Wear-related osteolysis continues to be a concern in the long-term outcome and survivorship of total hip arthroplasty (THA) and there continues to be an emphasis on bearing materials that exhibit improved wear profiles. Oxidized zirconium metal (Oxinium®, Smith & Nephew) was developed to reduce the amount of polyethylene wear as compared to cobalt chromium femoral heads, without the risk of brittle fracture seen with older generation ceramics. There are a limited number of retrieval studies evaluating the performance of Oxinium in THA. The aims of this study were 1) to visually assess damage on the surface of a large number of retrieved Oxinium femoral heads, 2) to measure surface roughness of scratches on the surfaces of Oxinium femoral heads, and 3) to use scanning electron microscopy (SEM) to assess the integrity of the oxidized zirconium surface in damaged areas. BIOLOX From 2006 to 2013, 59 retrieved Oxinium femoral heads in THAs were collected after an average time to revision surgery of 1.64 years. The mean patient age was 61.9 years, with 32 males and 27 females. Reasons for revision surgery were recurrent dislocation (24), femoral component loosening or subsidence (13), infection (9), acetabular loosening (4), periprosthethic fracture (4), acetabular malposition (2), heterotopic ossification (2), and 1 case of leg length discrepancy. The diameters of the femoral heads were 28 mm (9), 32 mm (22), 36mm (26) and 40mm (2). Three observers visually graded surface damage on all femoral heads according to the following criteria: 1) no scratches, 2) minimal damage with one to two scratches, 3) significant damage with multiple scratches. We measured the surface roughness of retrieved Oxinium and BIOLOX Introduction
Methods