We report a prospective study of the use of intramedullary bone blocks to improve the fixation of a matt-finish femoral stem in Charnley low-friction arthroplasties. There were 379 patients (441 hips), but at a minimum follow-up of ten years there were 258 arthroplasties in 221 patients including some which had been revised. The mean age at surgery was 41 years (17 to 51) and the mean follow-up was 13.4 years (1 to 20 including the early revisions). Nine stems (3.5%) had been revised for aseptic loosening, but there were no stem fractures. Survivorship of stems was 99.2% at ten years and 94.35% at 15 and 20 years. We found that the patient’s gender, the position of the stem and the experience of the surgeon all influenced the outcome. Our findings suggest that using our method of stem fixation, follow-up of over 11 years was needed to reveal the effects of endosteal cavitation of the femur, and of over 13 years to assess any divergence between the clinical and the radiological outcomes of stem fixation.
We report the findings from independent prospective clinical and laboratory-based joint-simulator studies of the performance of ceramic femoral heads of 22.225 mm diameter in cross-linked polyethylene (XLP) acetabular cups. We found remarkable qualitative and quantitative agreement between the clinical and simulator results for the wear characteristics with time, and confirmed that ceramic femoral heads penetrate the XLP cups at only about half the rate of otherwise comparable metal heads. In the clinical study, 19 hips in 17 patients were followed for an average of 77 months. In the hip-joint simulator a similar prosthesis was tested for 7.3 million cycles. Both clinical and simulator results showed relatively high rates of penetration over the first 18 months or 1.5 million cycles, followed by a very much lower wear thereafter. Once an initial bedding-in of 0.2 mm to 0.4 mm had taken place the subsequent rates of penetration were very small. The initial clinical wear during bedding-in averaged 0.29 mm/year; subsequent progression was an order of magnitude lower at about 0.022 mm/year, lower than the 0.07 mm/year in metal-to-UHMWP Charnley LFAs. Our results show the excellent tribological features of alumina-ceramic-to-XLP implants, and also confirm the value of well-designed joint simulators for the evaluation of total joint replacements.
We studied wear in the ultra-high-molecular-weight polyethylene offset bore socket in 54 hips which had had Charnley low-friction arthroplasty. At an average follow-up of 8.1 years, the mean penetration rate was 0.04 mm per year. Correlation between the depth of socket penetration and the incidence of socket migration was confirmed, but socket migration occurred with lower penetration than had been previously reported.