Aims

This study reports the ten-year wear rates, incidence of osteolysis, clinical outcomes, and complications of a multicentre randomized controlled trial comparing oxidized zirconium (OxZr) versus cobalt-chrome (CoCr) femoral heads with ultra-high molecular weight polyethylene (UHMWPE) and highly cross-linked polyethylene (XLPE) liners in total hip arthroplasty (THA).

Oxidized zirconium (Oxinium) and highly cross-linked polyethylene (HXLPE) were developed with the purpose of minimizing wear, and subsequent osteolysis, in Total Hip Arthroplasty (THA). However, few articles have been published on long-term results of Oxinium on highly cross-linked polyethylene. The purpose of this investigation is to report minimum 10-year HXLPE wear rates and the clinical outcome of patients in this group and compare this population to a control group of cobalt chrome and ceramic. One hundred forty THAs were performed for 123 patients using an Oxinium head with an HXLPE liner. Ninety-seven had 10 years of clinical follow-up (avg. 14.5). Harris Hip Scores (HHS) were collected preoperatively and at the most recent follow-up. Radiographs of 85 hips were available for a minimum 10-year follow-up (avg. 14.5) and used to calculate wear using PolyWare software. Control groups of cobalt chrome and ceramic articulation on HXLPE with a minimum 10-year follow-up were studied. Clinical follow-up of the Oxinium group showed a statistical improvement compared to preoperative and was similar to the control group of patients. Radiographic evaluation found the linear and volumetric wear rates for the Oxinium group of 0.03 mm/year (range 0.00–0.08) and 3.46 mm. 3. /year (range 1.0 to 15.0) respectively. There was no statistically significant difference in linear or volumetric wear rate between the groups (P-value 0.92 and 0.55 respectively). None of these patients underwent revision of their hip for any reason. Oxinium on highly cross-linked polyethylene has performed exceptionally with wear rates comparable to those of cobalt chrome or ceramic on HXLPE

The purpose of this study was to precisely measure the 10-year polyethylene wear rate of primary total hips using Radiostereometric analysis (RSA) comparing Oxidized Zirconium (OxZi) to cobalt chrome (CoCr) femoral heads articulating with highly cross-linked polyethylene (XLPE). RSA was performed on 46 patients who underwent total hip arthroplasty − 23 who received OxZi femoral heads and 23 who received CoCr heads in combination with XLPE at a minimum of 10 years follow-up. All patients had identical THR systems implanted except for the femoral head utilized. The Centre Index method was utilised to assess total wear rates (from index surgery until final evaluation) using a dedicated RSA Software program (UmRSA Digital Measure v.2.2.1). In addition, the Martell technique was used to subtract head penetration occurring in the first 1–2 years (i.e. bedding-in phase) to allow calculation of the ‘steady state’ wear rates. There were no significant differences in demographics (i.e age, BMI, gender) between the groups. The average time from surgery of the RSA examinations was 11.7 and 12.6 years for the CoCr and OxZi groups respectively. Using the Centre Index Method to calculate total head penetration, wear rates were slightly higher in the OxZi group (0.048 +/− 0.021mm/year) compared to the CoCr group (0.035 +/− 0.017mm/year) with no statistical difference between the groups (p= 0.02). After correction for the bedding-in period, there was no statistically significant difference in mean ‘steady-state’ wear rate between OxZi (0.031 +/− 0.021mm/year) and CoCr (0.024 +/− 0.019mm/year) at 10 year follow up (p= 0.24). A comparison of preoperative and postoperative SF12, HHS, and WOMAC scores showed no statistical difference between the groups. RSA demonstrated the 10 year in-vivo wear rates of both bearing combinations to be well below the threshold for osteolysis. There was no significant difference between either the total or ‘steady-state’ wear rates of the OxZi and CoCr groups at 10 years

This study reports the ten-year polyethylene liner wear rates, incidence of osteolysis, clinical outcomes and complications of a three-arm, multicentre randomised controlled trial comparing Cobalt-Chrome (CoCr) and Oxidised Zirconium (OxZr) femoral heads with ultra-high molecular weight polyethylene (UHMWPE) versus highly cross-linked polyethylene (XLPE) liners in total hip arthroplasty (THA).

Patients undergoing THA from four institutions were prospectively randomised into three groups. Group A received a CoCr femoral head and XLPE liner; Group B received an OxZr femoral head and XLPE liner; and Group C received an OxZr femoral head and UHMWPE liner. Blinded observers recorded predefined outcomes in 262 study patients at regular intervals for ten years following THA.

At ten years follow-up, increased linear wear rates were recorded in group C compared to group A (0.133 ± 0.21 mm/yr vs 0.031 ± 0.07 mm/yr respectively, p<0.001) and group B (0.133 ± 0.21 mm/yr vs 0.022 ± 0.05 mm/yr respectively, p<0.001). Patients in group C were associated with increased risk of osteolysis and aseptic loosening requiring revision surgery compared with group A (7/133 vs 0/133 respectively, p=0.007) and group B (7/133 vs 0/135 respectively, p=0.007). There was a non-significant trend towards increased liner wear rates in group A compared to group B (0.031 ± 0.07 mm/yr vs 0.022 ± 0.05 mm/yr respectively, p=0.128). All three groups were statistically comparable preoperatively and at ten years follow-up when measuring normalised Western Ontario and McMaster Universities Osteoarthritis Index(p=0.410), short-form-36 (p = 0.465 mental, p = 0.713 physical), and pain scale scores (p=0.451).

The use of UHMWPE was associated with progressively increased annual liner wear rates after THA. At ten years follow-up, this translated to UHMWPE leading to an increased incidence of osteolysis and aseptic loosening requiring revision THA, compared with XLPE. Femoral heads composed of OxZr were associated with a non-significant trend towards reduced wear rates compared to CoCr, but this did not translate to any differences in osteolysis, functional outcomes, or revision surgery between the two treatments groups.

This study reports the ten-year outcomes of a three-arm, multicentre randomised controlled trial comparing Cobalt-Chrome (CoCr) and Oxidised Zirconium (OxZr) femoral heads with ultra-high molecular weight polyethylene (UHMWPE) versus highly cross-linked polyethylene (XLPE) liners in total hip arthroplasty (THA).

Patients undergoing THA from four institutions were prospectively randomised into three groups. Group A received a CoCr femoral head and XLPE liner; Group B received an OxZr femoral head and XLPE liner; and Group C received an OxZr femoral head and UHMWPE liner. The outcomes of 262 study patients were analysed at ten years follow-up.

At ten years, increased linear wear rates were recorded in group C compared to group A (0.133 ± 0.21 mm/yr vs 0.031 ± 0.07 mm/yr respectively, p<0.001) and group B (0.133 ± 0.21 mm/yr vs 0.022 ± 0.05 mm/yr respectively, p<0.001). Patients in group C had increased risk of osteolysis and aseptic loosening requiring revision surgery compared with group A (7/133 vs 0/133 respectively, p=0.007) and group B (7/133 vs 0/135 respectively, p=0.007). There was a non- significant trend towards increased liner wear rates in group A compared to group B (0.031 ± 0.07 mm/yr vs 0.022 ± 0.05 mm/yr respectively, p=0.128). All three groups were statistically comparable preoperatively and at ten years follow-up from a clinical score perspective.

The use of UHMWPE was associated with progressively increased annual liner wear rates. At ten years follow-up, this translated to an increased incidence of osteolysis and aseptic loosening requiring revision, compared with XLPE. Femoral heads composed of OxZr were associated with a non-significant trend towards reduced wear rates compared to CoCr, but this did not translate to any differences in osteolysis, functional outcomes, or revision surgery between the two treatments groups.

Aims

The aim of this study was to evaluate fretting and corrosion in retrieved oxidized zirconium (OxZr; OXINIUM, Smith & Nephew, Memphis, Tennessee) femoral heads and compare the results with those from a matched cohort of cobalt-chromium (CoCr) femoral heads.