Utilization of reverse total shoulder arthroplasty (RTSA) has steadily increased since its 2003 introduction in the American market. Although RTSA was originally indicated for elderly, low demand patients, it is now being increasingly used to treat rotator cuff arthropathy, humeral fractures, neoplasms and failed total and hemi shoulder arthroplasty. There is, therefore, a growing interest in bearing surface wear of RTSA polyethylene humeral liners. In the current study, we examined humeral liners retrieved as part of an IRB approved study to determine the amount of bearing surface wear. We hypothesized that wear of the bearing surface by intentional contact with the glenosphere (mode I) would be minor compared to that produced by scapular notching and impingement of the humeral liner (mode II).

Twenty-three retrieved humeral liners were retrieved at revision surgery after an average of 1.5 years implantation time. The average age at implantation was 68 years (range 50–85). Shoulders were revised for loosening (7), instability (6), infection (6), pain (2), and other/unknown reasons (2). The liners were scanned using microCT at a resolution of 50 µm and then registered against unworn surfaces to estimate the bearing surface wear depth. The depth of surface penetration due to impingement of the liner with surrounding structures was measured and the location of the deepest penetration was noted.

Mode I wear of the bearing surface was detectable for five of the retrieved liners. The penetration depth was 100 µm or less for four of the liners and approximately 250 microns for the fifth liner. It was noted that the liners with discernable mode I wear were those with longer implantation times (average 2.4 years). Material loss and abrasion of the rim due to mode II wear was noted with measurable penetration in 18 of the liners. Mode II wear penetrated to the bearing surface in 11 liners. It was generally noted that volumetric material loss was dominated by mode II wear (Figure 1).

In this study of short to medium term retrieved RTSA humeral liners, mode I wear of the bearing surface was a minor source of material loss. Mode II wear due to scapular notching or impingement of the rim was the dominant source of volumetric wear. This is in agreement with a previous study that we have performed on a smaller cohort of seven liners. It is noteworthy that we were able to detect measurable mode I wear for liners with moderate implantation times. The quantity of bearing surface wear that will be seen in long term retrievals remains unknown at this time.

INTRODUCTION

Retrieval analysis is an important aspect of medical device development. Examination of retrieved devices allows device developers to close the design loop, understand the performance of devices, and validate assumptions made and methods used during preclinical testing. We provide an overview of the implant retrieval analysis performed at the Implant Research Center at Drexel University on reverse total shoulder systems retrieved after short to medium term implantation.