Introduction. In total hip arthroplasty ceramic on ceramic bearing couples are used more and more frequently and on a wordwide basis. The main reason of this choice is reduction of wear debris and osteolysis. The tribological properties and the mechanical behaviour of the implanted ceramic must remain the same throughout the patient's life. The aim of this study was to evaluate the resistance of Alumina Matrix Composite to environmental degradation. Material and method. The alumina matrix composite or BIOLOX ® delta is manufactured in Germany by CeramTec. It is made up of 80 vol.% Al2O3, 17 vol.% Yttria Stabilized ZrO2 and 3vol.% strontium aluminate platelets. The zirconia grains account for 1.3 mol.% of the Yttria content. Accelerated aging tests in water steam at 142°C, 134°C, 121°C, and 105°C were performed to evaluate the aging kinetics of the composite. X-ray diffraction was used to determine the monoclinic phase content on the material surface. Phase transformation is associated with weakness and increase in roughness of zirconia ceramic implants. Results. The data below shows average monoclinic contents before and after aging in water vapour according to the ISO standard test (134°C, 2 bars water steam, 10 h) on the surface and inside the 28 mm taper(12/14 taper) femoral ball heads manufactured in alumina ceramic composite. There are precisions concerning the roughness and the load to failure before and after aging concerning 28mm diameter heads. Before Aging 13%+/-3% of Monoclinic content. After 10 H at 134°C23%+/-3% of Monoclinic content the roughness of the polished surface remain the same (5nm+/− 2). The load to failure of 28 mm heads before aging is 76 kN +/− 5kN, and 72 kN +/− 5kN after aging. The results show that although a rise in monoclinic content is predictable after long aging duration in vivo, the impact of the transformation is quite different to monolithic zirconia. A zirconia femoral head exhibits an important increase of roughness from 2 nm to more than 50 nm when submitted to the same duration of ageing. Other tests with hip simulators under severe micro separation have been done to analyse the impact of aging on wear performance. The main wear zone on femoral heads underwent a phase transformation from tetragonal to monoclinic (23% monoclinic) at 5 milion cycles duration without any change in roughness after 5Mc duration. Conclusion. This experimental testing program has enabled a prediction for the long-term in vivo environmental resistance of prostheses made out of Alumina Matrix Composite. The substantial improvement in mechanical properties and the excellent wear behaviour, even under severe microseparation conditions has been clinically confirmed. Today more than 960,000 ceramic ball heads and more than 450 000 ceramic inserts made of the alumina matrix composite have been implanted. Additionally, due to enhanced mechanical behaviour, new applications in orthopaedics are possible

Due to increased life expectancy of human population, the amount of total knee replacements (TKR) is expected to increase. TKR reached a high grade of quality and safety, but most often it fail because of aseptic implant loosening caused by polyethylene (PE) wear debris. Wear is generated at the articulating surfaces, e.g. caused by three body particles, like bone fragments or bone cement particles. The aim of this experimental study was to compare the wear of tibial PE inserts combined with metallic and ceramic femoral components at three body wear situation induced by polymethylmethacrylate (PMMA) and zirconia (ZrO2) particles from the bone cement. Wear testing was performed for 5 Mio load cycles, using tibial standard PE inserts combined with the same CR femoral component, in two different materials, Cobalt Chromium (CoCrMo) and Biolox delta ® ceramic (Multigen Plus Knee System, Lima Corporate, Italy). A knee wear simulator, according to ISO 14243 (EndoLab GmbH, Rosenheim, Germany), was used to carry out the tests. The tests were performed in temperature-controlled test chambers at 37 °C, containing calf serum with a protein content of 30 g/l. Polymethylmethacrylate (PMMA) and zirconia (ZrO2) bone cement particles (Palacos R ®) were manufactured to a size of 30 μm. The three body particles were added at all stations onto the articulating surface of the tibial PE insert (7mg per condyle) at every 500,000 cycles. Wear was determined gravimetrically and the surfaces of tibial inserts were analysed by scanning electron microscope (SEM) after finishing the 5 million cycles. Furthermore, roughness of the PE insert surfaces and the articulating surfaces of the different femoral components were detected and the PE wear particles were analysed by SEM. The average gravimetrical wear rates of the tibial PE inserts in combination with CoCr and Biolox delta ® ceramic femoral components amounted to 6.4 ± 0.9 mg and 2.6 ± 0.4 mg per million cycles, respectively. Beside bone cement particles on the articulating surface of the PE inserts, polished surfaces and scratches were detected by SEM. In comparison to the untreated surfaces of the PE inserts at both material pairings the surface roughness at the articulating areas showed deep scratches and polished regions. Analyses of the metallic femoral components showed scratches at the articulating surfaces, none on ceramics. The present study pointed out the effect of femoral component material in an abrasive three body wear situation on the wear properties of TKR. The wear simulator tests showed that wear of PE inserts under three body wear conditions, in combination with ceramic femoral components, was significantly lower than with metallic femoral components. With regard to anti-allergic properties, ceramic femoral components are promising products for TKR

Introduction. Oxidized zirconium (OxZr) is used as a ceramic surface for femoral components in total knee arthroplasty (TKA). The aim of this study was to investigate its performance by examining retrieved femoral components and their corresponding PE inserts in matched comparison with conventional chrome/cobalt/molybdenum alloy (CrCoMo). Methods. 11 retrieved posterior stabilized (PS) TKA with an OxZr femoral component were included. From a cohort of 56 retrieved TKA with CrCoMo femoral components, pairs were matched according to duration of implantation, patient age, reason for revision, and BMI. The retrieved tibial polyethylene (PE) inserts were analyzed for wear using the Hood classification. Femoral components were optically viewed at 8–32x magnification and screened for scratching, pitting, delamination, and striation. Profilometry was performed to measure surface roughness of the OxZr components using a non-contact white light profiler. Results. The prostheses were in situ for a mean of 18.5±10.6 (OxZr) and 19.5±14.3 (CrCoMo) months (p=0.41). None of these cases were revised for problems directly related to the use of OxZr. There was one reaction to the implant in the CrCoMo group. The average wear of the tibial PE inserts was significantly lower with OxZr components (41.5±16.8 vs. 60.1±22.0, p=0.01). The average wear score in the visual analysis of the femoral components was significantly lower for the OxZr (1.6±1.3 vs. 9.5±0.6, p=0.005). Discussion and Conclusion. Femoral components made of OxZr are less sensitive to in vivo wear damage than those of CrCoMo. PE inlays show significantly less in vivo wear damage in combination with an OxZr femoral component

Our aim in this pilot study was to evaluate the fixation of, the bone remodelling around, and the clinical outcome after surgery of a new, uncemented, fully hydroxyapatite-coated, collared and tapered femoral component, designed specifically for elderly patients with a fracture of the femoral neck.

We enrolled 50 patients, of at least 70 years of age, with an acute displaced fracture of the femoral neck in this prospective single-series study. They received a total hip replacement using the new component and were followed up regularly for two years.

Fixation was evaluated by radiostereometric analysis and bone remodelling by dual-energy x-ray absorptiometry. Hip function and the health-related quality of life were assessed using the Harris hip score and the EuroQol-5D.

Up to six weeks post-operatively there was a mean subsidence of 0.2 mm (−2.1 to +0.5) and a retroversion of a mean of 1.2° (−8.2° to +1.5°). No component migrated after three months. The patients had a continuous loss of peri-prosthetic bone which amounted to a mean of 16% (−49% to +10%) at two years. The mean Harris hip score was 82 (51 to 100) after two years.

The two-year results from this pilot study indicate that this new, uncemented femoral component can be used for elderly patients with osteoporotic fractures of the femoral neck.