A damaged vertebral body can exhibit accelerated ‘creep’ under constant load, leading to progressive vertebral deformity. However, the risk of this happening is not easy to predict in clinical practice. The present cadaveric study aimed to identify morphometric measurements in a damaged vertebral body that can predict a susceptibility to accelerated creep. Mechanical testing of 28 human spinal motion segments (three vertebrae and intervening soft tissues) showed how the rate of creep of a damaged vertebral body increases with increasing “damage intensity” in its trabecular bone. Damage intensity was calculated from vertebral body residual strain following initial compressive overload. The calculations used additional data from 27 small samples of vertebral trabecular bone, which examined the relationship between trabecular bone damage intensity and residual strain.Abstract
Objectives
Methods
Osteoporotic vertebral fractures can cause severe vertebral wedging and kyphotic deformity. This study tested the hypothesis that kyphoplasty restores vertebral height, shape and mechanical function to a greater extent than vertebroplasty following severe wedge fractures. Pairs of thoracolumbar “motion segments” from seventeen cadavers (70–97 yrs) were compressed to failure in moderate flexion and then cyclically loaded to create severe wedge deformity. One of each pair underwent vertebroplasty and the other kyphoplasty. Specimens were then creep loaded at 1.0kN for 1 hour. At each stage of the experiment the following parameters were measured: vertebral height and wedge angle from radiographs, motion segment compressive stiffness, and stress distributions within the intervertebral discs. The latter indicated intra-discal pressure (IDP) and neural arch load-bearing (FN).Introduction
Methods
Vertebroplasty helps to restore mechanical function to a fractured vertebra. We investigated how the Nine pairs of three-vertebra cadaver spine specimens (aged 67–90 yr) were compressed to induce fracture. One of each pair underwent vertebroplasty with PMMA, the other with a resin (Cortoss). Specimens were then creep-loaded at 1.0kN for 1hr. Before and after vertebroplasty, compressive stiffness was determined, and stress profilometry was performed by pulling a pressure-transducer through each disc whilst under 1.0kN load. Profiles indicated intradiscal pressure (IDP) and compressive load-bearing by the neural arch (FN) at both disc levels. Micro-CT was used to quantify cement fill in the anterior and posterior halves of each augmented vertebral body, and also in the region immediately adjacent to the fractured endplateIntroduction
Methods
Fracture of an osteoporotic vertebral body reduces vertebral stiffness and decompresses the nucleus in the adjacent intervertebral disc. This leads to high compressive stresses acting on the annulus and neural arch. Altered load-sharing at the fractured level may influence loading of neighbouring vertebrae, increasing the risk of a fracture ‘cascade’. Vertebroplasty has been shown to normalise load-bearing by fractured vertebrae but it may increase the risk of adjacent level fracture. The aim of this study was to determine the effects of fracture and subsequent vertebroplasty on the loading of neighbouring (non-augmented) vertebrae. Fourteen pairs of three-vertebra cadaver spine specimens (67-92 yr) were loaded to induce fracture. One of each pair underwent vertebroplasty with PMMA, the other with a resin (Cortoss). Specimens were then creep loaded at 1.0kN for 1hr. In 17 specimens where the upper or lower vertebra fractured, compressive stress distributions were measured in the disc between adjacent non-fractured vertebrae by pulling a pressure transducer through the disc whilst under 1.0kN load. These ‘stress profiles’ were obtained at each stage of the experiment (in flexion and extension) in order to quantify intradiscal pressure (IDP), the size of stress concentrations in the posterior annulus (SP) and compressive load-bearing by anterior (FA) and posterior (FP) halves of the vertebral body and by the neural arch (FN).Background
Methods
Vertebral osteoporotic fracture increases both elastic and time-dependent ('creep') deformations of the fractured vertebral body during subsequent loading. The accelerated rate of creep deformation is especially marked in central and anterior regions of the vertebral body where bone mineral density is lowest. In life, subsequent loading of damaged vertebrae may cause anterior wedging of the vertebral body which could contribute to the development of kyphotic deformity. The aim of this study was to determine whether gradual creep deformations of damaged vertebrae can be reduced by vertebroplasty. Fourteen pairs of spine specimens, each comprising three vertebrae and the intervening soft tissue, were obtained from cadavers aged 67-92 yr. Specimens were loaded in combined bending and compression until one of the vertebral bodies was damaged. Damaged vertebrae were then augmented so that one of each pair underwent vertebroplasty with polymethylmethacrylate cement, the other with a resin (Cortoss). A 1kN compressive force was applied for 1 hr before fracture, after fracture, and after vertebroplasty, while creep deformation was measured in anterior, middle and posterior regions of each vertebral body, using a MacReflex optical tracking system.Introduction
Methods