Background. Pseudotumours have been associated with metal-on-metal (MoM) hip replacements. We define it as a solid mass which may have cystic components that is neither neoplastic nor infectious in aetiology. The cause of a pseudotumour is not fully understood but could be due to excessive wear, metal hypersensitivity or due to an as-yet unknown cause. Aim. We present the retrieval analysis of early failure MoM hips revised for pain, loosening or a symptomatic mass. Tissues and implants were examined for the possible causes of failure and pseudotumour formation. Corrosion as a potential new cause for pseudotumour formation will be presented. Methods. A group of 16 MoM hip replacements were collected for retrieval analysis. Six of which had a pseudotumour. An Artificial Hip Profiler (Redlux Ltd) was used to measure wear. Edge loading was determined using the 3D wear data. Tissues were histologically evaluated using a 10-point ALVAL scoring system, which strongly suggests hypersensitivity (1). Cases were assigned to one of three categories: high wear (rates >5m/yr), hypersensitivity or corrosion. Results. Of the 6 pseudotumours, 3 had edge loading, 2 had high ALVAL scores and one had corrosion at the head taper junction. The high wear group, (3 cases) all demonstrated edge loading. Histology revealed more metal wear particles and macrophages, with a low ALVAL score in these cases. Two cases were found to have hypersensitivity with a high ALVAL score, more lymphocytes with less visible wear debris and macrophages. The wear rates were also lower, <4m/yr. One total hip replacement had corrosion at the junction between the head and adaptor taper for the stem. The bearings had low wear and the tissue had extensive necrosis as well as products of corrosion enclosed in fibrin (2). There was no suggestion of hypersensitivity (low ALVAL score). Conclusion. Pseudotumours can be caused by high wear, but if this is ruled out, a hypersensitivity or corrosion product reaction should be considered

Hip resurfacing arthroplasty is an established and effective intervention for osteoarthritis of the hip in the young active patient, relying on the principle of femoral bone-stock preservation. A recognised mode of failure is neck thinning leading to radiological evidence of neck collapse and clinical failure. We report on a series of these slow-neck-failure patients and highlight the increased incidence of this phenomenon in post-menopausal female patients. This is a single operator, single implant series; 172 cases were identified from databases at our institution. 76 were female, mean (SD) age 52 (7) years. 96 were male, mean (SD) age 51(12) years. 15 (8.7%) patients required revision. 12 (80%) were female, 9 (75%) of these were due to slow neck failure. In the men one patient developed ALVAL requiring removal of his bilateral hip resurfacings, the other failure mode was early femoral neck failure. Mean time to failure was 6 months in men and 37 months in women. This difference in failure rates is also seen in the NJR figures. This review confirms the relatively high incidence of premature failure in post-menopausal females. NICE guidance in 2003, currently under review, stated that resurfacing is indicated in male patients up to 65 and female patients up to 60. As a result of this study we are currently advising post-menopausal patients that this risk of early failure may make total hip replacement a preferable option to resurfacing arthroplasty

Early failure of metal-on-metal (MoM) total hip replacements (THR) is now well established. We review 93 consecutive patients with CPT¯ stems MoM THR. Our series demonstrates a new mechanism of failure, which may be implant combination specific. Between January 2005 and June 2009, 93 consecutive MoM total hip replacements were preformed using CPT stems by 3 surgeons at our unit. 73 CPT¯ stems, Metasul¯ Large Diameter Heads (LDH) with Durom¯ acetabulae and 20 CPT¯ stems, Metasul¯ 28mm diameter heads in Allofit¯ shells (zimmer). Clinical outcomes were collected prospectively before surgery, at 3 months, 1 year, 2 years, 3 years, and at 5 years post surgery. Revision for any cause was taken as the primary endpoint and the roentgenograms and explanted prostheses were analyzed for failure patterns. In the LDH/Durom¯ group a total of 13 (18%) patients required revision (figs. 1) at a median of 35 months (range 6-44). 6 (8%) for periprosthetic fracture. All 6 periprostethic fractures were associated with minimal or no trauma and all had ALVAL identified histologically. To date there have been no failures in the CPT¯/28mm head Allofit¯ group. Several failures demonstrated bone loss in Gruen zones 8 ± 9 ± 10 (fig. 2). We demonstrate an unacceptably high rate of failure in CPT¯ MoM LDH hip replacements, with a high failure secondary to periprosthetic fracture and postulate a mechanism associated with local toxicity to metal ions. We strongly advise against this combination of prosthesis