We made a semiquantitative study of the comparative histology of pseudomembranes from 12 loose cemented ceramic-ceramic and 18 metal-polyethylene total hip replacements. We found no significant difference in cellular reaction between the two groups, but there was a major difference in the origin of the particulate debris. In the metal-polyethylene group, polyethylene of articular origin was predominant, while in the ceramic-ceramic group the cellular reaction appeared to be a response to zirconia ceramic particles used to opacify cement used for fixation.

Isolation and characterisation of the debris showed that the zirconia particles formed the greatest proportion (76%) in ceramic-ceramic hips, while alumina debris of articular origin formed only 12%.

Our study has indicated that aseptic loosening of ceramic cups is not due to a response to debris generated at the articular interface, but to mechanical factors which lead to fragmentation of the cement.

We report a prospective study of the liner-metal interfaces of modular uncemented acetabular components as sources of debris. We collected the pseudomembrane from the screw-cup junction and the empty screw holes of the metal backing of 19 acetabula after an average implantation of 22 months. Associated osteolytic lesions were separately collected in two cases. The back surfaces of the liners and the screws were examined for damage, and some liners were scanned by electron microscopy. The tissues were studied histologically and by atomic absorption spectrophotometry to measure titanium content. The pseudomembrane from the screw-cup junction contained polyethylene debris in seven specimens and metal debris in ten. The material from empty screw holes was necrotic tissue or dense fibroconnective tissue with a proliferative histiocytic infiltrate and foreign-body giant-cell reaction. It contained polyethylene debris in 14 cases and metal in five. The two acetabular osteolytic lesions also showed a foreign-body giant-cell reaction to particulate debris. The average titanium levels in pseudomembranes from the screw-cup junction and the empty screw holes were 959 micrograms/g (48 to 11,900) and 74 micrograms/g (0.72 to 331) respectively. The tissue from the two lytic lesions showed average titanium levels of 139 and 147 micrograms/g respectively. The back surfaces of the PE liners showed surface deformation, burnishing, and embedded metal debris. All 30 retrieved screws demonstrated fretting at the base of the head and on the proximal shaft. Non-articular modular junctions create new interfaces for the generation of particulate debris, which may cause granulomatous reaction.