We report the result of 49 revisions for aseptic cup loosening using freeze-dried allografts. We assessed the results according to the primary pathology, severity of bone loss, direction of socket migration before revision, method of bone grafting, socket position, graft incorporation and socket loosening. Patient’s mean age at revision was 56 years 8 months. At a mean follow up of 7 years and 5 months four cups have been revised for aseptic loosening. Five sockets have migrated but remained stable while six showed full demarcation but have not migrated. The other 34 remained stable and show radiographic evidence of graft incorporation.
We have prospectively studied the wear of enhanced ultra-high molecular-weight polyethylene (Hylamer) in combination with a zirconia femoral head of 22.225 mm diameter on a cemented, triple-tapered, collarless, polished stem, the C Stem. The 71 patients who underwent total hip arthroplasty had a mean follow-up of six years (3 to 8). No patient died or was lost to follow-up. The clinical results were excellent with 96% of patients satisfied. There were no revisions. Two cups were considered to be loose radiologically. One was avulsed from the cement in a skiing accident, with a periprosthetic fracture of the femur, but has remained stable for more than seven years. One femur shows radiological appearances which are compatible with a healing infection. One femoral component is at risk of loosening. The mean rate of penetration of the cup was 0.22 mm/year (0.06 to 0.55). Our results appear to be within the guidelines set by the National Institute of Clinical Excellence. We have discontinued the use of Hylamer despite excellent clinical results and no revisions to date because the high initial rates of penetration did not settle to the expected low levels within the anticipated time.
Pyrexia in the post-operative setting has often been associated with a possible systemic or wound infection. We assessed whether there is any justification for our concern regarding post-operative pyrexia following hip arthroplasty and subsequent deep prosthetic infection.
An assessment of the clinical outcome of 97 sequential patients who underwent 103 primary hip arthroplasty for primary osteoarthritis replacements. Daily temperature and systemic complications in the post-operative period were recorded. Clinical outcome was measured using an Oxford hip questionnaire. Patients had a mean follow-up of 5.2 years (range 3.5–7.2years).
A review of postoperative temperature records of 80 patients who had undergone primary total hip replacement. Thirty-one patients had required revision surgery at a mean time interval of 37.2 months (range 5–74 months) for confirmed deep prosthetic infection. The remaining Forty-nine patients were asymptomatic at a mean follow-up of 31.5 months.
Post-operative pyrexia of 38 degrees Celsius was present in 51% of patient’s undergoing primary hip replacement in the first post-operative week but in 21.1% no etiological cause could be identified. Clinical outcome measured by an oxford hip questionnaire was not influenced by the post-operative temperature pattern.
The mean peak temperature on the first post-operative day was significantly lower in patients with deep prosthetic infection then patients with a clinically normal outcome (p=0.01).
Between November 1962 and December1990 a group of 1092 patients, 668 women and 424 men, under the age of 51 years at the time of surgery, underwent 1434 primary Charnley low-frictional torque arthroplasties and are being followed up indefinitely. Their mean age at operation was 41 years (12 to 51). At the latest review in June 2001 the mean follow-up had been for 15 years 1 month. Of the 1092 patients 54 (66 hips) could not be traced, 124 (169 hips) were known to have died and 220 (248 hips) had had a revision procedure. At a mean follow-up of 17 years and 5 months, 759 patients (951 hips) are still attending. In this group satisfaction with the outcome is 96.2%. The incidence of deep infection for the whole group was 1.67%. It was more common in patients who had had previous surgery (hemi- and total hip arthroplasties excluded), 2.2% compared with 1.5% in those who had not had previous surgery, but this difference was not statistically significant (p = 0.4). There were fewer cases of deep infection if gentamicin-containing cement was used, 0.9% compared with 1.9% in those with plain acrylic cement, but this was not also statistically significant (p = 0.4). There was a significantly higher rate of revision in patients who had had previous hip surgery, 24.8% compared with 14.1% in those who had not had previous surgery (p <
0.001). At the latest review, 1.95% are known to have had at least one dislocation and 0.4% have had a revision for dislocation. The indication for revision was aseptic loosening of the cup (11.7%), aseptic loosening of the stem (4.9%), a fractured stem (1.7%), deep infection (1.5%) and dislocation (0.4%). With revision for any indication as the endpoint the survivorship was 93.7% (92.3 to 95.0) at ten years, 84.7% (82.4 to 87.1) at 15 years, 74.3% (70.5 to 78.0) at 20 years and 55.3% (45.5 to 65.0) at 27 years, when 55 hips remained ‘at risk’.
The calcar femorale is a vertical plate of bone lying deep to the lesser trochanter and is formed as a result of traction of the iliopsoas which separates the femoral cortex into two distinct layers, the calcar femorale and the medial femoral cortex. They fuse together proximally to form the medial femoral neck. A stem placed centrally will abut against the calcar femorale with little or no space for cement. Clearing of the calcar will offer space for a cement layer, which will support the stem proximally on the posterior aspect. We compared two consecutive groups of Charnley low-friction arthroplasties, with and without clearing of the calcar. In 330 patients who had an arthroplasty without clearing the calcar, there were ten revisions for aseptic loosening of the stem and six other stems were considered ‘definitely loose’, giving a rate of failure of 4.8%. In 111 patients in whom the calcar was cleared there was only one revision for aseptic loosening and no stems were classed as ‘definitely loose’, giving a rate of failure of 0.9%. Survivorship analysis has again shown the need for long-term follow-up; the differences became clear after ten years but because of the relatively small numbers, statistical analysis is not yet applicable. We now clear the calcar femorale routinely and advocate optimal access to the medullary canal and insertion of the stem in the area of the piriform fossa.
We have designed a modular cemented femoral component for revision of failed total hip arthroplasty in which deficiency of the proximal femur is such as to require a variable extrafemoral portion of the stem. We present the results of the first 74 operations in 72 patients; 56 of the patients had grade-3 or grade-4 femoral deficiency as defined by Gustilo and Pasternak and 24 had fractures of the proximal femur, of which 22 were periprosthetic. There was or had been infection in 19 hips. At a mean follow-up of 5 years 9 months (1 to 12 years) nine stems were radiologically loose of which three had been revised. There were no failures in 45 cases in which there was fixation of the distal stem of 10 cm or more. Dislocation occurred in nine patients and there were four cases of infection in the 19 which were, or had been, infected previously. There were no neurovascular complications and no intraoperative femoral fractures. The femoral bone stock improved radiologically in 45 hips of which 29 showed considerable reformation of the proximal femur; 27 remained unchanged and two showed increasing osteoporosis.
Between 1983 and 1988 we carried out 45 Charnley low-friction arthroplasties with autografts from the femoral head in 41 patients for developmental dysplasia of the hip. The preoperative radiographs were assessed for the severity of DDH according to the classifications of Crowe et al, Hartofilakidis et al and Sharp. The postoperative and follow-up radiographs were analysed for coverage of the socket by the graft, for loosening and for the outcome of the fixation of the bone graft. Two patients died (two hips) at four and seven years after THR from causes unrelated to the surgery and were excluded from the final radiological analysis. The mean age of the patients at the time of operation was 46 years 3 months. The autograft of the femoral head covered a mean 26% (16 to 35) of the acetabular component. All the grafts united. Some degree of resorption of the bone graft occurred in 27 patients, and always involved the lateral part of the graft, which was beyond the margin of the socket. After a mean follow-up of 11 years there had been no revisions and 38 patients had no pain or only slight discomfort. One socket migrated and four others were fully demarcated. Our findings indicate that the Charnley LFA with an autograft of the femoral head for DDH remains successful at a follow-up of 15 years.
We reviewed 261 patients with 320 Charnley low-friction arthroplasties who had a mean follow-up of 22 years 10 months (20 to 30). Of these, 93.9% considered the operation to be a success; 82.3% were free from pain and 11.6% had occasional discomfort. Satisfactory function was achieved in 59.6% and 62% had an excellent range of movement. The clinical results did not correlate well with the radiological appearance; radiologically loose components did not affect the clinical outcome. The main long-term problem was wear and loosening of the UHMWPE cup. Our findings suggest that the radiological appearance of the arthroplasty is a more reliable indication of the state of the arthroplasty than the clinical results.
We report the results of our continued review of 14 hip arthroplasties using alumina ceramic femoral heads with cross-linked polyethylene cups. There have been no complications and a very low rate of penetration. This was 0.02 mm per year after an initial ‘bedding-in’ period of two years. There has been no change in the mean rate between our earlier study at six years and the current results at 10 to 11 years. The use of these bearing surfaces appears to reduce the potential amount of polyethylene debris and may provide the next logical stage in the development of the Charnley low-friction arthroplasty.
The direction of wear in the acetabular socket has implications for the amount of debris that is generated during movement, for the magnitude of eccentric loading and for the incidence of impingement of the neck. We observed the direction of penetration with respect to a global co-ordinate system in 84 acetabular components retrieved at reoperation. The mean direction of wear relative to the open face of the sockets was found to be 37° with a range from 0° to 87°. For those values determined using the inclination of the socket on the prerevision radiograph, the mean direction of penetration in the coronal plane had a lateral, rather than a medial, component. The mean angle was 84° (SD 17°) with respect to the horizontal. The angle of penetration was found to correlate significantly with the depth, in that the lateral component became larger as the wear progressed. There was also a significant correlation between the rate of penetration and the direction of wear. Despite the theoretical advantage of penetration in the superolateral direction, i.e., along the margin of the socket, in reducing the probability of impingement of the neck, no significant correlation was seen between the angle of penetration and the period of use in vivo. This may suggest that impingement of the femoral neck on the rim of the socket may not be the dominant factor in loosening of the socket but can still be important in a few cases.
We examined stainless-steel, cobalt-chrome, titanium and alumina and zirconia ceramic femoral heads retrieved at revision surgery. All the heads had articulated against ultra-high-molecular-weight-polyethylene (UHMWPE) acetabular cups. We studied the simulation of third-body damage and the wear of UHMWPE against the various materials used for the heads. The surfaces of the retrieved heads were analysed using a two-dimensional contacting profilometer. Third-body damage was characterised by the mean height of the scratches above the mean line (Rpm). The alumina ceramic and zirconia ceramic retrieved heads were found to have significantly less damage. In laboratory studies the ceramics were also more resistant to simulated third-body damage than the metal alloys. We studied the wear of UHMWPE against the damaged counterfaces in simple configuration tests. The damaged ceramics produced less polyethylene wear than the damaged metal counterfaces. The wear factor of UHMWPE against the damaged materials was dependent on the amount of damage to the counterface (Rp). Our study has shown the benefit of using the harder and more damage-resistant ceramic materials for femoral heads.
Ultra-high-molecular-weight polyethylene (UHMWPE) components for total joint replacement generate wear particles which cause adverse biological tissue reactions leading to osteolysis and loosening. Sterilisation of UHMWPE components by gamma irradiation in air causes chain scissions which initiate a long-term oxidative process that degrades the chemical and mechanical properties of the polyethylene. Using a tri-pin-on-disc tribometer we studied the effect of ageing for ten years after gamma irradiation in air on the volumetric wear, particle size distribution and the number of particles produced by UHMWPE when sliding against a stainless-steel counterface. The aged and irradiated material produced six times more volumetric wear and 34 times more wear particles per unit load per unit sliding distance than non-sterilised UHMWPE. Our findings indicate that oxidative degradation of polyethylene after gamma irradiation in air with ageing produces more wear.
We report a prospective study of the use of intramedullary bone blocks to improve the fixation of a matt-finish femoral stem in Charnley low-friction arthroplasties. There were 379 patients (441 hips), but at a minimum follow-up of ten years there were 258 arthroplasties in 221 patients including some which had been revised. The mean age at surgery was 41 years (17 to 51) and the mean follow-up was 13.4 years (1 to 20 including the early revisions). Nine stems (3.5%) had been revised for aseptic loosening, but there were no stem fractures. Survivorship of stems was 99.2% at ten years and 94.35% at 15 and 20 years. We found that the patient’s gender, the position of the stem and the experience of the surgeon all influenced the outcome. Our findings suggest that using our method of stem fixation, follow-up of over 11 years was needed to reveal the effects of endosteal cavitation of the femur, and of over 13 years to assess any divergence between the clinical and the radiological outcomes of stem fixation.
We report the findings from independent prospective clinical and laboratory-based joint-simulator studies of the performance of ceramic femoral heads of 22.225 mm diameter in cross-linked polyethylene (XLP) acetabular cups. We found remarkable qualitative and quantitative agreement between the clinical and simulator results for the wear characteristics with time, and confirmed that ceramic femoral heads penetrate the XLP cups at only about half the rate of otherwise comparable metal heads. In the clinical study, 19 hips in 17 patients were followed for an average of 77 months. In the hip-joint simulator a similar prosthesis was tested for 7.3 million cycles. Both clinical and simulator results showed relatively high rates of penetration over the first 18 months or 1.5 million cycles, followed by a very much lower wear thereafter. Once an initial bedding-in of 0.2 mm to 0.4 mm had taken place the subsequent rates of penetration were very small. The initial clinical wear during bedding-in averaged 0.29 mm/year; subsequent progression was an order of magnitude lower at about 0.022 mm/year, lower than the 0.07 mm/year in metal-to-UHMWP Charnley LFAs. Our results show the excellent tribological features of alumina-ceramic-to-XLP implants, and also confirm the value of well-designed joint simulators for the evaluation of total joint replacements.
We studied wear in the ultra-high-molecular-weight polyethylene offset bore socket in 54 hips which had had Charnley low-friction arthroplasty. At an average follow-up of 8.1 years, the mean penetration rate was 0.04 mm per year. Correlation between the depth of socket penetration and the incidence of socket migration was confirmed, but socket migration occurred with lower penetration than had been previously reported.