Development of antibacterial surfaces or coatings to prevent bacterial adhesion and hence colonization of implants and biofilm formation is an attractive option, in order to reduce the tremendous impact of implant-related infections associated with modern surgery. To overcome the lack of Sterile sandblasted titanium discs of approximately 5cm2 surface area were used as substrates for bacterial adhesion. The gel was prepared as follows: syringes prefilled with 300 mg of DAC powder (Novagenit Srl) were reconstituted with 5 ml of sterile water to obtain a hydrogel with a DAC concentration of 6%. Two experiments were conducted. In the first, 200 mg of hydrogel were homogenously spread on the surface of titanium disc, with the spreading device provided by the manufacturer. Both coated and uncoated substrates (controls) were overlaid with a standardized inoculum (108 CFU/ml) of a wild methicillin-resistant The adhesion density of Our results shows that DAC, “Defensive Antibacterial Coating”, has anti-adhesive properties that allow to reduce bacterial adhesion on a sanded titanium surface by more than 80%, even in the presence of remarkably high bacterial loads (108 CFU/ml), of multi-resistant bacteria (MRSA) and even in the case of previous contamination. Providing anti-adhesive properties to a surface with a fast-resorbable coating may be a safe option to protect inorganic and organic surfaces and biomaterials. Those observation could be the pre-requisite for its
An Implant Disposable Antibacterial Coating (i-DAC®) is described, consisting of a fully resorbable, biocompatible hydrogel, able to release antibacterial and antibiofilm agents. Direct application of the hydrogel on implants prevented infection occurrence in an Biofilm-related infections are among the main reasons for failure of joint prosthesis with high associated social and economical costs. Bacterial adhesion and subsequent biofilm formation have been shown to develop early after biomaterials implant into the human body, when a “race to the surface” takes place between the host's cells and the colonizing bacteria eventually present at the surgical site. Providing an antibacterial/antibiofilm coating of the implant may then play a strategic role in preventing biofilm related infections. Here we report the results of a series of Summary Statement
Introduction