We present here a case of pseudotumor formation likely due to metal wear debris generated at the head-neck taper (trunnion) of the femoral stem and head components in a metal-on-highly cross-linked polyethylene (MOP) total hip arthroplasty. Over the last few years, this recently described diagnosis, trunnionosis, is being recognized and reported more frequently. This patient presented with a rather large (12 cm diameter) pseudotumor with accompanying loss of abductors and a pelvic discontinuity making reconstruction more challenging. We believe the psuedotumor in this patient developed from trunnionosis. This is an interesting case of aseptic lymphocyte-dominated vasculitis-associated lesions (ALVAL) in a MOP total hip arthroplasty.

The Accolade®TMZF is a taper-wedge cementless metaphyseal coated femoral stem widely utilized from 2002-2012. In recent years, there have been reports of early catastrophic failure of this implant. Establishing a deeper understanding of the rate and causes of revision in patients who developed aseptic failure in stems with documented concerns about high failure rates is critical. Understanding any potential patient or implant factors which are risk factors for failure is important to inform both clinicians and patients. We propose a study to establish the long-term survival of this stem and analyze patients who underwent aseptic revision to understand the causes and risk factors for failure. A retrospective review was undertaken of all patients who received a primary total hip arthroplasty with an Accolade® TMZF stem at a high-volume arthroplasty center. The causes and timing of revision surgery were documented and cross referenced with the Canadian Institute of Health Information Discharge Abstract Database to minimize loss to follow-up. Survivorship analysis was performed with use of the Kaplan-Meier curves to determine the overall and aseptic survival rates at final follow-up. Patient and implant factors commonly associated with aseptic failure were extracted and Cox proportional hazards model was used. A consecutive series of 2609 unilateral primary THA patients implanted with an Accolade®TMZF femoral hip stem were included. Mean time from primary surgery was 12.4 years (range 22 days to 19.5 years). Cumulative survival was 96.1% ± 0.2 at final follow-up. One hundred and seven patients underwent revision surgery with aseptic loosening of the femoral component was the most common cause of aseptic failure in this cohort (33/2609, 1.3%). Younger age and larger femoral head offset were independent risk factors for aseptic failure. To our knowledge, this is the largest series representing the longest follow-up of this taper-wedge cementless femoral implant. Despite early concerns, the Accolade® TMZF stem has excellent survivorship in this cohort. Trunnionosis as a recognized cause for revision surgery was rare. Younger age and larger femoral head offset were independent risk factors for aseptic failure

Metal Ion Levels Not Useful in Failed M-O-M Hips: Systematic Review; Revision of Failed M-O-M THA at a Tertiary Center; Trunnionosis in Metal-on-Poly THA?; Do Ceramic Heads Eliminate Trunnionosis?; Iliopsoas Impingement After 10 THA; Pain in Young, Active Patients Following THA; Pre-operative Injections Increase Peri-prosthetic THA Infection; Debridement and Implant Retention in THA Infection; THA after Prior Lumbar Spinal Fusion; Lumbar Back Surgery Prior to THA Associated with Worse Outcomes; Raising the Joint Line Causes Mid-Flexion Instability in TKA; No Improvement in Outcomes with Kinematic Alignment in TKA; Botox For TKA Flexion Contracture; Intra-operative Synovitis Predicts Worse Outcomes After TKA for OA; When is it Safe for Patients to Drive After Right TKA?; Alpha-Defensin for Peri-prosthetic Joint Infection; Medial Tibia Overhang and Pain Score After TKA

Trunnionosis in modular hip arthroplasty has recently been recognised to be clinically important. Gaining an understanding of how the material interface at the head-trunnion affects the tribology at the modular junctions has current clinical implications as well as an implication on future implant selection and material choice. This matched-cohort study aims to compare tribocorrosion between ceramic and cobalt-chromium trunnions and to investigate other factors that contribute to the difference in tribocorrosion if present. All hip prostheses retrieved between 1999 and 2015 at one centre were reviewed. Fifty two ceramic heads were retrieved, and these were matched to a cobalt-chromium cohort according to taper design, head size, neck length and implantation time in that order. The two cohorts were similar in male:female ratio (p=0.32) and body mass index (p=0.15) though the ceramic group was younger than the cobalt-chromium group (56.6 (+/−)13.5 years for ceramic group vs 66.3 (+/−14.4) years for cobalt-chromium group; p=0.001). There was no significant difference in the reasons for revision between the two groups (p=0.42). The femoral head trunnions were examined by two independent observers using a previously published 4-point scoring technique. The trunnions were divided into three zones: apex, middle and base. The observers were blinded to clinical and manufacturing data where possible. Ceramic head trunnions demonstrated a lower median fretting and corrosion score at the base zone (p<0.001), middle zone (p<0.001) and in the combined score (p<0.001). In a subgroup analysis by head size, ceramic heads had a lower fretting and corrosion score at 28mm head diameter (p<0.001). Within the ceramic group, taper design had a significant effect on fretting and corrosion in the apex zone (p=0.04). Taper design also had a similar effect in the cobalt-chromium group in the apex zone (p=0.03). For the ceramic trunnions, the largest effect was contributed by the difference between the 11/13 taper and the 12/14 taper. For the cobalt-chromium trunnions, the largest effect was contributed by the difference between the 5 degree 38′ 37″ taper and type 1 taper. Ceramic head trunnions showed a significantly lower fretting and corrosion score as compared to cobalt-chromium trunnions. Ceramic heads had a lower score than cobalt-chromium heads at 28mm head diameter. Taper design had an effect on fretting and corrosion within each cohort