Controversy exists with regard to the thickness of cement mantles that are necessary around the femoral components of cemented total hip arthroplasties. Conventional teaching, based on bench-top or computor models and theoretical analyses, as well as post-mortem & follow-up studies, suggests that the cement mantle should be complete and not less than 2–3mm in thickness. Mantles that are less than this are held to be at risk from mechanical failure in the long term; if they are incomplete, focal lysis may occur and progress to aseptic loosening.

However, long term experience with a number of French cemented femoral components suggests that these conventions may be erroneous. These French femoral components include the Charnley-Kerboull (stainless steel) and the Ceraver Osteal (Ti6Al4V) stems, in both of which the underlying design principle is that the stem should completely fill the femoral canal, the cement then being used purely to fill the gaps. Such a design philosophy implies that the cement mantles will be very thin, and since both of these stems are straight and the femoral medullary canal is not, the mantles may not only be thin, but also in places incomplete.

Conventional teaching would suggest that any stem utilising mantles of this type would fail from a combination of focal lysis and cement fracture. Yet the long term results of both of these stems have been outstandingly good, with extremely low levels of aseptic loosening and endosteal lysis, irrespective of the bearing combinations being used. Both these stems have a surface finish of Ra < 0.1 microns. A third French design, the Fare stem, manufactured from Ti6Al4V and based on the same principles, was associated with bad results when manufactured with a rough (> 1.5 microns) surface, and appreciably better results after the surface roughness was changed to < 0.1 microns.

These findings, that constitute the ‘French Paradox’, have profound implications for the mechanical behaviour of cement in the femur and for the mechanisms that underlie stem failure from loosening.