MATERIALS AND METHODS

The knee system used for testing consisted of cobalt chrome femoral components and tibial trays (Triathlon®, Stryker Orthopaedics, Mahwah, NJ). Modular tibial inserts were machined from GUR 1020 polyethylene that was irradiated to 30 kGy and annealed three times (Modular, n=5) (X3, Stryker Orthopaedics, Mahwah, NJ). Monoblock tibias were direct compression molded to a metal substrate and then irradiated to 30 kGy and annealed three times. For the purposes of this test, the polyethylene was removed from the monoblock component and machined into a standard tibial insert (Monoblock, n=5).

A 6-station knee simulator was utilized for testing (MTS, Eden Prairie, MN). All motion and loading was computer controlled and waveforms followed ISO 14243-3 [1]. Testing was conducted at a frequency of 1 Hz for 3 million cycles. The lubricant used was Alpha Calf Fraction serum (Hyclone Labs, Logan, UT) diluted to 50% with a pH-balanced 20-mMole solution of deionized water and EDTA [2]. The serum solution was replaced and inserts were weighed for gravimetric wear at least every 0.5 million cycles. Standard test protocols were used for cleaning, weighing and assessing the wear loss of the tibial inserts [3]. Soak control specimens were used to correct for fluid absorption with weight loss data converted to volumetric data (by material density). Statistical analysis was performed using the Student's t-test with significance determined at the 95% confidence level (p < 0.05).