Introduction. Iatrogenic proximal femur hoop-stress fracture is a recognised complication of uncemented hip arthroplasty. It has a reported incidence of two to three percent and increases patient morbidity. We describe a novel technology that predicts fracture in real-time by less than one minute. Method. Four proximal femora from red deer (Cervus elaphus), similar size to human proximal femora, were prepared to accept an uncemented hip arthroplasty femoral rasp (Finsbury Orthopaedics) and then mounted in a loading machine. The femora were fresh-frozen, defrosted and kept at room temperature in 0.9% saline swabs. The rasp was forced into each femur in repeated loading cycles every 10 seconds, in steps of 100N increasing from 200N to over 2000N until fracture, in a manner to simulate surgery. One sensor was attached to the surface of the proximal femur and one to the femoral rasp. The sensor outputs were recorded, analysed and displayed on a PC using a software algorithm to show signal energy (joules) and amplitude (decibels). The proximal femur was coated with specular marking paint to permit real-time 3-D digital image correlation (DIC) analysis. DIC is an established tool in engineering fracture analysis and utilises two spatially orientated video cameras to measure surface strain and fracture. The femur was observed by the human eye and loaded in cycles until a fracture was seen. The moment of fracture was marked in the recording timeline. DIC was used to confirm fracture. Results. All femora fractured in the anterior proximal cortex. Signals from both sensors were identical in form and differed by less than five percent in strength during loading. Both signals demonstrated significant increases in energy and amplitude shortly prior to fracture. Early during loading cycles the femoral rasp subsided and became well-fixed within the femur; this was associated with signals of 60-70dB. During later loading cycles the rasp ceased to subside in the femur and was well-fixed in a press-fit; subsequent loading caused fracture and this was preceded by a greater number of stronger signals of over 90dB. The increase occurred 1 to 3 loading cycles prior to fracture, or less than 30 seconds. DIC was used to confirm the presence of a fracture visible to the human eye. At the time of the first significant increase in signal there was no crack visible to the eye or to DIC analysis and the femoral rasp did not subside further into the femur. Conclusions. During press-fitting of an uncemented femoral rasp in a deer femur a significant change in signal characteristics occurs shortly prior to a fracture being visible to the eye and detectable by DIC analysis. The almost identical signal output from both sensors suggests that one single sensor mounted on a femoral rasp will suffice, thereby removing the need to expose more of the proximal femur during surgery. This technology may be able to predict and therefore prevent femur fracture during uncemented hip arthroplasty. Further research is necessary in animal and human cadavers to explore and validate this research

We have developed a bioactive bone cement (BA cement) consisting of Bis-GMA resin and bioactive glass powder. It has high compressive and tensile strengths, a low curing temperature and its bioactivity allows it to bond directly with bone. We operated on the 18 femora of nine mongrel dogs for intercalary replacement of part of the bone by a metal prosthesis using either PMMA cement or BA cement for fixation. Three dogs were killed at each of 4, 12 and 26 weeks after surgery for the evaluation of fixation strength by a push-out test and for histological examination by Giemsa surface staining and SEM. Fixation strengths with PMMA cement at 4, 12 and 26 weeks after surgery were 46.8 ± 18.9, 50.0 ± 24.7, and 58.2 ± 28.9 kgf (mean ±SD), respectively. Those with BA cement were 56.8 ± 26.1, 67.2 ± 19.2, and 72.8 ± 22.2 kgf, respectively. Fibrous tissue intervened between bone and PMMA cement but BA cement had bonded directly to bone at 12 and 26 weeks. This suggests that BA cement will be useful in providing long-lasting fixation of implants to bone under weight-bearing conditions

Hydroxyapatite-coated standard anatomical and customised femoral stems are designed to transmit load to the metaphyseal part of the proximal femur in order to avoid stress shielding and to reduce resorption of bone. In a randomised in vitro study, we compared the changes in the pattern of cortical strain after the insertion of hydroxyapatite-coated standard anatomical and customised stems in 12 pairs of human cadaver femora. A hip simulator reproduced the physiological loads on the proximal femur in single-leg stance and stair-climbing. The cortical strains were measured before and after the insertion of the stems.

Significantly higher strain shielding was seen in Gruen zones 7, 6, 5, 3 and 2 after the insertion of the anatomical stem compared with the customised stem. For the anatomical stem, the hoop strains on the femur also indicated that the load was transferred to the cortical bone at the lower metaphyseal or upper diaphyseal part of the proximal femur.

The customised stem induced a strain pattern more similar to that of the intact femur than the standard, anatomical stem.

In uncemented total hip arthroplasty (THA), the optimal femoral component should allow both maximum cortical contact with proximal load transfer and accurate restoration of individual joint biomechanics. This is often compromised due to a high variability in proximal femoral anatomy. The aim of this on-going study is to assess the variation in proximal femoral canal shape and its association with geometric and anthropometric parameters in primary hip OA.

In a retrospective cohort study, AP-pelvis radiographs of 98 consecutive patients (42 males, 56 females, mean age 61 (range:45-74) years, BMI 27.4 (range:20.3-44.6) kg/m2) who underwent THA for primary hip OA were reviewed. All radiographs were calibrated and femoral offset (FO) and neck-shaft-angle (NSA) were measured using a validated custom programme. Point-based active shape modelling (ASM) was performed to assess the shape of the inner cortex of the proximal femoral meta- and diaphysis. Independent shape modes were identified using principal component analysis (PCA). Hierarchical cluster analysis of the shape modes was performed to identify natural groupings of patients. Differences in geometric measures of the proximal femur (FO, NSA) and demographic parameters (age, height, weight, BMI) between the clusters were evaluated using Kruskal-Wallis one-way-ANOVA or Chi-square tests, as appropriate.

In the entire cohort, mean FO was 39.0 mm, mean NSA was 131 degrees. PCA identified 10 independent shape modes accounting for over 90% of variation in proximal femoral canal shape within the dataset. Cluster Analysis revealed 6 shape clusters for which all 10 shape modes demonstrated a significantly different distribution (p-range:0.000-0.015). We observed significant differences in age (p=0.032), FO (p<0.001) and NSA (p<0.001) between the clusters. No significant differences with regard to gender or BMI were seen.

Our preliminary analysis has identified 6 different patterns of proximal femoral canal shape which are associated with significant differences in femoral offset, neck-shaft-angle and age at time of surgery. We are currently evaluating the entire dataset of 345 patients which will allow a comprehensive classification of variation in proximal femoral shape and joint geometry. The present data may optimise preoperative planning and improve future implant design in THA.

We have studied the effect of hydroxyapatite (HA) coating in 15 ovariectomised and 15 normal rats which had had a sham procedure. Twenty-four weeks after operation, HA-coated implants were inserted into the intramedullary canal of the right femur and uncoated implants into the left femur. The prostheses were removed four weeks after implantation. Twelve specimens in each group had mechanical push-out tests. Sagittal sections of the other three were evaluated by SEM.

The bone mineral density (BMD) of the dissected left tibia was measured by dual-energy x-ray absorptiometry. The difference in BMD between the control and ovariectomised tibiae was 35.01 mg/cm² (95% CI, 26.60 to 43.42). The push-out strength of the HA-coated implants was higher than that of the uncoated implants in both groups (p < 0.0001), but the HA-coated implants of the ovariectomised group had a reduction in push-out strength of 40.3% compared with the control group (p < 0.0001).

Our findings suggest that HA-coated implants may improve the fixation of a cementless total hip prosthesis but that the presence of osteoporosis may limit the magnitude of this benefit.

A painful “dreaded black line” (DBL) has been associated with progression to complete fractures in atypical femur fractures (AFF). Adjacent sclerosis, an unrecognized radiological finding, has been observed in relation to the DBL. We document its incidence, associated features, demographics and clinical progression. We reviewed plain radiographs of 109 incomplete AFFs between November 2006 and June 2021 for the presence of sclerosis adjacent to a DBL. Radiographs were reviewed for location of lesions, and presence of focal endosteal or periosteal thickening. We collected demographical data, type and duration of bisphosphonate therapy, and progression to fracture or need for prophylactic stabilization, with a 100% follow up of 72 months (8 – 184 months). 109 femurs in 86 patients were reviewed. Seventeen sclerotic DBLs were observed in 14 patients (3 bilateral), involving 15.6% of all femora and 29.8% of femora with DBLs. Location was mainly subtrochanteric (41.2%), proximal diaphyseal (35.3%) and mid-diaphyseal (23.5%), and were associated with endosteal or periosteal thickening. All patients were female, mostly Chinese (92.9%), with a mean age of 69 years. 12 patients (85.7%) had a history of alendronate therapy, and the remaining 2 patients had zoledronate and denosumab therapy respectively. Mean duration of bisphosphonate therapy was 62 months. 4 femora (23.5%) progressed to complete fractures that were surgically managed, whilst 6 femora (35.3%) required prophylactic fixation. Peri-lesional sclerosis in DBL is a new radiological finding in AFFs, predominantly found in the proximal half of the femur, at times bilateral, and are always associated with endosteal or periosteal thickening. As a high proportion of patients required surgical intervention, these lesions could suggest non-union of AFFs, similar to the sclerotic margins commonly seen in fractures with non-union. The recognition of and further research into this new feature could shed more light on the pathophysiological progression of AFFs

This study aims to assess the fracture mechanics of type-2 diabetic (T2D) femoral bone using innovative site-specific tests, whilst also examining the cortical and trabecular bone microarchitecture from various regions using micro-computed tomography (CT) of the femur as the disease progresses. Male [Zucker Diabetic Fatty (ZDF: fa/fa) (T2D) and Zucker Lean (ZL: fa/+) (Control)] rats were euthanized at 12-weeks of age, thereafter, right and left femora were dissected (Right femora: n = 6, per age, per condition; Left femora: n=8-9, per age, per condition). Right femurs were notched in the posterior of the midshaft. Micro-CT was used to scan the proximal femur, notched and unnotched femoral midshaft (cortical) of the right femur and the distal metaphysis (trabecular) of the left femur to investigate microarchitecture and composition. Right femurs were fracture toughness tested to measure the stress intensity factor (Kic) followed by a sideways fall test using a custom-made rig to investigate femoral neck mechanical properties. There was no difference in trabecular and cortical tissue material density (TMD) between T2D and control rats. Cortical thickness was unchanged, but trabeculae were thinner (p<0.01) in T2D rats versus controls. However, T2D rats had a greater number of trabeculae (p<0.05) although trabecular spacing was not different to controls. T2D rats had a higher connectivity distribution (p<0.05) and degree of anisotropy (p<0.05) in comparison to controls. There was no difference in the mechanical properties between strains. At 12-weeks of age, rats are experiencing early-stage T2Ds and the disease impact is currently not very clear. Structural and material properties are unchanged between strains, but the trabecular morphology shows that T2D rats have more trabecular struts present in order to account for the thinner trabeculae

Introduction and Objective. In multiple trauma patients, as well as in the healing of isolated fractures (Fx) with heavy bleeding (trauma haemorrhage, TH), complications occur very often. This is particularly evident in elderly patients over 65 years of age. Since these accompanying circumstances strongly influence the clinical course of treatment, the influence of age on bone regeneration after femoral fracture and severe blood loss was investigated in this study. Materials and Methods. 12 young (17–26 weeks) and 12 old (64–72 weeks) male C57BL / 6J mice per group were examined. The fracture group Fx underwent an osteotomy after applying an external fixator. The THFx group also received blood pressure-controlled trauma hemorrhage (35 mmHg for 90 minutes) and reperfusion with Ringer's solution for 30 minutes. The Sham group received only the catheter and one external fixator. μCT scans of the femora were performed in vivo after 2 weeks and ex vivo after 3 weeks. Histological and biomechanical examinations were also carried out. The statistical significance was set at p ≤ 0.05. The non-normally distributed data were analyzed using the Mann-Whitney-U or Kruskal-Wallis test. Results. The histology showed less mineralized bone in the fracture gap in old animals of the Fx (25.41% [1.68%]) and THFx groups (25.50% [4.07%]) compared with the young ones (34.20% [6.36%], p = 0.003; 34.31% [5.12%], p=0.009). Moreover, a severe blood loss lead to more cartilage in both young (6.91% [5.08%]) and old animals (4.17% [1.42%]) compared to animals with only a fracture (2, 45% [1.04%], p=0.004; 2.95% [1.12%], p=0.032). In old animals (11.37 / nm. 2. [17.17 / nm. 2. ]) in contrast the young mice with an isolated fracture (33.6/nm. 2. [8.83/nm. 2. ]) fewer osteoclasts were present (p=0.009). Therefore, the severe blood loss further reduced the number of osteoclasts only in young animals (16.83/nm. 2. [6.07/nm. 2. ]) (p=0.004). In the in vivo μCT, after 2 weeks, a lower volume of bone, cortex and callus was found in old THFx animals (3.14 mm. 3. [0.64 mm. 3. ]); 1.01 mm. 3. [0.04 mm. 3. ]; 2.07 mm. 3. [0.57 mm. 3. ]) compared with the Fx animals (4.29 mm. 3. [0.74 mm. 3. ], p=0.008; 1.18 mm. 3. [0, 25 mm. 3. ], p=0.004; 3.02 mm. 3. [0.77 mm. 3. ], p=0.008) After 3 weeks, the ex vivo μCT scans also showed a reduced callus percentage in old THFx animals (61.18% [13.9 9%]), as well as a low number of trabeculae (1.81 mm. -1. [0.23 mm. -1. ]) compared to animals without blood loss (68.72% [15.71%], p = 0.030; 2.06mm. -1. [0.37mm. -1. ], p=0.041). In the biomechanical test, a reduced elasticity limit of the old THFx mice (7.75 N [3.33 N]) in contrast to the old Fx (10.24 N [3.32 N]) animals was shown (p=0.022). Conclusions. A severe blood loss has a higher negative effect on the healing, morphometry, and biomechanical properties of previously fractured femora in old compared to young individuals

We implanted titanium and carbon fibre-reinforced plastic (CFRP) femoral prostheses of the same dimensions into five prosthetic femora. An abductor jig was attached and a 1 kN load applied. This was repeated with five control femora. Digital image correlation was used to give a detailed two-dimensional strain map of the medial cortex of the proximal femur. Both implants caused stress shielding around the calcar. Distally, the titanium implant showed stress shielding, whereas the CFRP prosthesis did not produce a strain pattern which was statistically different from the controls. There was a reduction in strain beyond the tip of both the implants. This investigation indicates that use of the CFRP stem should avoid stress shielding in total hip replacement

Introduction and Objective. Trochanteric fractures are associated with increasing incidence and represent serious adverse effect of osteoporosis. Their cephalomedullary nailing in poor bone stock can be challenging and associated with insufficient implant fixation in the femoral head. Despite ongoing implant improvements, the rate of mechanical complications in the treatment of unstable trochanteric fractures is high. Recently, two novel concepts for nailing with use of a helical blade – with or without bone cement augmentation – or an interlocking screw have demonstrated advantages as compared with single screw systems regarding rotational stability and cut-out resistance. However, these two concepts have not been subjected to direct biomechanical comparison so far. The aims of this study were to investigate in a human cadaveric model with low bone density (1) the biomechanical competence of cephalomedullary nailing with use of a helical blade versus an interlocking screw, and (2) the effect of cement augmentation on the fixation strength of the helical blade. Materials and Methods. Twelve osteoporotic and osteopenic femoral pairs were assigned for pairwise implantation using either short TFN-ADVANCED Proximal Femoral Nailing System (TFNA) with a helical blade head element, offering the option for cement augmentation, or short TRIGEN INTERTAN Intertrochanteric Antegrade Nail (InterTAN) with an interlocking screw. Six osteoporotic femora, implanted with TFNA, were augmented with 3 ml cement. Four study groups were created – group 1 (TFNA) paired with group 2 (InterTAN), and group 3 (TFNA augmented) paired with group 4 (InterTAN). An unstable pertrochanteric OTA/AO 31-A2.2 fracture was simulated. All specimens were biomechanically tested until failure under progressively increasing cyclic loading featuring physiologic loading trajectory, with monitoring via motion tracking. Results. T-score in groups 3 and 4 was significantly lower compared with groups 1 and 2, p=0.03. Stiffness (N/mm) in groups 1 to 4 was 335.7+/−65.3, 326.9+/−62.2, 371.5+/−63.8 and 301.6+/−85.9, being significantly different between groups 3 and 4, p=0.03. Varus (°) and femoral head rotation around neck axis (°) after 10,000 cycles were 1.9+/−0.9 and 0.3+/−0.2 in group 1, 2.2+/−0.7 and 0.7+/−0.4 in group 2, 1.5+/−1.3 and 0.3+/−0.2 in group 3, and 3.5+/−2.8 and 0.9+/−0.6 in group 4, both with significant difference between groups 3 and 4, p<=0.04. Cycles to failure and failure load (N) at 5° varus in groups 1 to 4 were 21428+/−6020 and 1571.4+/−301.0, 20611+/−7453 and 1530.6+/−372.7,21739+/−4248 and 1587.0+/−212.4, and 18622+/−6733 and 1431.1+/−336.7, both significantly different between groups 3 and 4, p=0.04. Conclusions. From a biomechanical perspective, cephalomedullary nailing of trochanteric fractures with use of helical blades is comparable to interlocking screw fixation in femoral head fragments with low bone density. Moreover, bone cement augmentation of helical blades considerably improves their fixation strength in poor bone quality

Introduction and Objective. Distal femoral fractures are commonly treated with a straight plate fixed to the lateral aspects of both proximal and distal fragments. However, the lateral approach may not always be desirable due to persisting soft-tissue or additional vascular injury necessitating a medial approach. These problems may be overcome by pre-contouring the plate in helically shaped fashion, allowing its distal part to be fixed to the medial aspect of the femoral condyle. The objective of this study was to investigate the biomechanical competence of medial femoral helical plating versus conventional straight lateral plating in an artificial distal femoral fracture model. Materials and Methods. Twelve left artificial femora were instrumented with a 15-hole Locking Compression Plate – Distal Femur (LCP-DF) plate, using either conventional lateral plating technique with the plate left non-contoured, or the medial helical plating technique by pre-contouring the plate to a 180° helical shape and fixing its distal end to the medial femoral condyle (n=6). An unstable extraarticular distal femoral fracture was subsequently simulated by means of an osteotomy gap. All specimens were tested under quasi-static and progressively increasing cyclic axial und torsional loading until failure. Interfragmentary movements were monitored by means of optical motion tracking. Results. Initial axial stiffness was significantly higher for helical (185.6±50.1 N/mm) versus straight (56.0±14.4) plating, p<0.01. However, initial torsional stiffness in internal and external rotation remained not significantly different between the two fixation techniques (helical plating:1.59±0.17 Nm/° and 1.52±0.13 Nm/°; straight plating: 1.50±0.12 Nm/° and 1.43±0.13Nm/°), p≥0.21. Helical plating was associated with significantly higher initial interfragmentary movements under 500 N static compression compared to straight plating in terms of flexion (2.76±1.02° versus 0.87±0.77°) and shear displacement under 6 Nm static rotation in internal (1.23±0.28° versus 0.40±0.42°) and external (1.21±0.40° versus 0.57±0.33°) rotation, p≤0.01. In addition, helical plating demonstrated significantly lower initial varus/valgus deformation than straight plating (4.08±1.49° versus 6.60±0.47°), p<0.01. Within the first 10000 cycles of dynamic loading, helical plating revealed significantly bigger flexural movements and significantly lower varus/valgus deformation versus straight plating, p=0.02. No significant differences were observed between the two fixation techniques in terms of axial and shear displacement, p≥0.76. Cycles to failure was significantly higher for helical plating (13752±1518) compared to straight plating (9727±836), p<0.01. Conclusions. Although helical plating using a pre-contoured LCP-DF was associated with higher shear and flexion movements, it demonstrated improved initial axial stability and resistance against varus/valgus deformation compared to straight lateral plating. Moreover, helical plate constructs demonstrated significantly improved endurance to failure, which may be attributed to the less progressively increasing lever bending moment arm inherent to this novel fixation technique. From a biomechanical perspective, helical plating may be considered as a valid alternative fixation technique to standard straight lateral plating of unstable distal femoral fractures

Summary. A novel bipolar cooled radiofrequency ablation probe, optimised for bone metastases applications, is shown in two preclinical models to offer a safe and minimally invasive treatment option that can ablate large tissue volumes and preserve the regenerative ability of bone. Introduction. Use of radiofrequency ablation (RFA) in treating of skeletal metastases has been rising, yet its impact on bone tissue is poorly understood. 2–11 RF treatment induces frictional heating and effectively necrotises tissue in a local and minimally invasive manner.1 Bipolar cooled RF (BCRF) is a significant improvement to conventional RF whereby larger regions can be safely treated, protecting sensitive neighbouring tissues from thermal effects. This study aimed to evaluate the safety and feasibility of a novel bipolar RFA probe to create large contained lesions within healthy pig vertebrae and its determine its effects on bone and tumour cells in a rabbit long bone tumour model. Methods. Following a pre-treatment MRI, a BCRF probe was placed transpedicularly into targeted lumbar vertebrae of six Yorkshire pigs. Energy was delivered for 15min at a set temperature of 65°C (n=2 per animal) with a sham control performed at a non-contiguous level (n=1 per animal). Post-treatment neurologic evaluation, MRI and histology were used to characterise the region of effect. Twelve New Zealand White Rabbits received a 200 µl injection of VX2 tumour cells into one femur. On day 14, half of the tumour-bearing and contralateral healthy femora were RF-treated (n=6 per group). RF-treated femora were compared to tumour-bearing and healthy sham groups (n=6 per group) through pre (day 14) and post treatment (day 28) MRI and histology (H&E (for general evaluation), AE1/AE3 (for VX2 tumour cell evaluation), TRAP (for osteoclast evaluation) and TUNEL (for osteocyte evaluation)). Results. In treated porcine spines there were no neurological complications. MR imaging confirmed a 2cm oval shaped ablative zone. External thermocouple measurements indicated output values in the physiological temperature range suggesting treatment was safely confined within targeted vertebrae. Histological results correlated well with the ablation regions determined using MRI sequences in both models. In rabbit femora, large zones of RF ablation (average volume 12.9±5.5 cm3) extended beyond the femur cortex (corresponding to the probe design for human use) into the surrounding soft tissue. The RFA-treated tumour-involved specimens demonstrated a significant reduction in tumour volume compared to sham femora, however a small number of viable tumour cells remained within the ablation volume. Newly formed trabecular structures were also seen in all treated femora. TRAP staining demonstrated a significant reduction in osteoclast number post-RFA in both the tumour-involved and healthy groups. TUNEL staining revealed areas of patchy cortical osteocyte necrosis within the ablation zone. Discussion/Conclusions. The large histologic region of effect created by RFA was consistent with MRI findings in both models. Treatment was contained in the porcine vertebrae without collateral damage to neighbouring sensitive structures. In the femora, while osteoclasts were found to be very susceptible to RFA, a small number of tumour cells and osteocytes in the treated regions remained viable. As the treatment zone did not encompass the full extent of the intramedullary lesions, it is possible that the sporadic VX2 cell viability may be explained by local tumour cell migration. Limited destruction of healthy osteocytes by RFA may be desirable in restoring bone health

The use of retrograde femoral intramedullary nails in children for deformity correction is controversial. It is unknown if the injury to the central part of the growth plate results in premature bony union, leading to limb deformities or discrepancies. The aim of this study was to assess physeal healing and bone growth after insertion of a retrograde femoral nail thorough the centre of the physis in a skeletally immature experimental porcine model. Eleven immature pigs were included in the study. One leg was randomised for operation with a retrograde femoral nail (diameter 10.7 mm), whilst the non-operated contralateral remained as control. All nails were inserted centrally in coronal and sagittal plane under fluoroscopic guidance, and the nails spanned the physis. The nails were removed at 8 weeks. Both femora in all animals underwent MRI at baseline (pre-operatively), 8 weeks (after nail removal) and 16 weeks (before euthanasia). Femoral bone length was measured at 5 sites (anterior, posterior, central, lateral and medial) using 3d T1-weighted MRI. Growth was calculated after 8 weeks (growth with nail) and 16 weeks (growth without nail). Physeal cross-sectional area and percentage violated by the nail was determined on MRI. Operated side was compared to non-operated. Corresponding 95% confidence intervals were calculated. No differences in axial growth were observed between operated and non-operated sides. Mean growth difference was 0,61 mm [−0,78;2,01] whilst the nail was inserted into the bone and 0,72 mm [−1,04;1,65] after nail removal. No signs of angular bone deformities were found when comparing operated side to non-operated side. No premature bony healing at the physis occurred. Histology confirmed fibrous healing. Mean physeal violation was 5.72% [5.51; 5.93] by the femoral nail. The insertion of a retrograde femoral nail through the centre of an open physis might be a safe procedure with no subsequent growth arrest. However, experiments assessing the long term physeal healing and growth are needed

It is common belief that consolidated intramedullary nailed trochanteric femur fractures can result in secondary midshaft or supracondylar fractures, involving the distal screws, when short or long nails are used, respectively. In addition, limited data exists in the literature to indicate when short or long nails should be selected for treatment. The aim of this biomechanical cadaveric study was to investigate short versus long Trochanteric Femoral Nail Advanced (TFNA) fixation in terms of construct stability and generation of secondary fracture pattern following trochanteric fracture consolidation. Eight intact human cadaveric femur pairs were assigned to 2 groups of 8 specimens each for nailing using either short or long TFNA with blade as head element. Each specimen was first biomechanically preloaded at 1 Hz over 2000 cycles in superimposed synchronous axial compression to 1800 N and internal rotation to 11.5 Nm. Following, internal rotation to failure was applied over an arc of 90° within 1 second under 700 N axial load. Torsional stiffness, torque at failure, angle at failure and energy at failure were evaluated. Fracture patterns were analyzed. Outcomes in the groups with short and long nails were 9.7±2.4 Nm/° and 10.2±2.9 Nm/° for torsional stiffness, 119.8±37.2 Nm and 128.5±46.7 Nm for torque at failure, 13.5±3.5° and 13.4±2.6° for angle at failure, and 887.5±416.9 Nm° and 928.3±461.0 Nm° for energy at failure, respectively, with no significant differences between them, P≥0.167. Fractures through the distal locking screw occurred in 5 and 6 femora instrumented with short and long nails, respectively. Fractures through the lateral entry site of the head element were detected in 3 specimens within each group. For short nails, fractures through the distal shaft region, not interfacing with the implant, were detected in 3 specimens. From biomechanical perspective, the risk of secondary peri-implant fracture after intramedullary nailed trochanteric fracture consolidation is similar when using short or long TFNA. Moreover, for both nail versions the fracture pattern does not unexceptionally involve the distal locking screw

Summary Statement. Thickness and cellularity of human periosteum are important parameters both for engineering replacement tissue as well as for surgeons looking to minimise tissue damage while harvesting the most viable periosteum possible for autologous regenerative therapies. This study provides a new foundation for understanding the basic structural features of middiaphyseal periosteum from femora and tibiae of aged donors. Introduction. A number of recent studies describe mechanical, permeability and regenerative properties of periosteal tissue and periosteum derived cells in a variety of animal models [1,2]. However, due to lack of access in healthy patients, the structural properties underlying human periosteum's inherent regenerative power and advanced material properties are not well understood. Periosteum comprises a cellular cambium layer directly apposing the outer surface of bone and an outer fibrous layer encompassed by the surrounding soft tissues. As a first step to elucidate periosteum's structural and cellular characteristics in human bone, the current study aims to measure cambium and fibrous layer thickness as well as cambium cellularity in human femora and tibiae of aged donors. Methods. Five cm segments of the mid-diaphysis were harvested from the left and right tibiae and femora of formalin-fixed cadavers donated to the Department of Anatomy at the Ludwig Maximilians University of Munich. Overlying skin and musculature was preserved during embedding to avoid disruption of periosteal tissue. A total of 29 mid-diaphyseal samples were collected from eight donors, aged between 68 and 99. Cambium layer thickness, fibrous thickness and cambium cell number were measured at regular 100 μm intervals from the centroidal axis along the bone's outer surface (ImageJ 1.42q). The major and minor centroidal axes (CA) serve as automated reference points in cross sections of cadaveric mid-diaphyseal femora and tibiae. Results. Based on the results of this study, within a given individual, the cambium layer of the major CA of the tibia is significantly thicker and more cellular than the respective layer of the femur. These significant intraindividual differences do not translate to significant interindividual differences. Further, mid-diaphyseal periosteal measures including cambium and fibrous layer thickness and cellularity do not correlate significantly with age or body mass. Finally, qualitative observations of periosteum in amputated and contralateral or proximal long bones of the lower extremity exhibit stark changes in layer organization, thickness, and cellularity. Discussion/Conclusion. In a translational context, these unprecedented data, though inherently limited by availability and accessibility of human mid-diaphyseal periosteum tissue, provide important reference values for use of periosteum in context of facilitated healing and regeneration of tissue

Corrective osteotomies are often planned and performed on the basis of normal anatomical proportions. We have evaluated the length and torsion of the segments of the lower limb in normal individuals, to analyse the differences between left and right sides, and to provide tolerance figures for both length and torsion. We used CT on 355 adult patients and measured length and torsion by the Ulm method. We excluded all patients with evidence of trauma, infection, tumour or any congenital disorder. The mean length of 511 femora was 46.3 ± 6.4 cm (±2. sd. ) and of 513 tibiae 36.9 ± 5.6 cm; the mean total length of 378 lower limbs was 83.2 ± 11.4 cm with a tibiofemoral ratio of 1 to 1.26 ± 0.1. The 99th percentile level for length difference in 178 paired femora was 1.2 cm, in 171 paired tibiae 1.0 cm and in 60 paired lower limbs 1.4 cm. In 505 femora the mean internal torsion was 24.1 ± 17.4°, and in 504 tibiae the mean external torsion was 34.9 ± 15.9°. For 352 lower limbs the mean external torsion was 9.8 ± 11.4°. The mean torsion angle of right and left femora in individuals did not differ significantly, but mean tibial torsion showed a significant difference between right (36.46° of external torsion) and left sides (33.07° of external torsion). For the whole legs torsion on the left was 7.5 ± 18.2° and 11.8 ± 18.8°, respectively (p < 0.001). There was a trend to greater internal torsion in femora in association with an increased external torsion in tibiae, but we found no correlation. The 99th percentile value for the difference in 172 paired femora was 13°; in 176 pairs of tibiae it was 14.3° and for 60 paired lower limbs 15.6°. These results will help to plan corrective osteotomies in the lower limbs, and we have re-evaluated the mathematical limits of differences in length and torsion

We studied the morphometry of 35 femora from 31 female patients with developmental dysplasia of the hip (DDH) and another 15 from 15 age- and sex-matched control patients using CT and three-dimensional computer reconstruction models. According to the classification of Crowe et al 15 of the dysplastic hips were graded as class I (less than 50% subluxation), ten as class II/III (50% to 100% subluxation) and ten as class IV (more than 100% subluxation). The femora with DDH had 10 to 14° more anteversion than the control group independent of the degree of subluxation of the hip. In even the most mildly dysplastic joints, the femur had a smaller and more anteverted canal than the normal control. With increased subluxation, additional abnormalities were observed in the size and position of the femoral head. Femora from dislocated joints had a short, anteverted neck associated with a smaller, narrower, and straighter canal than femora of classes I and II/III or the normal control group. We suggest that when total hip replacement is performed in the patient with DDH, the femoral prosthesis should be chosen on the basis of the severity of the subluxation and the degree of anteversion of each individual femur

The accurate positioning of the total knee arthroplasty affects the survival of the implants(1). Alignment of the femoral component in relation to the native knee is best determined using pre- and post-operative 3D-CT reconstruction(2). Currently, the scans are visualised on separate displays. There is a high inter- and intra-observer variability in measurements of implant rotation and translation(3). Correct alignment is required to allow a direct comparison of the pre- and post-operative surfaces. This is prevented by the presence of the prostheses, the bone shape alteration around the implant, associated metal artefacts, and possibly a segmentation noise. The aim is to create a novel method to automatically register pre- and post-operative femora for the direct comparison of the implant and the native bone. The concept is to use post-operative femoral shaft segments free of metal noise and of surgical alteration for alignment with the pre-operative scan. It involves three steps. Firstly, using principal component analysis, the femoral shafts are re-oriented to match the X axis. Secondly, variants of the post-operative scan are created by subtracting 1mm increments from the distal femoral end. Thirdly, an iterative closest point algorithm is applied to align the variants with the pre-operative scan. For exploratory validation, this algorithm was applied to a mesh representing the distal half of a 3D scanned femur. The mesh of a prosthesis was blended with the femur to create a post-operative model. To simulate a realistic environment, segmentation and metal artefact noise were added. For segmentation noise, each femoral vertex was translated randomly within +−1mm,+−2mm,+−3mm along its normal vector. To create metal artefact random noise was added within 50 mm of the implant points in the planes orthogonal to the shaft. The alignment error was considered as the average distance between corresponding points which are identical in pre- and post-operative femora. These preliminary results obtained within a simulated environment show that by using only the native parts of the femur, the algorithm was able to automatically register the pre- and post-operative scans even in presence of the implant. Its application will allow visualisation of the scans on the same display for the direct comparison of the perioperative scans. This method requires further validation with more realistic noise models and with patient data. Future studies will have to determine if correct alignment has any effect on inter- and intra-observer variability

Malpositioning of the trochanteric entry point during the introduction of an intramedullary nail may cause iatrogenic fracture or malreduction. Although the optimal point of insertion in the coronal plane has been well described, positioning in the sagittal plane is poorly defined. . The paired femora from 374 cadavers were placed both in the anatomical position and in internal rotation to neutralise femoral anteversion. A marker was placed at the apparent apex of the greater trochanter, and the lateral and anterior offsets from the axis of the femoral shaft were measured on anteroposterior and lateral photographs. Greater trochanteric morphology and trochanteric overhang were graded. The mean anterior offset of the apex of the trochanter relative to the axis of the femoral shaft was 5.1 mm (. sd. 4.0) and 4.6 mm (. sd. 4.2) for the anatomical and neutralised positions, respectively. The mean lateral offset of the apex was 7.1 mm (. sd. 4.6) and 6.4 mm (. sd. 4.6), respectively. Placement of the entry position at the apex of the greater trochanter in the anteroposterior view does not reliably centre an intramedullary nail in the sagittal plane. Based on our findings, the site of insertion should be about 5 mm posterior to the apex of the trochanter to allow for its anterior offset. Cite this article: Bone Joint J 2014;96-B:1274–81

We have compared the changes in the pattern of the principal strains in the proximal femur after insertion of eight uncemented anatomical stems and eight customised stems in human cadaver femora. During testing we aimed to reproduce the physiological loads on the proximal femur and to simulate single-leg stance and stair-climbing. The strains in the intact femora were measured and there were no significant differences in principal tensile and compressive strains in the left and right femora of each pair. The two types of femoral stem were then inserted randomly into the left or right femora and the cortical strains were again measured. Both induced significant stress shielding in the proximal part of the metaphysis, but the deviation from the physiological strains was most pronounced after insertion of the anatomical stems. The principal compressive strain at the calcar was reduced by 90% for the anatomical stems and 67% for the customised stems. Medially, at the level of the lesser trochanter, the corresponding figures were 59% and 21%. The anatomical stems induced more stress concentration on the anterior aspect of the femur than did the customised stems. They also increased the hoop strains in the proximomedial femur. Our study shows a consistently more physiological pattern of strain in the proximal femur after insertion of customised stems compared with standard, anatomical stems