Aims. This study reports the ten-year wear rates, incidence of osteolysis, clinical outcomes, and complications of a multicentre randomized controlled trial comparing oxidized zirconium (OxZr) versus cobalt-chrome (CoCr) femoral heads with ultra-high molecular weight polyethylene (UHMWPE) and highly cross-linked polyethylene (XLPE) liners in total hip arthroplasty (THA). Methods. Patients undergoing primary THA were recruited from four institutions and prospectively allocated to the following treatment groups: Group A, CoCr femoral head with XLPE liner; Group B, OxZr femoral head with XLPE liner; and Group C, OxZr femoral head with UHMWPE liner. All study patients and assessors recording outcomes were blinded to the treatment groups. The outcomes of 262 study patients were analyzed at ten years’ follow-up. Results. Patients in Group C were associated with increased mean liner wear rates compared to patients in Group A (0.133 mm/yr (SD 0.21) vs 0.031 mm/yr (SD 0.07), respectively; p < 0.001) and Group B (0.133 mm/yr (SD 0.21) vs 0.022 mm/yr (SD 0.05), respectively; p < 0.001) at ten years’ follow-up. Patients in Group C were also associated with increased risk of osteolysis and aseptic loosening requiring revision surgery, compared with patients in Group A (7/133 vs 0/133, respectively; p = 0.007) and Group B (7/133 vs 0/135, respectively; p = 0.007). There was a non-statistically significant trend towards increased mean liner wear rates in Group A compared with Group B (0.031 mm/yr (SD 0.07) vs 0.022 mm/yr (SD 0.05), respectively; p = 0.128). All three groups were statistically comparable preoperatively and at ten years’ follow-up when measuring normalized Western Ontario and McMaster Universities Osteoarthritis Index (p = 0.410), 36-Item Short Form Health Survey (p = 0.465 mental, p = 0.713 physical), and pain scale scores (p = 0.451). Conclusion. The use of UHMWPE was associated with progressively increased annual liner wear rates after THA compared to XLPE. At ten years’ follow-up, the group receiving UHMWPE demonstrated an increased incidence of osteolysis and aseptic loosening requiring revision surgery compared to XLPE. Femoral heads composed of OxZr were associated with trend towards reduced wear rates compared to CoCr, but this did not reach statistical significance and did not translate to any differences in osteolysis, functional outcomes, or revision surgery between the two femoral head components. Cite this article: Bone Joint J 2022;104-B(7):833–843

Aims

We present the ten-year data of a cohort of patients, aged between 18 and 65 years (mean age 52.7 years; 19 to 64), who underwent total hip arthroplasty. Patients were randomised to be treated with a cobalt-chrome (CoCr) femoral head with an ultra-high molecular weight polyethylene (UHMWPE), highly cross-linked polyethylene (XLPE) or ceramic-on-ceramic (CoC) bearing surface.

Aims. The aim of this prospective cohort study was to evaluate the early migration of the TriFit cementless proximally coated tapered femoral stem using radiostereometric analysis (RSA). Methods. A total of 21 patients (eight men and 13 women) undergoing primary total hip arthroplasty (THA) for osteoarthritis of the hip were recruited in this study and followed up for two years. Two patients were lost to follow-up. All patients received a TriFit stem and Trinity Cup with a vitamin E-infused highly cross-linked ultra-high molecular weight polyethylene liner. Radiographs for RSA were taken postoperatively and then at three, 12, and 24 months. Oxford Hip Score (OHS), EuroQol five-dimension questionnaire (EQ-5D), and adverse events were reported. Results. At two years, the mean subsidence of the head and tip for the TriFit stem was 0.38 mm (SD 0.32) and 0.52 mm (SD 0.36), respectively. The total migration of the head and tip was 0.55 mm (SD 0.32) and 0.71 mm (SD 0.38), respectively. There were no statistically significant differences between the three to 12 months' migration (p = 0.105) and 12 to 24 months' migration (p = 0.694). The OHS and EQ-5D showed significant improvements at two years. Conclusion. The results of this study suggest that the TriFit femoral stem achieves initial stability and is likely to be stable in the mid and long term. A long-term outcome study is required to assess late mechanisms of failure and the effects of bone mineral density (BMD) related changes. Cite this article: Bone Joint J 2021;103-B(4):644–649

Majority of ultra-high molecular weight polyethylene (UHMWPE) medical devices used in total joint arthroplasty are crosslinked using gamma radiation to improve wear resistance. Alternative methods of crosslinking are urgently needed to replace gamma radiation due to rapid decline in its supply. Peroxide crosslinking is a candidate method with widespread industrial applications. Oxidative stability and biocompatibility, which are critical requirements for medical device applications, can be achieved using vitamin-E as an additive and by removing peroxide by-products through high temperature melting, respectively. We investigated compression molded UHMWPE/vitamin-E/di-cumyl peroxide blends followed by high-temperature melting in inert gas as a material candidate for tibial knee inserts. Wear resistance increased and mechanical properties remained largely unchanged. Oxidation induction time was higher than most of the other clinically available formulations. The material passed the local-end point biocompatibility tests per ISO 10993. Compounds found in exhaustive extraction were of no concern with margin-of-safety values well above the accepted level, indicating a desirable toxicological risk profile. Peroxide crosslinked, vitamin-E stabilized, and high temperature melted UHMWPE has recently been cleared for clinical use in tibial knee inserts. With all the salient characteristics needed in a material that can provide superior long-term performance in total joint patients, peroxide crosslinking can replace gamma radiation crosslinking of UHMWPE for use in all total joint replacement implant including acetabular liners

The design of the Charnley total hip replacement follows the principle of low frictional torque. It is based on the largest possible difference between the radius of the femoral head and that of the outer aspect of the acetabular component. The aim is to protect the bone-cement interface by movement taking place at the smaller radius, the articulation. This is achieved in clinical practice by a 22.225 mm diameter head articulating with a 40 mm or 43 mm diameter acetabular component of ultra-high molecular weight polyethylene. We compared the incidence of aseptic loosening of acetabular components with an outer diameter of 40 mm and 43 mm at comparable depths of penetration with a mean follow-up of 17 years (1 to 40). In cases with no measurable wear none of the acetabular components were loose. With increasing acetabular penetration there was an increased incidence of aseptic loosening which reflected the difference in the external radii, with 1.5% at 1 mm, 8.8% at 2 mm, 9.7% at 3 mm and 9.6% at 4 mm of penetration in favour of the larger 43 mm acetabular component. Our findings support the Charnley principle of low frictional torque. The level of the benefit is in keeping with the predicted values

This study reports the ten-year outcomes of a three-arm, multicentre randomised controlled trial comparing Cobalt-Chrome (CoCr) and Oxidised Zirconium (OxZr) femoral heads with ultra-high molecular weight polyethylene (UHMWPE) versus highly cross-linked polyethylene (XLPE) liners in total hip arthroplasty (THA). Patients undergoing THA from four institutions were prospectively randomised into three groups. Group A received a CoCr femoral head and XLPE liner; Group B received an OxZr femoral head and XLPE liner; and Group C received an OxZr femoral head and UHMWPE liner. The outcomes of 262 study patients were analysed at ten years follow-up. At ten years, increased linear wear rates were recorded in group C compared to group A (0.133 ± 0.21 mm/yr vs 0.031 ± 0.07 mm/yr respectively, p<0.001) and group B (0.133 ± 0.21 mm/yr vs 0.022 ± 0.05 mm/yr respectively, p<0.001). Patients in group C had increased risk of osteolysis and aseptic loosening requiring revision surgery compared with group A (7/133 vs 0/133 respectively, p=0.007) and group B (7/133 vs 0/135 respectively, p=0.007). There was a non- significant trend towards increased liner wear rates in group A compared to group B (0.031 ± 0.07 mm/yr vs 0.022 ± 0.05 mm/yr respectively, p=0.128). All three groups were statistically comparable preoperatively and at ten years follow-up from a clinical score perspective. The use of UHMWPE was associated with progressively increased annual liner wear rates. At ten years follow-up, this translated to an increased incidence of osteolysis and aseptic loosening requiring revision, compared with XLPE. Femoral heads composed of OxZr were associated with a non-significant trend towards reduced wear rates compared to CoCr, but this did not translate to any differences in osteolysis, functional outcomes, or revision surgery between the two treatments groups

This study reports the ten-year polyethylene liner wear rates, incidence of osteolysis, clinical outcomes and complications of a three-arm, multicentre randomised controlled trial comparing Cobalt-Chrome (CoCr) and Oxidised Zirconium (OxZr) femoral heads with ultra-high molecular weight polyethylene (UHMWPE) versus highly cross-linked polyethylene (XLPE) liners in total hip arthroplasty (THA). Patients undergoing THA from four institutions were prospectively randomised into three groups. Group A received a CoCr femoral head and XLPE liner; Group B received an OxZr femoral head and XLPE liner; and Group C received an OxZr femoral head and UHMWPE liner. Blinded observers recorded predefined outcomes in 262 study patients at regular intervals for ten years following THA. At ten years follow-up, increased linear wear rates were recorded in group C compared to group A (0.133 ± 0.21 mm/yr vs 0.031 ± 0.07 mm/yr respectively, p<0.001) and group B (0.133 ± 0.21 mm/yr vs 0.022 ± 0.05 mm/yr respectively, p<0.001). Patients in group C were associated with increased risk of osteolysis and aseptic loosening requiring revision surgery compared with group A (7/133 vs 0/133 respectively, p=0.007) and group B (7/133 vs 0/135 respectively, p=0.007). There was a non-significant trend towards increased liner wear rates in group A compared to group B (0.031 ± 0.07 mm/yr vs 0.022 ± 0.05 mm/yr respectively, p=0.128). All three groups were statistically comparable preoperatively and at ten years follow-up when measuring normalised Western Ontario and McMaster Universities Osteoarthritis Index(p=0.410), short-form-36 (p = 0.465 mental, p = 0.713 physical), and pain scale scores (p=0.451). The use of UHMWPE was associated with progressively increased annual liner wear rates after THA. At ten years follow-up, this translated to UHMWPE leading to an increased incidence of osteolysis and aseptic loosening requiring revision THA, compared with XLPE. Femoral heads composed of OxZr were associated with a non-significant trend towards reduced wear rates compared to CoCr, but this did not translate to any differences in osteolysis, functional outcomes, or revision surgery between the two treatments groups

Oxidised zirconium (OxZi) has been developed as an alternative bearing surface for femoral heads in total hip arthroplasty (THA). This study has investigated polyethylene wear, functional outcomes and complications, comparing OxZi and cobalt–chrome (CoCr) as part of a three-arm, multicentre randomised controlled trial. Patients undergoing THA from four institutions were prospectively randomised into three groups. Group A received a CoCr femoral head and highly cross-linked polyethylene (XLPE) liner; Group B received an OxZi femoral head and XLPE liner; Group C received an OxZi femoral head and ultra-high molecular weight polyethylene (UHMWPE) liner. At five years, 368 patients had no statistically significant differences in short-form-36 (p = 0.176 mental, p = 0.756 physical), Western Ontario and McMaster Universities Osteoarthritis Index (p = 0.847), pain scores (p = 0.458) or complications. The mean rate of linear wear was 0.028 mm/year (standard deviation (. sd) 0.010). for Group A, 0.023 mm/year (. sd. 0.010) for Group B, and 0.09 mm/year (. sd. 0.045) for Group C. Penetration was significantly higher in the UHMWPE liner group compared with both XLPE liner groups (p < 0.001) but no significant difference was noted between CoCr and OxZi when articulating with XLPE (p = 0.153). In this, the largest randomised study of this bearing surface, it appears that using a XLPE acetabular liner is more important in reducing THA component wear than the choice of femoral head bearing, at mid-term follow-up. There is a non-significant trend towards lower wear, coupling OxZi rather than CoCr with XLPE but long-term analysis is required to see if this observation changes with time and becomes significant. Cite this article: Bone Joint J 2015;97-B:883–9

It has been suggested that the wear of ultra-high molecular weight polyethylene (UHMWPE) in total hip replacement is substantially reduced when the femoral head is ceramic rather than metal. However, studies of alumina and zirconia ceramic femoral heads on the penetration of an UHMWPE liner in vivo have given conflicting results. The purpose of this study was to examine the surface characteristics of 30 alumina and 24 zirconia ceramic femoral heads and to identify any phase transformation in the zirconia heads. We also studied the penetration rate of alumina and zirconia heads into contemporary UHMWPE liners. The alumina heads had been implanted for a mean of 11.3 years (8.1 to 16.2) and zirconia heads for a mean of 9.8 years (7.5 to 15). The mean surface roughness values of the explanted alumina heads (Ra 40.12 nm and Rpm 578.34 nm) were similar to those for the explanted zirconia heads (Ra 36.21 nm and Rpm 607.34 nm). The mean value of the monoclinic phase of two control zirconia heads was 1% (0.8% to 1.5%) and 1.2% (0.9% to 1.3%), respectively. The mean value of the monoclinic phase of 24 explanted zirconia heads was 7.3% (1% to 26%). In the alumina group, the mean linear penetration rate of the UMWPE liner was 0.10 mm/yr (0.09 to 0.12) in hips with low Ra and Rpm values (13.22 nm and 85.91 nm, respectively). The mean linear penetration rate of the UHMWPE liner was 0.13 mm/yr (0.07 to 0.23) in hips with high Ra and Rpm values (198.72 nm and 1329 nm, respectively). This difference was significant (p = 0.041). In the zirconia head group, the mean linear penetration rate of the UHMWPE liner was 0.09 mm/yr (0.07 to 0.14) in hips with low Ra and Rpm values (12.78 nm and 92.99 nm, respectively). The mean linear penetration rate of the UHMWPE liner was 0.12 mm/yr (0.08 to 0.22) in hips with high Ra and Rpm values (199.21 nm and 1381 nm, respectively). This difference was significant (p = 0.039). The explanted zirconia heads which had a minimal phase transformation had similar surface roughness and a similar penetration rate of UHMWPE liner as the explanted alumina head

Introduction. Ultra-high molecular weight polyethylene (UHMWPE) can provide local sustained delivery of therapeutics. 1,2. For example, it can deliver analgesics to address post-arthroplasty pain. 2. Given that several analgesics, such as bupivacaine (anesthetic) and tolfenamic acid (NSAID), were shown to possess antibacterial activity against Staphylococci, we hypothesize that analgesic-loaded UHMWPE can also yield antimicrobial effects, preventing the development of periprosthetic joint infections. Methods. Bupivacaine and tolfenamic acid were incorporated into UHMWPE via phase-separated compression molding. Drug release from the prepared samples was measured using high-performance liquid chromatography. Antibacterial studies of the obtained materials were conducted against methicillin-sensitive, and methicillin-resistant S. aureus, as well as S. epidermidis. Time-kill curves were obtained to characterize antimicrobial activity against planktonic bacteria. The dynamics of bacterial adhesion were assessed to characterize antibiofilm activity. Scanning electron microscopy (SEM) was used to visualize adherent bacteria. Anticolonizing activity of the tested materials was characterized using the “daughter cell” method as outlined elsewhere. 3. Cytotoxicity profile of drug-loaded UHMWPEs was evaluated using MG-63 osteoblast cell line. Results. The bupivacaine release rate generally increased with increasing drug loading (e.g. a model knee implant loaded with bupivacaine would release ca. 15–500 mg over 24 hours). While also proportional, drug release from UHMWPE loaded with tolfenamic acid was much lower. The bacterial viability curves showed that bupivacaine-loaded UHMWPE possessed moderate antibacterial activity against planktonic MSSA, MRSA, and S. epidermidis, slowing bacteria proliferation by up to 70%. Bupivacaine-loaded UHMWPE also mitigated biofilm formation and development during the initial culture period. SEM images confirmed the observed antibiofilm effect (Fig. 1). Tolfenamic acid-loaded UHMWPE allowed proliferation of planktonic bacteria. At the same time, these materials showed pronounced dose-dependent anticolonizing activity against tested strains, providing 3-log reduction of “daughter” cells. Bupivacaine- and tolfenamic acid-loaded UHMWPEs showed little-to-no cytotoxicity against osteoblasts. Discussion & Conclusions. We demonstrated for the first time that bupivacaine-loaded UHMWPE possesses dose-dependent antibacterial properties against planktonic and adherent MSSA, MRSA, and S. epidermidis – pathogens commonly associated with periprosthetic joint infections. Pronounced anticolonizing activity was evident for tolfenamic acid-loaded UHMWPE. Due to the low solubility of tolfenamic acid, the material's antibacterial effect against planktonic bacteria was lower. These results demonstrate that analgesic-loaded UHMWPE, used as a tool in multimodal pain management, can also yield antibacterial effects, opening an entirely new avenue for providing post-arthroplasty antibacterial prophylaxis. This pioneering approach has a potential to reduce patients' morbidity and mortality after arthroplasty. For any tables or figures, please contact the authors directly

Osteolysis secondary to ultra-high molecular weight polyethylene (UHMWPE) wear is a leading cause of late-term implant failure via aseptic loosening in patients treated with total hip arthroplasty (THA). Radiation crosslinking of UHMWPE has been shown to decrease wear. However, the resulting polymer (crosslinked-PE) has a high free radical content. Two different methods that have been used to reduce the remaining free radicals are mechanical annealing and chemical stabilization using Vitamin E, a free radical scavenger. The primary purpose of the current study was to evaluate and compare the wear properties of vitamin E-doped crosslinked-PE (VEPE) and one formulation of mechanically annealed crosslinked-PE using radiostereometric analysis (RSA) in patients five years after primary THA. We also sought to understand the association between polyethylene wear and patient-reported outcome measures (PROMs). Three-hundred and five patients from six international centers were enrolled. Seventy-six percent were treated with highly-crosslinked (95 kGy) VEPE liners, and the rest received moderately-crosslinked (50 kGy) (ModXL), mechanically annealed liners. Data was collected prospectively at one-, two-, and five-year intervals. At the 5-year follow-up, proximal femoral head penetration into the VEPE liners (median = 0.05mm (range, −0.03–1.20)) was significantly lower than the penetration into the ModXL liners (median = 0.15mm (range, −0.22–1.04)) (p<0.001). In the VEPE cohort the median proximal penetration did not increase from one- to five-year follow-up (p=0.209). In contrast, there was a significant increase in femoral head penetration for the ModXL group (p<0.001) during that same time. Multivariable regression showed that the only variable predictive of increased wear was ModXL liner type (B=0.12, p<0.001). There were no differences in PROMs between the liner groups, and there was no correlation between polyethylene wear and PROMs for the cohort as a whole. The current study is the largest analysis of polyethylene wear at five-year follow-up using the RSA technique. We observed similar bedding in through the two-year interval between the two liner types, however, there was significantly more wear in the ModXL cohort at five-years. Currently, the wear rates for both liner groups are below the osteolysis threshold and have not led to any implant failures via aseptic loosening. Continued follow-up will provide a better understanding of the association between wear rate and clinical outcomes

Introduction. Reverse hybrid total hip replacement (THR) offers significant theoretical benefits but is uncommonly used. Our primary objective was to evaluate implant survival with all cause revision and revision for aseptic loosening of either component as endpoints. Patients/Materials & Methods. Data was collected prospectively on 1, 088 (988 patients) consecutive reverse hybrid THRs. Mean patient age was 69.3 years (range, 21–94) and mean follow-up was 8.2 years (range, 5–11.3). No patients were lost to follow-up. Overall, 194 (17.8%) procedures were performed in patients under 60 years, 666 (61.1%) were performed in female patients and 349 (32.1%) were performed by a trainee. Acetabular components were ultra-high molecular weight polyethylene in 415 (38.1%) hips, highly cross-linked polyethylene in 669 (61.5%) hips and vitamin E stabilised polyethylene in 4 (0.4%) hips. Femoral stems were collared in 757 (69.7%) hips and collarless in 331 (30.3%) hips. Femoral head sizes were 28 mm in 957 (87.9%) hips and 32 mm in 131 (12.1%) hips. Survival analysis was performed using Kaplan Meier methodology. Log rank tests were used to asses differences in survival by age, gender, head size and surgeon grade. Results. Ten-year implant survival (122 hips at risk) was 97.2% (95% CI 95.8–98.1%) for all cause revision (Figure 1), 100% for aseptic acetabular loosening and 99.6% (95% CI 99.0–99.9%) for aseptic stem loosening (Figure 2). There was no difference in implant survival by age (p = 0.39), gender (p = 0.68), head size (p = 0.76) or surgeon grade (p = 0.20) for all cause revision. There was no difference in survival by gender (p = 0.12), head size (p = 0.38) or surgeon grade (p = 0.76) for stem revision. Four (0.4%) stems failed at mean 2.5 years (range, 0.6–4.8) because they were undersized. These were associated with patient age under 60 years (p = 0.015). Discussion. This is the largest reported study on the outcomes of reverse hybrid THR in a consecutive series of patients at medium to long term follow-up. Cemented acetabular components are less costly than uncemented cups and offer other significant benefits such as improved fixation in osteoporotic or pathological bone, reduced risk of intraoperative periprosthetic fracture, easier revision and local antibiotic delivery which can reduce deep infection rates. Advantages of uncemented stems over cemented stems include biological fixation, shorter operating times, fewer adverse pulmonary events and reduced proximal stress shielding. Our results indicate high implant survival rates at ten-year follow-up with low rates of aseptic loosening (0.4%). Meticulous surgical technique is required to avoid stem undersizing which may lead to early failure particularly in younger patients. Conclusion. This study confirms that reverse hybrid THR offers highly successful outcomes, irrespective of age, gender, head size and surgeon grade. For any figures and tables, please contact the authors directly

Aims

This study reports the results of 38 total hip arthroplasties (THAs) in 33 patients aged less than 50 years, using the JRI Furlong hydroxyapatite ceramic (HAC)-coated femoral component.

Aims

The primary outcome was investigating differences in wear, as measured by femoral head penetration, between cross-linked vitamin E-diffused polyethylene (vE-PE) and cross-linked polyethylene (XLPE) acetabular component liners and between 32 and 36 mm head sizes at the ten-year follow-up. Secondary outcomes included acetabular component migration and patient-reported outcome measures (PROMs) such as the EuroQol five-dimension questionnaire, 36-Item Short-Form Health Survey, Harris Hip Score, and University of California, Los Angeles Activity Scale (UCLA).

Aims

BoneMaster is a thin electrochemically applied hydroxyapatite (HA) coating for orthopaedic implants that is quickly resorbed during osseointegration. Early stabilization is a surrogacy marker of good survival of femoral stems. The hypothesis of this study was that a BoneMaster coating yields a fast early and lasting fixation of stems.

Aims

The aim of this study was to evaluate the performance of first-generation annealed highly cross-linked polyethylene (HXLPE) in cementless total hip arthroplasty (THA).

Aims

We aimed to investigate if the use of the largest possible cobalt-chromium head articulating with polyethylene acetabular inserts would increase the in vivo wear rate in total hip arthroplasty.

Aims

We present the results, in terms of survival, clinical outcome, and radiological appearance at 20 years, in a cohort of 225 cemented Exeter Universal femoral components (Stryker, Newbury, UK) implanted in 207 patients, at a district general hospital.

The creep and wear behaviour of highly cross-linked polyethylene and standard polyethylene liners were examined in a prospective, double-blind randomised, controlled trial using radiostereometric analysis.

We randomised 54 patients to receive hip replacements with either highly cross-linked polyethylene or standard liners and determined the three-dimensional penetration of the liners over three years.

After three years the mean total penetration was 0.35 mm (SD 0.14) for the highly cross-linked polyethylene group and 0.45 mm (SD 0.19) for the standard group. The difference was statistically significant (p = 0.0184). From the pattern of penetration it was possible to discriminate creep from wear. Most (95%) of the creep occurred within six months of implantation and nearly all within the first year. There was no difference in the mean degree of creep between the two types of polyethylene (highly cross-linked polyethylene 0.26 mm, SD 0.17; standard 0.27 mm, SD 0.2; p = 0.83). There was, however, a significant difference (p = 0.012) in the mean wear rate (highly cross-linked polyethylene 0.03 mm/yr, SD 0.06; standard 0.07 mm/yr, SD 0.05). Creep and wear occurred in significantly different directions (p = 0.01); creep was predominantly proximal whereas wear was anterior, proximal and medial.

We conclude that penetration in the first six months is creep-dominated, but after one year virtually all penetration is due to wear. Highly cross-linked polyethylene has a 60% lower rate of wear than standard polyethylene and therefore will probably perform better in the long term.

Aims

The aim of this study was to describe temporal trends and survivorship of total hip arthroplasty (THA) in very young patients, aged ≤ 20 years.