Achilles tendon mechanical properties depend on a complex hierarchical design, with collagen being the smallest load-bearing unit. At the nanoscale, collagen molecules are organized into fibrils, which at the microscale are assembled into fibers, followed by larger structures such as sub-tendons or fascicles. Degree of in vivo loading affects the collagen content, and organization and consequently the tissue's mechanical response. We aim to unravel how composition, structural organization, and mechanical response are affected by degree of in vivo loading at each length scale. The presentation will outline the results to date about to the use of high-resolution synchrotron-based tissue characterisation methods on several length scales in combination with in situ mechanical tests. We use a rat model, where the tendons are subjected to varying loading in vivo. To characterize the tissue microstructure, phase-contrast enhanced synchrotron micro-tomography is performed. The 3D fiber organization in fully loaded tendons is highly aligned, whereas the fibers in unloaded tendons are significantly more heterogeneously arranged and crimped. To characterize the collagen fibril response, Small Angle X-ray Scattering is performed. Two types of fibril organizations are found; a single population oriented towards the main load direction and two fibril subpopulations with clearly distinct orientations. Scattering during loading showed that the fibrils in unloaded tendons did not strain as much in fully loaded. In situ loading concurrently with high resolution synchrotron experiments show the complex tendon response to in situ load and its relation to in vivo loading and tendon hierarchical structure. Unloading seems to alter the organization of the fibrils and fibers, e.g. increased crimping and more pronounced sub-tendon twists.

Acknowledgements: Funding from Knut and Alice Wallenberg Foundation and European Research Council (101002516). Paul Scherrer Institut, Switzerland for beamtime at cSAXS and TOMCAT.

To characterize the microstructural organization of collagen fibers in human medial menisci and the response to mechanical loading in relation to age. We combine high resolution imaging with mechanical compression to visualize the altered response of the tissue at the microscale. Menisci distribute the load in the knee and are predominantly composed of water and specifically hierarchically arranged collagen fibers. Structural and compositional changes are known to occur in the meniscus during aging and development of osteoarthritis. However, how microstructural changes due to degeneration affect mechanical performance is still largely unknown [1].

Fresh frozen 4 mm Ø plugs of human medial menisci (n=15, men, 20-85 years) with no macroscopic damage nor known diseases from the MENIX biobank at Skåne University Hospital were imaged by phase contrast synchrotron tomography at the TOMCAT beamline (Paul Scherrer Institute, CH). A rheometer was implemented into the beamline to perform in-situ stress relaxation (2 steps 15% and 30% strain) during imaging (21 keV, 2.75μm pixel size). 40s scans were acquired before and after loading, while 14 fast tomographs (5s acquisitions) were taken during relaxation. The fiber 3D orientations and structural changes during loading were determined using a structure tensor approach (adapting a script from [1]). The 3D collagen fiber orientation in menisci revealed alternating layers of fibers. Two main areas are shown: surfaces and bulk. The surface layers are a mesh of randomly oriented fibers. Within the bulk 2-3 layers of fibers are visible that alternate about 30° to each other. Structural degeneration with age is visible and is currently being quantified. During stress-relaxation all menisci show a similar behavior, with samples from older donors being characterized by larger standard deviation Furthermore, the behavior of the different layers of fibers is tracked during relaxation showing how fibers with different orientation respond to the applied loading.

Acknowledgments: We thank PSI for the beamtime at the TOMCAT beamline X02DA, and funding from Swedish Research Council (2019-00953), under the frame of ERA PerMed, and the Novo Nordisk Foundation through MathKOA (NNF21OC0065373).