Osteoarthritis (OA) is a multifactorial debilitating disease that affects over four million Canadians. Although the mechanism(s) of OA onset is unclear, the biological outcome is cartilage degradation. Cartilage degradation is typified by the progressive loss of extracellular matrix components - aggrecan and type II collagen (Col II) – partly due to the up-regulation of catabolic enzymes - aggrecanases a disintegrin and metalloprotease with thrombospondin motifs (ADAMTS-) 4 and 5 and matrix metalloproteinases (MMPs). There is currently no treatment that will prevent or repair joint damage, and current medications are aimed mostly at pain management. When pain becomes unmanageable arthroplastic surgery is often performed. Interest has developed over the presence of calcium crystals in the synovial fluid of OA patients, as they have been shown to activate synovial fibroblasts inducing the expression of catabolic agents. We recently discovered elevated levels of free calcium in the synovial fluid of OA patients and raised the question on its role in cartilage degeneration. Articular cartilage was isolated from 5 donors undergoing total hip replacement. Chondrocytes were recovered from the cartilage of each femoral head or knee by sequential digestion with Pronase followed by Collagenase and expanded in DMEM supplemented with 10% heat-inactivated FBS. OA and normal human articular chondrocytes (PromoCell, Heidelberg, Germany) were transferred to 6-well plates in culture medium containing various concentrations of calcium (0.5, 1, 2.5, and 5 mM CaCl2), and IL-1β. Cartilage explants were prepared from the same donors and included cartilage with the cortical bone approximately 1 cm2 in dimension. Bovine articular cartilage explants (10 months) were used as a control. Explants were cultured in the above mentioned media, however, the incubation period was extended to 21 days. Immunohistochemistry was performed on cartilage explants to measure expression of Col X, MMP-13, and alkaline phosphatase. The sulfated glycosaminoglycan (GAG, predominantly aggrecan) content of cartilage was analyzed using the 1,9-dimethylmethylene blue (DMMB) dye-binding assay, and aggregan fragmentation was determined by Western blotting using antibody targeted to its G1 domain. Western blotting was also performed on cell lysate from both OA and normal chondrocytes to measure aggrecan, Col II, MMP-3 and −13, ADAMTS-4 and −5. Ca2+ significantly decreased the proteoglycan content of the cartilage explants as determined by the DMMB assay. The presence of aggrecan and Col II also decreased as a function of calcium, in both the human OA and bovine cartilage explants. When normal and OA chondrocytes were cultured in medium supplemented with increasing concentrations of calcium (0.5–5 mM Ca2+), aggrecan and Col II expression decreased dose-dependently. Surprisingly, increasing Ca2+ did not induce the release of MMP-3, and −13, or ADAMTS-4 and-5 in conditioned media from OA and normal chondrocytes. Interestingly, inhibition of the extracellular calcium-sensing receptor CaSR) reversed the effects of calcium on matrix protein synthesis. We provide evidence that Ca2+ may play a direct role in cartilage degradation by regulating the expression of aggrecan and Col II through activation of CaSR

Introduction:. Unicompartmental knee arthroplasty (UKA) has been used in the past decades to treat progressive cartilage degeneration in a single compartment. Concern has been raised over the rate of revision procedures for polyethylene wear and osteoarthritic progression into the adjacent compartment. Few studies have examined the pathology of cartilage degeneration in the setting of UKA. This study aims to investigate the viability of knee chondrocytes introduced to high and low concentrations of orthopaedic wear debris particulate. Methods:. Normal human articular chondrocytes (nHAC-Kn) were expanded in DMEM/F12 containing 10% FBS, 1% Penicillin/Streptomycin (Pen/Strp), and 50 μg/mL ascorbic acid (Asc). 24 hours prior to the start of the experiment, cells were seeded on 96-well plates at a density of 3500 cells/cm. 2. and exposed to DMEM/F12 containing 5% FBS, 1% Pen/Strp, and 50 μg/mL Asc. Particles (equivalent circle diameter range: 0.2–7 μm) at a low dose of 100: 1 (particles: cells) and high dose 1000: 1 (particles: cells) were introduced to treatment wells (n = 6). Control wells (n = 6) contained particles with no cells. Treatment groups included high and low doses of TiAl. 6. V. 4. alloy, 316L Stainless Steel, and Co-Cr-Mo alloy. At days 1, 3, 5, and 7, cells were assayed with a 3-(4,5-Dimethylthiazol-2-yl)-2,5-dyphenyltetrazolium bromide (MTT) assay for determination of cell viability. Light microscopy was performed at each timepoint to assess change in cell morphology. Results:. All groups displayed a minor decrease in cell viability after 24 hours of exposure to particles. Similarly, a second distinct decrease in viability occurred at the day 3 timepoint. Days 5 and 7 yielded little change in cell viability. Results are displayed in Figure 1. Observations of light microscopy revealed cells may actively engulf particles over time. Images show particle concentrations at the same locations as chondrocytes with few particles present between cells. Conclusions:. Wear debris has been implicated as a contributing source to osteolysis and component loosening. A potential effect on the cellular level can ultimate lead to effects on the entire tissue and complications on the clinical level. A decrease in chondrocyte viability has been shown in response to the presence of particulate wear debris. Our results showed decreases in cell viability were most noticeable between 24 and 72 hours after introduction to particles. Chondrocyte death may contribute to progression of cartilage degeneration into healthy compartments of the knee. Continued experiments are underway further characterizing chondrocyte response to wear debris particulate with respect to protein and gene expression in an extended 7 day in vitro culture

Purpose. Traumatic articular cartilage (AC) defects are common in young adults and frequently progresses to osteoarthritis. Matrix-Induced Autologous Chondrocyte Implantation (MACI) is a recent advancement in cartilage resurfacing techniques and is a variant of ACI, which is considered by some surgeons to be the gold standard in AC regeneration. MACI involves embedding cultured chondrocytes into a scaffold that is then surgically implanted into an AC defect. Unfortunately, chondrocytes cultured in a normoxic environment (conventional technique) tend to de-differentiate resulting in decreased collagen II and increased collagen I producing in a fibrocartilagous repair tissue that is biomechanically inferior to AC and incapable of withstanding physiologic loads over prolonged periods. The optimum conditions for maintenance of chondrocyte phenotype remain elusive. Normal oxygen tension within AC is <7%. We hypothesized that hypoxic conditions would induce gene expression and matrix production that more closely characterizes normal articular chondrocytes than that achieved under normoxic conditions when chondrocytes are cultured in a collagen scaffold. Method. Chondrocytes were isolated from Outerbridge grade 0 and 1 AC from four patients undergoing total knee arthroplasty and embedded within 216 bovine collagen I scaffolds. Scaffolds were incubated in hypoxic (3% O2) or normoxic (21% O2) conditions for 1hr, 21hr and 14 days. Gene expression was determined using Q-rt-PCR for col I/II/X, COMP, SOX9, aggrecan and B actin. Matrix production was determined using glycosaminoglycan (GAG) content relative to cell count determined by DNA quantification. Cell viability and location within the matrix was determined by Live/Dead assay and confocal microscopy. Statistical analysis was performed using a two-tailed T-test. Results. Chondrocytes cultured under hypoxic conditions showed an upregulation of all matrix related genes compared to normoxic conditions noted most markedly in col II, COMP and SOX9 expression. There were similar numbers of chondrocytes between hypoxic and normoxic groups (P=0.68) but the chondrocytes in the hypoxic group produced more GAG per cell (P= 0.052). Viable cells were seen throughout the matrix in both groups. Conclusion. Important matrix related genes (col II, COMP, SOX9) were most significantly upregulated in hypoxic conditions compared to normoxic conditions. This was supported by an increase in GAG production per cell in hypoxic conditions. The results indicate that hypoxia induces an upregulation in the production of extracellular matrix components typical of AC with only modest increases in col I (possibly related to the col I based scaffold used in this experiment). These results indicate that hypoxic conditions are important for the maintenance of chondrocyte phenotype even when the cells are cultured in a 3D environment. In conclusion, hypoxic culture conditions should be used to help maintain chondrocyte phenotype even when culturing these cells in a 3D scaffold

Hyaline articular cartilage has been known to be a troublesome tissue to repair once damaged. Since the introduction of autologous chondrocyte implantation (ACI) in 1994, a renewed interest in the field of cartilage repair with new repair techniques and the hope for products that are regenerative have blossomed. This article reviews the basic science structure and function of articular cartilage, and techniques that are presently available to effect repair and their expected outcomes.