Background. Pseudotumours have been associated with metal-on-metal (MoM) hip replacements. We define it as a solid mass which may have cystic components that is neither neoplastic nor infectious in aetiology. The cause of a pseudotumour is not fully understood but could be due to excessive wear, metal hypersensitivity or due to an as-yet unknown cause. Aim. We present the retrieval analysis of early failure MoM hips revised for pain, loosening or a symptomatic mass. Tissues and implants were examined for the possible causes of failure and pseudotumour formation. Corrosion as a potential new cause for pseudotumour formation will be presented. Methods. A group of 16 MoM hip replacements were collected for retrieval analysis. Six of which had a pseudotumour. An Artificial Hip Profiler (Redlux Ltd) was used to measure wear. Edge loading was determined using the 3D wear data. Tissues were histologically evaluated using a 10-point ALVAL scoring system, which strongly suggests hypersensitivity (1). Cases were assigned to one of three categories: high wear (rates >5m/yr), hypersensitivity or corrosion. Results. Of the 6 pseudotumours, 3 had edge loading, 2 had high ALVAL scores and one had corrosion at the head taper junction. The high wear group, (3 cases) all demonstrated edge loading. Histology revealed more metal wear particles and macrophages, with a low ALVAL score in these cases. Two cases were found to have hypersensitivity with a high ALVAL score, more lymphocytes with less visible wear debris and macrophages. The wear rates were also lower, <4m/yr. One total hip replacement had corrosion at the junction between the head and adaptor taper for the stem. The bearings had low wear and the tissue had extensive necrosis as well as products of corrosion enclosed in fibrin (2). There was no suggestion of hypersensitivity (low ALVAL score). Conclusion. Pseudotumours can be caused by high wear, but if this is ruled out, a hypersensitivity or corrosion product reaction should be considered

INTRODUCTION. Ceramic-on-metal hip replacements (COM, where the head is a Biolox Delta ceramic and liner is Co Cr alloy), have demonstrated reduced wear under standard conditions in vitro compared to metal-on-metal (MOM) [1]. Early clinical results are also encouraging [2]. Recently concerns have been raised regarding the poor clinical performance of MOM hip resurfacings [3], particularly when cups are steeply inclined. Laboratory hip simulator testing has been used to replicate edge loading, also demonstrating elevated wear [4]. Therefore, a range of conditions to replicate sub-optimal use clinically to better predict in vivo performance should be used. The aim of this study was to compare the wear rates of MOM and COM under adverse edge loading conditions in an in vitro hip simulator test. METHODS. Ceramic-on-metal (n=3) and metal-on-metal (n=3) 36mm hip prostheses (supplied by DePuy International Ltd, UK) were tested in the Leeds Physiological Anatomical Hip Joint Simulator. Liners were mounted to provide a clinical angle of 45o, and stems positioned anatomically. A simplified gait cycle and microseparation was applied as previously described [5] for two million cycles in 25% new born calf serum. Gravimetric analysis was completed every million cycles and wear volumes calculated. RESULTS. The overall mean volumetric wear rate of COM bearings was 0.36 ± 0.55mm3 per million cycles, this was significantly less than the MOM bearing wear (1.32 ± 0.91mm3 per million cycles). For both COM and MOM bearings wear under these edge loading conditions was significantly greater if compared to previously reported wear under standard conditions [1]. DISCUSSION. The reduced wear of COM has been attributed to the differential hardness decreasing adhesive wear and reduced corrosive wear [6]. Wear under the harsh edge-loading conditions in this study is also reported to be significantly less in COM bearings compared to MOM. In MOM bearings in edge contact conditions, the wear zone becomes starved of lubrication, this elevates wear and increases damage at the edge of the cup. In COM bearings the harder head does not become damaged when there is lubricant starvation and hence wear does not accelerate in the same way. In conclusion, COM bearings show reduced wear compared to MOM bearings under standard and adverse conditions and there is some early evidence to support this finding clinically. ACKNOWLEDGEMENTS. Supported by DePuy International Ltd. SW is supported by a Royal Academy of Engineering/EPSRC (UK) fellowship

INTRODUCTION. Studies have suggested that there is a reduction in head-neck-ratio (HNR) associated with MoMHRA. A reduction in HNR at operation would decrease range of movement and increase impingement risk. Impingement could lead to 20 edge loading, increasing wear. Serum ion levels of Chromium (Cr) and Cobalt (Co) are surrogate markers of wear. Although acetabular component orientation has been shown to contribute to wear and PT development, the role of a decrease in HNR has only been highlighted in PT development. This study aimed to measure changes in HNR that occur at resurfacing and determine any gender- and component size-specific differences. In addition it aimed to determine whether changes in HNR could be associated with increased wear. METHODS. 84 patients (56M: 28F) with unilateral MoMHRA were included. The mean age at surgery was 57 years. The mean femoral component was 49mm. Components were considered small if <45mm, average if between 45–50mm and large if >50mm. Three designs were implanted; BHR, C+ and Recap. The average follow up was 4 years. All patients had Cr/Co levels measured at follow up. Patients were considered to have high ions if Cr and Co levels were 5.1ppb and 4.4ppb respectively. Pre-operative HNR (HNRpre) and the post-operative HNR (HNRpost) were made from the respective pelvic radiographs. Assuming a 2mm thick cartilage layer, the HNR based on the diameter of the articular cartilage pre-operatively (HNRart) was calculated. The immediate changes in HNR as a result of the operation were expressed relative to articular HNR pre-op:. HNRartpost=HNRpost–HNRart. RESULTS. The changes in HNR at operation were significantly negatively correlated with HNRpre, (p<0.001), (rho=−0.77). Females had greater ion levels (p=0.013) and smaller components (p<0.001). Females had bigger pre-operative HNRart and were downsized more (p<0.001). Similarly, patients with small components had higher ions (p=0.032). They had greater HNRart and were downsized more (p<0.001) Twelve patients comprised the high ion group. These patients had smaller components (p=0.004), greater HNRart and were down-sized significantly more at resurfacing (p<0.001). DISCUSSION. This study highlights HNR changes that occur in resurfaced hips. Females, patients with small components and patients in the high ion group had higher pre-operative HNR and were downsized more at operation. Femoral downsize, would probably increase impingement risk, lead to secondary edge loading and contribute to greater incidence of wear related problems