Purpose. Exeter stem was introduced to Japanese market at 1996. Since then, owing to its excellent clinical results, the number of the stem used has been increased year by year and more than 2000 stems have been implanted during the year 2009. The present study aims to prove its efficacy for Japanese patients by evaluating short term results of four major dedicated hip centers. Method. We present the short-term multi-center results of primary THA with Exeter stem combined with modern cementing technique in 881 patients (1000 hips). The average age of the patients at operation was 62.3years (ranging 23 to 89 years). Mean postoperative follow up period was 4.0 (ranging 2 to 9) years. Results. Intraoperative complications such as femoral fracture were observed in 6 hips. Postoperative cementing grade using Barrack's classification was judged as A for 735 hips, as B for 246 hips, and as C for 4 hips, respectively. Twenty-four patients died with unrelated disease and 52 patients were lost during follow-up period. Follow-up ratio was 94.8%. Thirty postoperative complications which include 9 infections, 14 dislocations, 5 deep vein thrombosis, and 2 sciatic nerve palsies were observed. Symptomatic pulmonary embolization or femoral fracture was not observed. Re-operations for infection and dislocation were performed for 8 and 6 hips, respectively. At the final follow-up, no radiolucent line at bone-cement interface was observed. Cortical hypertrophy was observed in 9.6% at Gruen zone 2 to 6. Kaplan-Meier survivorship analysis predicted a rate of survival at 5 years of 100% with radiolucent line at bone-cement interface of the femur as the endpoint, and of 98.8% when re-operation for any reason was used. Conclusion. The present study revealed excellent short-term result was obtained using Exeter stem combined with modern cementing technique for primary THAs in Japan

Aims

The aim of this study was to describe services available to patients with periprosthetic femoral fracture (PPFF) in England and Wales, with focus on variation between centres and areas for care improvement.

Aims

Monocyte-lymphocyte ratio (MLR) or neutrophil-lymphocyte ratio (NLR) are useful for diagnosing periprosthetic joint infection (PJI), but their diagnostic values are unclear for screening fixation-related infection (FRI) in patients for whom conversion total hip arthroplasty (THA) is planned after failed internal fixation for femoral neck fracture.

Despite proven advantages, pulsatile lavage seems to be used infrequently during preparation in cemented total knee arthroplasty. This remains irritating, as the technique has been suggested to improve radiological survival in cemented TKA, where aseptic loosening of the tibial component represents the main reason for revision. Furthermore, there may be a potential improvement of fixation strength for the tibial tray achieved by increased cement penetration. In this study, the influence of pulsed lavage on mechanical stability of the tibial component and bone cement penetration was analyzed in a cadaveric setting. Six pairs of cadaveric, proximal tibia specimen underwent computed tomography (CT) for assessment of bone mineral density (BMD) and exclusion of osseous lesions. Following surgical preparation, in one side of a pair, the tibial surface was irrigated using 1800ml normal saline and pulsatile lavage, while in the other side syringe lavage using the identical amount of fluid was applied. After careful drying, bone cement was hand-pressurized on the bone surface, tibial components were inserted and impacted in an identical way. After curing of cement, specimen underwent a postimplantation CT analysis). Cement distrubution was then assessed using a three-dimenionsional visualization software. Trabecular bone, cement and implant were segmented based on an automatic thresholding algorithm, which had been validated in a previous study. This allowed to determine median cement penetration for the entire cemented area. Furthermore, fixation strength of the tibial trays was determined by a vertical pull-out test using a servohydraulic material testing machine. Testing was performed under displacement control at a rate of 0,5mm/sec until implant failure. Data was described by median and range. Results were compared by a Wilcoxon matched pairs signed rank test with a type 1 error probability of 5 %. Median pull-out forces in the pulsed lavage group were 1275N (range 864–1391) and 568N (range 243–683) in the syringe lavage group (p=0.031). Cement penetration was likewise increased (p=0.031) in the pulsed lavage group (1.32mm; range 0.86–1.94), when compared to the syringe irrigated group (0.79mm; range 0.51–1.66). Failure occurred in the pulsatile lavage group at the implant-cement interface and in the syringe lavage group at the bone-cement interface, which indicates the weakness of the latter. Altogether, improved mechanical stability of the tibial implant and likewise increased bone cement interdigitation could be demonstrated in the current study, when pulsed lavage is implemented. Enhanced fixation strength was suggested being a key to improved survival of the implant. If this is the case, pulsatile lavage should be considered being a mandatory preparation step when cementing tibial components in TKA

Aims

To evaluate the outcomes of cemented total hip arthroplasty (THA) following a fracture of the acetabulum, with evaluation of risk factors and comparison with a patient group with no history of fracture.