface (MoP Our results demonstrated significantly higher mean cobalt and
chromium (Co and Cr) blood levels in the MoM group at all follow-up
points following surgery (p <
0.01), but there were no significant
differences in the chromosomal aberration indices between MoM and
MoP at two or five years (two years: p = 0.56, p = 0.08, p = 0.91, p
= 0.51 and five years: p = 0.086, p = 0.73, p = 0.06, p = 0.34)
for translocations, breaks, loss and gain of chromosomes respectively.
Regression analysis showed a strong linear relationship between
Cr levels and the total chromosomal aberration indices in the MoM
group (R2 = 0.90016), but this was not as strong for
Co (R2 = 0.68991). In the MoP group, the analysis revealed
a poor relationship between Cr levels and the total chromosomal
aberration indices (R2 = 0.23908) but a slightly stronger
relationship for Co (R2 = 0.64292). Across both groups,
Spearman’s correlation detected no overall association between Co and Cr
levels and each of the studied chromosomal aberrations. There remains
no clear indication which THA bearing couple is the most biocompatible,
especially in young active patients. While THA continues to be very
successful at alleviating pain and restoring function, the long-term
biological implications of the procedure still require further scrutiny. Cite this article: