The current procedures being applied in the clinical setting to address osteoporosis-related delayed union and nonunion bone fractures have been found to present mostly suboptimal outcomes. As a result, bone tissue engineering (BTE) solutions involving the development of implantable biomimetic scaffolds to replace damaged bone and support its regeneration are gaining interest. The piezoelectric properties of the bone tissue, which stem primarily from the significant presence of piezoelectric type I collagen fibrils in the tissue's extracellular matrix (ECM), play a key role in preserving the bone's homeostasis and provide integral assistance to the regeneration process. However, despite their significant potential, these properties of bone tend to be overlooked in most BTE-related studies. In order to bridge this gap in the literature, novel hydroxyapatite (HAp)-filled osteoinductive and piezoelectric poly(vinylidene fluoride-co-tetrafluoroethylene) (PVDF-TrFE) electrospun nanofibers were developed to replicate the bone's fibrous ECM composition and electrical features. Different HAp nanoparticle concentrations (1–10%, wt%) were tested to assess their effect on the physicochemical and biological properties of the resulting fibers. The fabricated scaffolds displayed biomimetic collagen fibril-like diameters, while also presenting mechanical features akin to type I collagen. The increase in HAp presence was found to enhance both surface and piezoelectric properties of the fibers, with an improvement in scaffold wettability and increase in β-phase nucleation (translating to increased piezoelectricity) being observed. The HAp-containing scaffolds also exhibited an augmented bioactivity, with a more comprehensive surface mineralization of the fibers being obtained for the scaffolds with the highest HAp concentrations. Improved osteogenic differentiation of seeded human mesenchymal stem/stromal cells was achieved with the addition of HAp, as confirmed by an increased ALP activity, calcium deposition and upregulated expression of key osteogenic markers. Overall, our findings highlight, for the first time, the potential of combining PVDF-TrFE and HAp to develop electroactive and osteoinductive nanofibers for BTE.
Bone defects can result from different incidents such as acute trauma, infection or tumor resection. While in most instances bone healing can be achieved given the tissue's innate ability of self-repair, for critical-sized defects spontaneous regeneration is less likely to occur, therefore requiring surgical intervention. Current clinical procedures have failed to adequately address this issue. For this reason, bone tissue engineering (BTE) strategies involving the use of synthetic grafts for replacing damaged bone and promoting the tissue's regeneration are being investigated. The electrical stimulation (ES) of bone defects using direct current has yielded very promising results, with neo tissue formation being achieved in the target sites
The growing number of non-union fractures in an aging population has increased the clinical demand for tissue-engineered bone. Electrical stimulation (ES) has been described as a promising strategy for bone regeneration treatments in several clinical studies. However the underlying mechanism by which ES augments bone formation is still poorly understood and its use in bone tissue engineering (BTE) strategies is currently underexplored. Additive manufacturing (AM) technologies (Fused Deposition Modeling/3D Printing) have been widely used in BTE due to their ability to fabricate scaffolds with a high control over their structural and mechanical properties in a reproducible and scalable manner. Thus, in this work, we combined AM methods with conductive biomaterials and ES to enhance the osteogenic differentiation of human bone marrow-derived mesenchymal stem/stromal cells (hBMSCs) envisaging improved BTE strategies. First, we started by developing AM-based electro-bioreactor devices containing medical-grade electrodes (stainless steel and Ti6Al4V) to apply ES to monolayer 2D cultures and 3D cell-seeded scaffolds. Computer modeling(Finite Element Analysis-FEA) was employed to predict the magnitude/distribution of electrical fields within the ES devices and along the different conductive scaffolds. Prior to scaffold culture, 5 different ES protocols were tested in terms of their ability to promote hBMSCs proliferation and osteogenic differentiation in 2D cultures. The best performance ES protocol was then used in two different AM-based BTE strategies: 1) Two different conductive scaffolds (conductive poly lactic acid (PLA) and titanium) were seeded with hBMSCs and cultured for 21 days under osteogenic medium conditions with and without ES and their biological performance was evaluated in comparison to non-conductive standard PLA scaffolds; 2) Different PEDOT:PSS-based coating solutions were screened to obtain PEDOT:PSS/Gelatin-coated 3D polycaprolactone (PCL) scaffolds with a high(11 S.cm-1) and stable electroconductivity. When cultured under ES, PEDOT:PSS/Gelatin-PCL scaffolds enhanced significantly hBMSCs osteogenic differentiation and mineralization(calcium deposition), highlighting their potential for BTE applications.
