The treatment of infected nonunions is difficult. Antibiotic cement-coated (ACC) rods provide stability as well as delivering antibiotics. We conducted a review of 110 infected nonunions treated with ACC rods. Patients were divided into two groups: group A (67 patients) with an infected arthrodesis, and group B (43 patients) with an infected nonunion in a long bone. In group A, infected arthrodesis, the success rate after the first procedure was 38/67 (57%), 29/67 (43%) required further surgery for either control of infection or non-union. At last follow-up, five patients required amputation, representing a limb salvage rate of 62/67 (93%) overall. In all, 29/67 (43%) presented with a bone defect with a mean size of 6.78 cm (2 to 25). Of those with a bone defect, 13/29 (45%) required further surgery and had a mean size of defect of 7.2 cm (3.5 to 25). The cultures were negative in 17/67 (26%) and the most common organism cultured was methicillin-resistant staphylococcus aureus (MRSA) (23/67, (35%)). In group B, long bones nonunion, the success rate after the first procedure was 26/43 (60%), 17/43 (40%) required further surgery for either control of infection or nonunion. The limb salvage rate at last follow-up was 43/43 (100%). A total of 22/43 (51%) had bone defect with a mean size of 4.7 cm (1.5 to 11.5). Of those patients with a bone defect, 93% required further surgery with a mean size of defect of 5.4 cm (3 to 8.5). The cultures were negative in 10/43 (24%) and the most common organism cultured was MRSA, 15/43 (35%). ACC rods are an effective form of treatment for an infected nonunion, with an acceptable rate of complications.

Cite this article: Bone Joint J 2014; 96-B:1349–54

A silver-containing hydroxyapatite (Ag-HA) coating has been developed using thermal spraying technology. We evaluated the osteoconductivity of this coating on titanium (Ti) implants in rat tibiae in relation to bacterial infection in joint replacement.

At 12 weeks, the mean affinity indices of bone formation of a Ti, an HA, a 3%Ag-HA and a 50%Ag-HA coating were 97.3%, 84.9%, 81.0% and 40.5%, respectively. The mean affinity indices of bone contact of these four coatings were 18.8%, 83.7%, 77.2% and 40.5%, respectively. The indices of bone formation and bone contact around the implant of the 3%Ag-HA coating were similar to those of the HA coating, and no significant differences were found between them (bone formation, p = 0.99; bone contact, p = 0.957). However, inhibition of bone formation was observed with the 50%Ag-HA coating.

These results indicate that the 3%Ag-HA coating has low toxicity and good osteoconductivity, and that the effect of silver toxicity on osteoconductivity depends on the dose.