We report the five-year outcome of a randomised controlled trial which used radiostereometric analysis (RSA) to assess the influence of surface oxidised zirconium (OxZr, Oxinium) on polyethylene wear in vivo.

A total of 120 patients, 85 women and 35 men with a mean age of 70 years (59 to 80) who were scheduled for primary cemented total hip arthroplasty were randomly allocated to four study groups. Patients were blinded to their group assignment and received either a conventional polyethylene (CPE) or a highly cross-linked (HXL) acetabular component of identical design. On the femoral side patients received a 28 mm head made of either cobalt-chromium (CoCr) or OxZr.

The proximal head penetration (wear) was measured with repeated RSA examinations over five years. Clinical outcome was measured using the Harris hip score.

There was no difference in polyethylene wear between the two head materials when used with either of the two types of acetabular component (p = 0.3 to 0.6). When comparing the two types of polyethylene there was a significant difference in favour of HXLPE, regardless of the head material used (p < 0.001).

In conclusion, we found no advantage of OxZr over CoCr in terms of polyethylene wear after five years of follow-up. Our findings do not support laboratory results which have shown a reduced rate of wear with OxZr. They do however add to the evidence on the better resistance to wear of HXLPE over CPE.

Cite this article: Bone Joint J 2015;97-B:1463–9.

Oxidised zirconium (OxZi) has been developed as an alternative bearing surface for femoral heads in total hip arthroplasty (THA). This study has investigated polyethylene wear, functional outcomes and complications, comparing OxZi and cobalt–chrome (CoCr) as part of a three-arm, multicentre randomised controlled trial. Patients undergoing THA from four institutions were prospectively randomised into three groups. Group A received a CoCr femoral head and highly cross-linked polyethylene (XLPE) liner; Group B received an OxZi femoral head and XLPE liner; Group C received an OxZi femoral head and ultra-high molecular weight polyethylene (UHMWPE) liner. At five years, 368 patients had no statistically significant differences in short-form-36 (p = 0.176 mental, p = 0.756 physical), Western Ontario and McMaster Universities Osteoarthritis Index (p = 0.847), pain scores (p = 0.458) or complications. The mean rate of linear wear was 0.028 mm/year (standard deviation (. sd) 0.010). for Group A, 0.023 mm/year (. sd. 0.010) for Group B, and 0.09 mm/year (. sd. 0.045) for Group C. Penetration was significantly higher in the UHMWPE liner group compared with both XLPE liner groups (p < 0.001) but no significant difference was noted between CoCr and OxZi when articulating with XLPE (p = 0.153). In this, the largest randomised study of this bearing surface, it appears that using a XLPE acetabular liner is more important in reducing THA component wear than the choice of femoral head bearing, at mid-term follow-up. There is a non-significant trend towards lower wear, coupling OxZi rather than CoCr with XLPE but long-term analysis is required to see if this observation changes with time and becomes significant. Cite this article: Bone Joint J 2015;97-B:883–9

This study reports the ten-year polyethylene liner wear rates, incidence of osteolysis, clinical outcomes and complications of a three-arm, multicentre randomised controlled trial comparing Cobalt-Chrome (CoCr) and Oxidised Zirconium (OxZr) femoral heads with ultra-high molecular weight polyethylene (UHMWPE) versus highly cross-linked polyethylene (XLPE) liners in total hip arthroplasty (THA). Patients undergoing THA from four institutions were prospectively randomised into three groups. Group A received a CoCr femoral head and XLPE liner; Group B received an OxZr femoral head and XLPE liner; and Group C received an OxZr femoral head and UHMWPE liner. Blinded observers recorded predefined outcomes in 262 study patients at regular intervals for ten years following THA. At ten years follow-up, increased linear wear rates were recorded in group C compared to group A (0.133 ± 0.21 mm/yr vs 0.031 ± 0.07 mm/yr respectively, p<0.001) and group B (0.133 ± 0.21 mm/yr vs 0.022 ± 0.05 mm/yr respectively, p<0.001). Patients in group C were associated with increased risk of osteolysis and aseptic loosening requiring revision surgery compared with group A (7/133 vs 0/133 respectively, p=0.007) and group B (7/133 vs 0/135 respectively, p=0.007). There was a non-significant trend towards increased liner wear rates in group A compared to group B (0.031 ± 0.07 mm/yr vs 0.022 ± 0.05 mm/yr respectively, p=0.128). All three groups were statistically comparable preoperatively and at ten years follow-up when measuring normalised Western Ontario and McMaster Universities Osteoarthritis Index(p=0.410), short-form-36 (p = 0.465 mental, p = 0.713 physical), and pain scale scores (p=0.451). The use of UHMWPE was associated with progressively increased annual liner wear rates after THA. At ten years follow-up, this translated to UHMWPE leading to an increased incidence of osteolysis and aseptic loosening requiring revision THA, compared with XLPE. Femoral heads composed of OxZr were associated with a non-significant trend towards reduced wear rates compared to CoCr, but this did not translate to any differences in osteolysis, functional outcomes, or revision surgery between the two treatments groups

This study reports the ten-year outcomes of a three-arm, multicentre randomised controlled trial comparing Cobalt-Chrome (CoCr) and Oxidised Zirconium (OxZr) femoral heads with ultra-high molecular weight polyethylene (UHMWPE) versus highly cross-linked polyethylene (XLPE) liners in total hip arthroplasty (THA). Patients undergoing THA from four institutions were prospectively randomised into three groups. Group A received a CoCr femoral head and XLPE liner; Group B received an OxZr femoral head and XLPE liner; and Group C received an OxZr femoral head and UHMWPE liner. The outcomes of 262 study patients were analysed at ten years follow-up. At ten years, increased linear wear rates were recorded in group C compared to group A (0.133 ± 0.21 mm/yr vs 0.031 ± 0.07 mm/yr respectively, p<0.001) and group B (0.133 ± 0.21 mm/yr vs 0.022 ± 0.05 mm/yr respectively, p<0.001). Patients in group C had increased risk of osteolysis and aseptic loosening requiring revision surgery compared with group A (7/133 vs 0/133 respectively, p=0.007) and group B (7/133 vs 0/135 respectively, p=0.007). There was a non- significant trend towards increased liner wear rates in group A compared to group B (0.031 ± 0.07 mm/yr vs 0.022 ± 0.05 mm/yr respectively, p=0.128). All three groups were statistically comparable preoperatively and at ten years follow-up from a clinical score perspective. The use of UHMWPE was associated with progressively increased annual liner wear rates. At ten years follow-up, this translated to an increased incidence of osteolysis and aseptic loosening requiring revision, compared with XLPE. Femoral heads composed of OxZr were associated with a non-significant trend towards reduced wear rates compared to CoCr, but this did not translate to any differences in osteolysis, functional outcomes, or revision surgery between the two treatments groups

Aims

To present a surgically relevant update of trunnionosis.