In biomaterial engineering the surface of an implant can influence cell differentiation, adhesion and affinity towards the implant. Increased bone marrow derived mesenchymal stromal cell (BMSC) differentiation towards bone forming osteoblasts, on contact with an implant, can improve osteointegration. The process of micropatterning has been shown to improve osteointegration in polymers, but there are few reports surrounding ceramics. The purpose of this study was to establish a co-culture of BMSCs with osteoclast progenitor cells and to observe the response to micropatterned zirconia toughened alumina (ZTA) ceramics with 30 µm diameter pits. The aim was to establish if the pits were specifically bioactive towards osteogenesis or were generally bioactive and would also stimulate osteoclastogenesis that could potentially lead to osteolysis. We demonstrate specific bioactivity of micropits towards osteogenesis with more nodule formation and less osteoclastogenesis. This may have a role when designing ceramic orthopaedic implants

Introduction. In knee arthroplasty a ceramic component has several advantages: first, there is no ion release implying a risk for potential allergies. Second, the hardness of the material leads to a scratch resistance which ultimately reduces PE wear over time. In the past, ceramic components in knee applications were limited in the variety of design possibilities due to necessary thickness of the component resulting from the associated fracture risk of ceramics. By the development of an alumina matrix composite material with increased mechanical properties it is possible to develop ceramic knee components which have nearly the same design as a metal component and use the same implantation technique as well as the same instruments. This offers the surgeon the opportunity to choose intraoperatively between metal or ceramic knee components. Extensive in-vitro testing shows that ceramic knee components achieve superior mechanical test results. The reliability of the components is proven by two different burst tests and a fatigue test for both a femoral and a tibial ceramic knee component. Material and method. The mechanical proof-test was developed by subsequent steps of numerical load/stress analysis and design of an adequate mechanical test equipment. The procedure was organized as follows:. Oncologic: Analysis of relevant maximum in-vivo loading conditions. Analysis of the “boundary conditions”. Finite Element analysis: Identifying regions of highest stress concentration. Design analysis and accommodation if necessary. Development of an adequate mechanical test equipment which produces stresses comparable to the in-vivo conditions. Performing mechanical tests with ceramic femoral components. Validation of the test concept: comparison of test results and stress analysis. Assign “safety margin”,. Establish “proof test”. Results. Two independent load scenarios have been determined for each type of components as being in-vivo relevant. Hence, the developed proof-test consists of two subsequent load tests, the so-called regular test and the tension test for the femoral components, and the upper side test and the lower side test for the tibial components. In the regular test, the mechanical strength of the polished outer condyles is tested using a force which is equivalent to an in-vivo loading of 16 times bodyweight. In the tension test, the interior sides of the condyles are stressed in the sagittal plane ensuring a mechanically reliable implantation. This test is performed with a force equivalent to 10 times bodyweight. Discussion. The procedure to determine the proof loads using the maximum in-vivo loads together with a safety factor ensures the mechanical safety of the ceramic knee component. Together with the well-known excellent wear and biological behaviour of ceramics, this application provides an alternative to common metallic knee components. Clinical observations in the framework of a multi-centre study in different European countries have been started and show very promising results

Aims

Musculoskeletal infection is a devastating complication in both trauma and elective orthopaedic surgeries that can result in significant morbidity. Aim of this study was to assess the effectiveness and complications of local antibiotic impregnated dissolvable synthetic calcium sulphate beads (Stimulan Rapid Cure) in the hands of different surgeons from multiple centres in surgically managed bone and joint infections.

INTRODUCTION. One of the recent advances in the hard-on-hard hip arthroplasty is the development of a new material of diffusion hardened oxidised zirconium (DHOxZr). The DHOxZr material consists of a ceramic layer on the top surface which is supported by a thick oxygen diffusion hardened (DH) zone underneath. With the desired properties of metal substrate, ceramic surface and a gradient structure of the oxygen diffusion zone, the DHOxZr-on-DHOxZr bearing combination is expected to produce low wear and minimal metal ions. This can possibly address the concerns associated with metal hypersensitivity associated with metal on metal bearings and fracture risk associated with ceramics. The aim of this study was to evaluate the wear of DHOxZr-on-DHOxZr as a possible hard on hard bearing combination in hips. METHODS. Three pairs of 50 mm DHOxZr prototype hip joint devices, each consisting of a DHOxZr modular head and a DHOxZr liner were wear tested in a ProSim hip joint simulator under standard testing conditions used by the Implant Development Centre (IDC), Smith & Nephew, Leamington Spa for 5 million cycles (Mc). The flexion/extension was 30° and 15°. The internal/external rotation was ± 10°. The force was Paul-type stance phase loading, with a maximum load of 3 kN and a standard ISO swing phase load of 0.3 kN. The test frequency was 1 Hz. Gravimetric analysis was carried out at 0, 0.5, 1, 2, 3, 4 & 5 million cycles. The lubricant was new born calf serum with 2 g/l sodium azide concentration diluted with de-ionised water to achieve average protein concentration of 20 g/l. Lubricant was changed every 0.25Mc during the first million cycles of the test and at every 0.33 Mc from 1 to 5Mc. RESULTS. A biphasic wear pattern was observed for the DHOxZr on DHOxZr devices during the test, with a running in phase from 0–1 Mc and a steady state phase from 1–5 Mc. At a confidence level of 95%, the mean wear rate was 0.21 ±0.06 mm3/Mc during the running-in stage, and the wear rate was reduced to 0.01 ±0.03 mm3/Mc during the steady state for the device tested. The wear volume loss of the DHOxZr on DHOxZr devices was significantly lower than that generated by CoCrMo metal on metal (MoM) devices (p < 0.05) under identical simulator test conditions

Due to increased life expectancy of human population, the amount of total knee replacements (TKR) is expected to increase. TKR reached a high grade of quality and safety, but most often it fail because of aseptic implant loosening caused by polyethylene (PE) wear debris. Wear is generated at the articulating surfaces, e.g. caused by three body particles, like bone fragments or bone cement particles. The aim of this experimental study was to compare the wear of tibial PE inserts combined with metallic and ceramic femoral components at three body wear situation induced by polymethylmethacrylate (PMMA) and zirconia (ZrO2) particles from the bone cement. Wear testing was performed for 5 Mio load cycles, using tibial standard PE inserts combined with the same CR femoral component, in two different materials, Cobalt Chromium (CoCrMo) and Biolox delta ® ceramic (Multigen Plus Knee System, Lima Corporate, Italy). A knee wear simulator, according to ISO 14243 (EndoLab GmbH, Rosenheim, Germany), was used to carry out the tests. The tests were performed in temperature-controlled test chambers at 37 °C, containing calf serum with a protein content of 30 g/l. Polymethylmethacrylate (PMMA) and zirconia (ZrO2) bone cement particles (Palacos R ®) were manufactured to a size of 30 μm. The three body particles were added at all stations onto the articulating surface of the tibial PE insert (7mg per condyle) at every 500,000 cycles. Wear was determined gravimetrically and the surfaces of tibial inserts were analysed by scanning electron microscope (SEM) after finishing the 5 million cycles. Furthermore, roughness of the PE insert surfaces and the articulating surfaces of the different femoral components were detected and the PE wear particles were analysed by SEM. The average gravimetrical wear rates of the tibial PE inserts in combination with CoCr and Biolox delta ® ceramic femoral components amounted to 6.4 ± 0.9 mg and 2.6 ± 0.4 mg per million cycles, respectively. Beside bone cement particles on the articulating surface of the PE inserts, polished surfaces and scratches were detected by SEM. In comparison to the untreated surfaces of the PE inserts at both material pairings the surface roughness at the articulating areas showed deep scratches and polished regions. Analyses of the metallic femoral components showed scratches at the articulating surfaces, none on ceramics. The present study pointed out the effect of femoral component material in an abrasive three body wear situation on the wear properties of TKR. The wear simulator tests showed that wear of PE inserts under three body wear conditions, in combination with ceramic femoral components, was significantly lower than with metallic femoral components. With regard to anti-allergic properties, ceramic femoral components are promising products for TKR

Aims

To clarify the effectiveness of the induced membrane technique (IMT) using beta-tricalcium phosphate (β-TCP) for reconstruction of segmental bone defects by evaluating clinical and radiological outcomes, and the effect of defect size and operated site on surgical outcomes.