We aimed to establish if radiological parameters, dual energy x-ray absorbtiometry (DEXA) and quantitative CT (qCT) could predict the risk of sustaining a femoral neck fracture following hip resurfacing.

Twenty-one unilateral fresh frozen femurs were used. Each femur had a plain AP radiograph, DEXA scan and quantitative CT scan. Femurs were then prepared for a Birmingham Hip Resurfacing femoral component with the stem shaft angle equal to the native neck shaft angle. The femoral component was then cemented onto the prepared femoral head. No notching of the femoral neck occurred in any specimens. A repeat radiograph was performed to confirm the stem shaft angle. The femurs were then potted in a position of single leg stance and tested in the axial direction to failure using an Instron mechanical tester. The load to failure was then analysed with the radiological, DEXA and qCT parameters using multiple regression.

The strongest correlation with the load to failure values was the total mineral content of the femoral neck at the head/neck junction using qCT r= 0.74 (p< 0.001). This improved to r=0.76 (p< 0.001) when neck width was included in the analysis. The total bone mineral density measurement from the DEXA scan showed a correlation with the load to failure of r=0.69 (p< 0.001). Radiological parameters only moderately correlated with the load to failure values; neck width (r=0.55), head diameter (r= 0.49) and femoral off-set (r=0.3).

This study suggests that a patient’s risk of femoral neck fracture following hip resurfacing is most strongly correlated with total mineral content at the head/neck junction and bone mineral density. This biomechanical data suggests that the risk of post-operative femoral neck fracture may be most accurately identified with a pre-operative quantitative CT scan through the head/neck junction combined with the femoral neck width.

We aimed to establish if radiological parameters, dual energy x-ray absorbtiometry (DEXA) and quantitative CT (qCT) could predict the risk of sustaining a femoral neck fracture following hip resurfacing. 21 unilateral fresh frozen femurs were used. Each femur had a plain AP radiograph, DEXA scan and quantitative CT scan. Femurs were then prepared for a Birmingham Hip Resurfacing femoral component with the stem shaft angle equal to the native neck shaft angle. The femoral component was then cemented onto the prepared femoral head. No notching of the femoral neck occurred in any specimens. A repeat radiograph was performed to confirm the stem shaft angle. The femurs were then potted in a position of single leg stance and tested in the axial direction to failure using an Instron mechanical tester. The load to failure was then analysed with the radiological, DEXA and qCT parameters using multiple regression. The strongest correlation with the load to failure values was the total mineral content of the femoral neck at the head/neck junction using qCT r= 0.74 (p< 0.001). This improved to r=0.76 (p< 0.001) when neck width was included in the analysis. The total bone mineral density measurement from the DEXA scan showed a correlation with the load to failure of r=0.69 (p< 0.001). Radiological parameters only moderately correlated with the load to failure values; neck width (r=0.55), head diameter (r= 0.49) and femoral off-set (r=0.3). This study suggests that a patient’s risk of femoral neck fracture following hip resurfacing is most strongly correlated with total mineral content at the head/neck junction and bone mineral density. This biomechanical data suggests that the risk of post-operative femoral neck fracture may be most accurately identified with a pre-operative quantitative CT scan through the head/neck junction combined with the femoral neck width.