Two Durasul highly crosslinked polyethylene liners were exchanged during revision surgery four and five years after implantation, respectively. The retrieved liners were evaluated macroscopically and surface analysis was performed using optical and electron microscopy. A sample of each liner was used to determine the oxidation of the material by Fourier transform infrared spectroscopy. Samples of the capsule were examined histologically.

The annual wear rate was found to be 0.010 and 0.015 mm/year, respectively. Surface analysis showed very little loss of material caused by wear. Histological evaluation revealed a continuous neosynovial lining with single multinucleated foreign-body giant cells. Our findings showed no unexpected patterns of wear on the articulating surfaces up to five years after implantation and no obvious failure of material.

We revised seven alumina-blasted cementless hip prostheses (Ti-alloy stems, cp Ti threaded sockets) with low- or high-carbon Co-alloy bearings at a mean of 20.1 months after implantation because of pain and loosening. Histological examination of the retrieved periprosthetic tissues from two cases in which the implant was stable and three in which the socket was loose showed macrophages with basophilic granules containing metal and alumina wear particles and lymph-cell infiltrates. In one of the two cases of stem loosening the thickened neocapsule also contained definite lymphatic follicles and gross lymphocyte/plasma-cell infiltrates. Spectrometric determination of the concentration of elements in periprosthetic tissues from six cases was compared with that of joint capsules from five control patients undergoing primary hip surgery. In the revisions the mean concentration of implant-relevant elements was 693.85 μg/g dry tissue. In addition to Cr (15.2%), Co (4.3%), and Ti (10.3%), Al was predominant (68.1%) and all concentrations were significantly higher (p < 0.001) than those in the control tissues. The annual rates of linear wear were calculated for six implants. The mean value was 11.1 μm (heads 6.25 μm, inserts 4.82 μm). SEM/EDXA showed numerous fine scratches and deep furrows containing alumina particles in loosened sockets, and stems showed contamination with adhering or impacted alumina particles of between 2 and 50 μm in size.

We compared wear particles from two different designs of total hip arthroplasty with polycrystalline alumina-ceramic bearings of different production periods (group 1, before ISO 6474: group 2, according to ISO 6474). The neocapsules and interfacial connective tissue membranes were retrieved after mean implantation times of 131 months and 38 months, respectively. Specimen blocks were freed from embedding media, either methylmethacrylate or paraffin and digested in concentrated nitric acid. Particles were then counted and their sizes and composition determined by SEM and energy-dispersive x-ray analysis (EDXA).

The mean numbers and sizes of most alumina wear particles did not differ for both production periods, but the larger sizes of particle in group 1 point to more severe surface destruction. The increased metal wear in group 2 was apparently due to alumina-induced abrasion of the stems. In this study the concentrations of particles in the periprosthetic tissues were 2 to 22 times lower than those observed previously with polyethylene and alumina/polyethylene wear couples.

We report the clinical and tribological performance of 67 ceramic acetabular prostheses implanted between 1976 and 1979 without bone cement. They articulated with ceramic femoral heads mounted on mental femoral stems. After a mean elapsed period of 144 months, 59 sockets were radiographically stable but two showed early signs and six showed late signs of loosening. Four of the loose sockets have been revised. Histological analysis of the retrieved tissue showed a fibrous membrane around all the implants, with fibrocartilage in some. There was no bone ingrowth, and the fibrous membrane was up to 6 mm thick and infiltrated with lymphocytes, plasma cells, and macrophages. Intra- and extracellular birefringent wear particles were seen. Tribological analysis showed total wear rates in two retrieved alumina-on-alumina joints of 2.6 microns per year in a stable implant and 68 microns in a loose implant. Survival analysis showed a revision rate of 12.4% at 136 months.

Bone-marrow oedema syndrome (BMOS) of the hip gives a characteristic MRI pattern, in association with severe pain, non-specific focal loss of radiological density and a positive bone scan. In our MRI-controlled study, nine patients with non-traumatic BMOS in ten hips all had core decompression. Bone-marrow pressure measurements and intraosseous venography in five cases showed pathological values. All patients had immediate relief of pain, with return of MRI signals to normal after three months. Regular review was continued for at least 24 months with serial clinical radiological and MRI assessment. At a mean follow-up of 33 months all patients remained free of pain with normal radiographs and MR scans. The histological evaluation of undecalcified sections obtained from eight core decompressions confirmed the presence of bone-marrow oedema, with necrotic and reparative processes involving bone and marrow similar to those of early avascular necrosis but with no evidence of 'osteoporosis'. These findings support the assumption that BMOS may be the initial phase of non-traumatic avascular necrosis. In most patients BMOS will have a self-limiting course, but the duration of symptoms may be reduced by core decompression treatment.

1. Into osseous defects cut in the pelvis of rats, Kiel bone grafts were implanted after impregnation with the animals' own fresh bone marrow, obtained by femoral puncture. Unimpregnated Kiel bone grafts and Kiel bone grafts impregnated with an antibiotic solution were implanted as controls.

2. Histological examination of the implant area showed that in the marrow-impregnated grafts new bone formation could be observed after twelve days, and that during an observation period of 135 days after implantation bone formation occurred in thirteen out of nineteen rats. In four of these cases a continuous bony bridge developed over the defect.

3. In the unimpregnated grafts no more than a small amount of new bone was seen in only one of seven rats. In the antibiotic-impregnated grafts no bone formation was found in six rats during the same period of observation.