The CoCrMo large bearings had shown a high failure rate, because of metal ion and particle release. Alumina matrix composite (AMC) ball heads have shown to mitigate such phenomena. The aim of this study was to investigate the leaching properties of AMC clinically as well as experimentally. Two patient groups were compared: a control group (n=15) without any implant (Controls) and 15 Patients with unilateral treatment with Biolox delta ceramic-on-ceramic (CoC). Whole-blood samples of Controls and Patients (after 3 and 12 months from treatment with CoC) were measured by means of trace element analysis using a HR-ICPMS. The leaching behaviour of BIOLOX delta was also analysed in-vitro: five Biolox delta heads and five CoCrMo heads were immersed in serum for seven days at 37°C. Aluminium, cobalt, chromium and strontium were detected based on HR-ICPMS.Background
Methods
Ceramics are excellently suited for applications in arthroplasty, mainly total hip, knee and shoulder replacement. As the most prominent representative of this demanding type of material, BIOLOX® To assess the influence of INTRODUCTION
OBJECTIVES
The role and importance of fretting and corrosion in modular hip endoprostheses has become of more and more interest within the last years. Especially bearing couples with large diameters may experience high friction moments leading to an increase of relative micro movements between the surfaces of the taper connections. Recently published studies show that the risk of fretting and corrosion is significantly reduced by using ceramic ball heads compared to metal ball heads. Goal of this study was to investigate the risk of fretting and corrosion as well as possible loosening of large ceramic ball heads with metal sleeves.INTRODUCTION
OBJECTIVES
The reported revision rate for THA is below 10% at 10 years. Major factors for revision are aseptic loosening or dislocation of the articulating components. CoC bearings in total hip arthroplasty (THA) have demonstrated very low wear rates. Due to producing the least number of wear particles of any articular bearing used for THA, osteolysis is very rarely observed. Zirconia-platelet toughened alumina (ZPTA) has improved toughness and bending strength while maintaining all other advantageous properties of alumina. Consequently, its clinical fracture rate is minimal and wear resistance is superior to alumina. Since a trend exists towards the usage of larger bearings the aim of this study was to compare the tribological behavior of different ZPTA/ZPTA THAs with respect to their ball head diameter.INTRODUCTION
OBJECTIVES