Aims. The aim of this study was to conduct the largest low contact stress (LCS) retrieval study to elucidate the failure mechanisms of the Porocoat and Duofix femoral component. The latter design was voluntarily recalled by the manufacturer. Materials and Methods. Uncemented LCS explants were divided into three groups: Duofix, Porocoat, and mixed. Demographics, polyethylene wear, tissue ingrowth, and metallurgical analyses were performed. Results. In 104 implants, a decrease in the odds of loosening and an increase in metallosis and tissue staining in the Duofix group relative to Porocoat group was detected (p = 0.028). There was an increased presence of embedded metallic debris in the Duofix group (p < 0.001). Decreased tissue ingrowth was associated with the Duofix surface (p < 0.001). The attached beads had reduced microhardness, indicative of adverse thermal processing, which resulted in bead shedding, particulate debris, and metallosis. Conclusion. Hydroxyapatite coating of the LCS femoral component produced unexpected results and led to its recall. The root cause was likely a combination of retained alumina grit and a reduction in bead microhardness (mechanical strength) resulting in increased particle debris, metallosis, and early revision. The Duofix LCS femoral component was not equivalent to the Porocoat version despite its approval through the Food and Drug Administration (FDA) 510(k) equivalance approval process. Regulation of the introduction of modified existing devices needs to be improved and the Duofix LCS should have been considered to be a new device for which equivalence had not been demonstrated at the point of introduction. Cite this article: Bone Joint J 2019;101-B:1248–1255

Aims

The Exeter V40 cemented femoral stem was first introduced in 2000. The largest single-centre analysis of this implant to date was published in 2018 by Westerman et al. Excellent results were reported at a minimum of ten years for the first 540 cases performed at the designer centre in the Exeter NHS Trust, with stem survivorship of 96.8%. The aim of this current study is to report long-term outcomes and survivorship for the Exeter V40 stem in a non-designer centre.

Objectives

Wear debris released from bearing surfaces has been shown to provoke negative immune responses in the recipient. Excessive wear has been linked to early failure of prostheses. Analysis using coordinate measuring machines (CMMs) can provide estimates of total volumetric material loss of explanted prostheses and can help to understand device failure. The accuracy of volumetric testing has been debated, with some investigators stating that only protocols involving hundreds of thousands of measurement points are sufficient. We looked to examine this assumption and to apply the findings to the clinical arena.