Objectives. The cytotoxicity induced by cobalt ions (Co. 2+. ) and cobalt nanoparticles (Co-NPs) which released following the insertion of a total hip prosthesis, has been reported. However, little is known about the underlying mechanisms. In this study, we investigate the toxic effect of Co. 2+. and Co-NPs on liver cells, and explain further the potential mechanisms. Methods. Co-NPs were characterised for size, shape, elemental analysis, and hydrodynamic diameter, and were assessed by Transmission Electron Microscope, Scanning Electron Microscope, Energy Dispersive X-ray Spectroscopy and Dynamic Light Scattering. BRL-3A cells were used in this study.
Objectives. Intra-articular injections of local anaesthetics (LA), glucocorticoids (GC), or hyaluronic acid (HA) are used to treat osteoarthritis (OA). Contrast agents (CA) are needed to prove successful intra-articular injection or aspiration, or to visualize articular structures dynamically during fluoroscopy. Tranexamic acid (TA) is used to control haemostasis and prevent excessive intra-articular bleeding. Despite their common usage, little is known about the cytotoxicity of common drugs injected into joints. Thus, the aim of our study was to investigate the effects of LA, GC, HA, CA, and TA on the viability of primary human chondrocytes and tenocytes in vitro. Methods. Human chondrocytes and tenocytes were cultured in a medium with three different drug dilutions (1:2; 1:10; 1:100). The following drugs were used to investigate cytotoxicity: lidocaine hydrochloride 1%; bupivacaine 0.5%; triamcinolone acetonide; dexamethasone 21-palmitate; TA; iodine contrast media; HA; and distilled water. Normal saline served as a control. After an incubation period of 24 hours, cell numbers and morphology were assessed. Results. Using LA or GC, especially triamcinolone acetonide, a dilution of 1:100 resulted in only a moderate reduction of viability, while a dilution of 1:10 showed significantly fewer cell counts. TA and CA reduced viability significantly at a dilution of 1:2. Higher dilutions did not affect viability. Notably, HA showed no effects of cytotoxicity in all drug dilutions. Conclusion. The toxicity of common intra-articular injectable drugs, assessed by cell viability, is mainly dependent on the dilution of the drug being tested. LA are particularly toxic, whereas HA did not affect cell viability. Cite this article: P. Busse, C. Vater, M. Stiehler, J. Nowotny, P. Kasten, H. Bretschneider, S. B. Goodman, M. Gelinsky, S. Zwingenberger.
Despite the satisfactory short-term implant survivor-ship, there is an increasing concern that the metal-on-metal hip resurfacing arthroplasty (MoMHRA) release large amount of very small wear particles and metal ions. The periprosthetic soft-tissue masses such as pseudotumours are being increasingly reported. These were found be locally destructive, requiring revision surgery in most patients. It has been suggested that either an immune reaction or cytotoxic effect of chromium(Cr) or cobalt(Co) may play a role in its aetiology. However, the effect of the phagocytosis of implant-associated metal nanoparticles on macrophages has not been elucidated. The aim of this study was to investigate the in vitro viability and proliferative response of murine macrophages to clinically relevant metal nanoparticles and ions.
At the end of day 1 and 4, two methods were used to quantify cell proliferation and viability. The AlamarBlue assay(Invitrogen) incorporates a fluorimetric growth indicator and the fluorescence signal correlates with metabolic activity of the cells. LIVE/DEAD stain kit(Molecular Probes) contains two fluorescent dyes to stain living cells green and dead cells red. The viability was calculated by the number of live cells divided by total cell numbers. Inter-group comparisons were performed using one-way ANOVA with Tukey post hoc test. Differences at p<
0.05 were considered to be significant.
Metal and their alloys have been widely used as implantable materials and prostheses in orthopaedic surgery. However, concerns exist as the metal nanoparticles released from wear of the prostheses cause clinical complications and in some cases result in catastrophic host tissue responses. The mechanism of nanotoxicity and cellular responses to wear metal nanoparticles are largely unknown. The aim of this study was to characterise macrophage phagocytosed cobalt/chromium metal nanoparticles both in vitro and in vivo, and investigate the consequent cytotoxicity. Two types of macrophage cell lines, murine RAW246.7 and human THP-1s were used for in vitro study, and tissues retrieved from pseudotumour patients caused by metal-on-metal hip resurfacing (MoMHR) were used for ex vivo observation. Transmission electron microscopy (TEM), scanning electron microscopy (SEM) in combination with backscatter, energy-disperse X-ray spectrometer (EDS), focused ion beam (FIB) were employed to characterise phagocytosed metal nanoparticles. Alamar blue assay, cell viability assays in addition to confocal microscopy in combination with imaging analysis were employed to study the cytotoxiticy in vitro. The results showed that macrophages phagocytosed cobalt and chromium nanoparticles in vitro and the phagocytosed metal particles were confirmed by backscatter SEM+EDS and FIB+EDS. these particles were toxic to macrophages at a dose dependent manner. The analysis of retrieved tissue from revision of MoMHR showed that cobalt/chromium metal nanoparticles were observed exclusively in living macrophages and fragments of dead macrophages, but they were not seen within either live or dead fibroblasts. Dead fibroblasts were associated with dead and disintegrated macrophages and were not directly in contact with metal particles; chromium but not cobalt was the predominant component remaining in tissue. We conclude that as an important type of innate immune cells and phagocytes, macrophages play a key role in metal nanoparticles related cytotoxicity. Metal nanoparticles are taken up mainly by macrophages. They corrode in an acidic environment of the phagosomes. Cobalt that is more soluble than chromium may release inside macrophages to cause death of individual nanoparticle-overloaded macrophages. It is then released into the local environment and results in death of fibroblasts and is subsequently leached from the tissue.
In orthopaedic and trauma surgery, implant-associated infections are increasingly treated with local application of antibiotics, which allows a high local drug concentration to be reached without eliciting systematic adverse effects. While ceftriaxone is a widely used antibiotic agent that has been shown to be effective against musculoskeletal infections, high local concentrations may harm the surrounding tissue. This study investigates the acute and subacute cytotoxicity of increasing ceftriaxone concentrations as well as their influence on the osteogenic differentiation of human bone progenitor cells. Human preosteoblasts were cultured in presence of different concentrations of ceftriaxone for up to 28 days and potential cytotoxic effects, cell death, metabolic activity, cell proliferation, and osteogenic differentiation were studied.Aims
Methods
Fresh frozen femoral head (FFH) allograft is commonly used in impaction grafting for revision hip arthroplasty and long term success has been demonstrated by some groups. The optimum treatment of the graft prior to impaction has not yet been determined. Some groups wash the graft prior to impaction and others do not. Washing of the graft has been shown to improve bone ingrowth in a bone chamber animal model however the reasons for this remain unclear. The aim of this study was to identify any underlying cellular cytotoxicty of fresh frozen allograft bone before and after washing. Samples of morcellised FFH allograft were taken during revision hip arthroplasties prior to impaction grafting. Paired samples, taken before and after washing were taken from each case. Washing was performed by 4 consecutive washes in 300ml warmed saline, the bone being filtered between each exchange of saline. Cytotox-icity was assessed for all samples using both contact and extract assays. Contact assays involved culture of cell lines in direct contact with bone samples. Extract assays utilised culture media conditioned with bone samples and subsequent quantitative assessment of cell metabolism and viability using both dimethylthiazol (MTT) and neutral red (NR) assays. All assays were performed using both human osteoblastic (MG63) and fibroblastic (HSF) cell lines. Nine pairs of samples were analysed for cytotoxicity using both cell lines. Contact assays demonstrated a clear zone of cellular inhibition around the unwashed bone samples. Extract assays were performed in triplicate for each cell type and both MTT and NR assays giving 108 paired assay results. 88.9% of pairs (92/108) showed cytotoxicity in the unwashed sample. No washed samples demonstrated cytotoxicity. When grouped by assay and cell type, analysis of means showed statistically significant differences between washed and unwashed samples in MG63-NR (p=0.0025), HSF-NR (p=0.0004) and MG63-MTT (p=0.008). The difference observed in the HSF-MTT assays did not reach statistical signifi-cance (p=0.06). In conclusion, we have shown that unwashed FFH allograft can be cytotoxic to human osteoblastic and fibroblastic cell lines in vitro. This suggests that allograft should be washed prior to impaction in order to optimise the biological compatibility.
Little information exists when using cell viability assays to evaluate cells within whole tissue, particularly specific types such as the intervertebral disc (IVD). When comparing the reported methodologies and the protocols issued by manufacturers, the processing, working times, and dye concentrations vary significantly, making the assay's reproducibility a costly and time-consuming trial and error process. This study aims to develop a detailed step-by-step cell viability assay protocol for evaluating IVD tissue. IVDs were harvested from bovine tails (n=8) and processed at day 0 and after 7 days of culture. Nucleus pulposus (NP) and the annulus fibrosus (AF) 3 mm cuts were incubated at room temperature (26˚C) with a Viability/
Aim. Prosthetic joint infections pose a major clinical challenge. Developing novel material surface technologies for orthopedic implants that prevent bacterial adhesion and biofilm formation is essential. Antimicrobial coatings applicable to articulating implant surfaces are limited, due to the articulation mechanics inducing wear, coating degradation, and toxic particle release. Noble metals are known for their antimicrobial activity and high mechanical strength and could be a viable coating alternative for orthopaedic implants [1]. In this study, the potential of thin platinum-based metal alloy coatings was developed, characterized, and tested on cytotoxicity and antibacterial properties. Method. Three platinum-based metal alloy coatings were sputter-coated on medical-grade polished titanium discs. The coatings were characterized using optical topography and scanning electron microscopy with energy dispersive spectroscopy (SEM/EDS). Ion release was measured using inductively coupled plasma optical emission spectrometry (ICP-OES).
Aim. Antibacterial activity of coatings based on metal and metal oxide nanoparticles (NPs) often depends on materials and biotic targets resulting in a material-specific killing activity of selected Gram-positive and Gram-negative bacteria, including drug-resistant strains. In this perspective, the NPs loading amount, the relative elemental concentration inside the nanogranular building blocks and the deposition method are of paramount importance when the goal is to widen the antimicrobial spectrum, but at the same time to avoid high levels of metal content to limit undesired toxic effects. Aim of the present study was evaluation of the antimicrobial properties of two multielement nanogranular coatings composed of Titanium-Silver and Copper and of Magnesium-Silver and Copper. Method. Ti-Ag-Cu and Mg-Ag-Cu NPs were deposited on circular cover glasses (VWR) by Supersonic Cluster Beam Deposition. Biofilm-producer strains of Staphylococcus aureus (methicillin susceptible and resistant), Staphylococcus epidermidis (methicillin susceptible and resistant), Escherichia coli (fully susceptible and producer of extended spectrum beta lactamases), and Pseudomonas aeruginosa (susceptible and multidrug-resistant) were selected. The abilities of the selected strains to adhere, colonize and produce biofilm on the discs coated with Ti-Ag-Cu or Mg-Ag-Cu NPs were compared to uncoated circular cover glasses which were used as growth control.
Aim. Implant-associated infection usually require prolonged treatment or even removal of the implant. Local application of antibiotics is used commonly in orthopaedic and trauma surgery, as it allows reaching higher concentration in the affected compartment, while at the same time reducing systematic side effects. Ceftriaxone release from calcium sulphate has a particularly interesting, near-constant release profile in vitro, making it an interesting drug for clinical application. Purpose of the present study was to investigate the potential cytotoxicity of different ceftriaxone concentrations and their influence on osteogenic differentiation of human pre-osteoblasts. Method. Human pre-osteoblasts were cultured up to 28 days in different ceftriaxone concentrations, ranging between 0 mg/L and 50’000 mg/L.
Introduction and Objective. Regeneration of cartilage injuries is greatly limited. Therefore, cartilage injuries are often the starting point for later osteoarthritis. In the past, various bioactive glass (BG) scaffolds have been developed to promote bone healing. Due to the fact that they induce the deposition of hydroxyapatite (HA) -the main component of bone matrix, these BG types are not suitable for chondrogenesis. Hence, a novel BG (Car12N) lacking HA formation, was established. Since BG are generally brittle the combination with polymers is helpful to achieve suitable biomechanic stability. The aim of this interdisciplinary project was to investigate the effects of biodegradable polymer Poly(D,L-lactide-co-glycolide) (PLLA) infiltration into a Car12N scaffold for cartilage tissue engineering. Materials and Methods. BG scaffolds were infiltrated with PLLA using phase separation within a solvent. Pure BG Car12N scaffolds served as control. To assess whether the polymer was homogeneously distributed the polymer to glass ratio and pore contents in the upper, middle and lower third of the scaffolds were examined by light microscopy. For a more precise characterization of the scaffold topology, the glass strut length, the glass strut diameter and the pore circumference were also measured. Leaching tests in 0.1M HCl solution over 8 days were used to allow a gel layer formation on the scaffolds surface. Non-leached and leached scaffolds were subjected to strength testing.
Introduction and Objective. Guided Bone Regeneration (GBR) uses biodegradable collagen membranes of animal origin tissues (dermis and pericardium). Their barrier effect prevents soft tissues to interfere with the regeneration of alveolar bone. However, their xenogeneic origin involves heavy chemical treatments which impact their bioactivity. Wharton's Jelly (WJ) from the umbilical cord is a recoverable surgery waste. WJ is mostly made from collagen fibers, proteoglycans, hyaluronic acid, and growth factors. WJ with immunologically privileged status and bioactive properties lends credence to its use as an allograft. Nevertheless, low mechanical properties limit its use in bone regenerative strategies. Herein, our objective is to develop a crosslinked WJ-based membrane to improve its strength and thus its potential use as a GBR membrane. Materials and Methods. The umbilical cords are collected after delivery and then stored at −20°C until use. The WJ membranes (1 × 5 × 12 mm) were obtained after the removal of blood vessels and amniotic tissue, washed, lyophilized, and stored at −20°C. WJ membranes were incubated in genipin solutions in decreasing concentrations (0.3 g / 100 mL − 0.03 g / 100 mL) for 24 hours at 37°C. The crosslinking degree was estimated by ninhydrin and confirmed by FTIR (Fourier-transform infrared spectroscopy) assays. The swelling rate was obtained after the rehydration of dry crosslinked WJ-membrane for 10 min in D-PBS. The mechanical properties were assessed in hydrated conditions on a tensile bench. The resistance to the degradation was evaluated by collagenase digestion (1 mg/mL for 60 hours) assay. The cytotoxicity of crosslinked WJ-membrane was evaluated in accordance with the standard ISO.10993-5 (i.e. Mitochondrial activity and Lactate Dehydrogenase release) against Mesenchymal Stem Cells (MSCs). Finally, the MSCs colonization and proliferation were followed after 21 days of culture on crosslinked WJ-membranes. Results. The increase of crosslinking rates from 30% to 90% of the WJ membrane was demonstrated by the ninhydrin assay. FTIR analysis showed a prominent peak at 1732 cm. -1. , confirming the incorporation of genipin in the WJ. The swelling rate of crosslinked WJ-membrane decreased with an increase of the crosslinking rate. An increase in elastic modulus and an increase in the resistance to the collagenase degradation were observed along with an increase in the crosslinking degree.
Direct metal printed (DMP) porous iron implants possess promising mechanical and corrosion properties for various clinical application. Nevertheless, there is a requirement for better co-relation between in vitro and in vivo corrosion and biocompatibility behaviour of such biomaterials. Our present study evaluates absorption of porous iron implants under both static and dynamic conditions. Furthermore, this study characterizes their cytocompatibility using fibroblastic, osteogenic, endothelial and macrophagic cell types. In vitro degradation was performed statically and dynamically in a custom-built set-up placed under cell culture conditions (37 °C, 5% CO2 and 20% O2) for 28 days. The morphology and composition of the degradation products were analysed by scanning electron microscopy (SEM, JSM-IT100, JEOL). Iron implants before and after immersion were imaged by μCT (Quantum FX, Perkin Elmer, USA). Biocompatibility was also evaluated under static and dynamic in vitro culture conditions using L929, MG-63, HUVEC and RAW 264.7 cell lines. According to ISO 10993, cytocompatibility was evaluated directly using live/dead staining (Live and Dead Cell Assay kit, Abcam) in dual channel fluorescent optical imaging (FOI) and additionally quantified by flow cytometry. Furthermore, cytotoxicity was indirectly quantified using ISO conform extracts in proliferation assays. Strut size of DMP porous iron implants was 420 microns, with a porosity of 64% ± 0.2% as measured by micro-CT. After 28 days of physiological degradation in vitro, dynamically tested samples were covered with brownish degradation products. They revealed a 5.7- fold higher weight loss than statically tested samples, without significant changes in medium pH. Mechanical properties (E = 1600–1800 MPa) of these additively manufactured implants were still within the range of the values reported for trabecular bone, even after 28 days of biodegradation. Less than 25% cytotoxicity at 85% of the investigated time points was measured with L929 cells, while MG-63 and HUVEC cells showed 75% and 60% viability, respectively, after 24 h, with a decreasing trend with longer incubations.
Introduction. According to American Joint Replacement Registry, particle mediated osteolysis represents 13 % of the knee revision surgeries performed in the United States. The comprehension of mechanical and wear properties of materials envisioned for TJR is a key step in product development. Furthermore, the maintenance of UHMWPE mechanical properties after material modification is an important aspect of material success. Initial studies conducted by our research group demonstrated that the incorporation of ibuprofen in UHMWPE had a minor impact on UHMWPE physicochemical and mechanical properties. Drug release was also evaluated and resulted in an interesting profile as a material to be used as an anti-inflammatory system. Therefore, the present study investigated the effect of drug release on the mechanical and biological properties of ibuprofen-loaded UHMWPE. Experimental. UHMWPE resin GUR 1020 from Ticona was for sample preparation. Samples with drug concentrations of 3% and 5% wt were consolidated as well as samples without anti-inflammatory addition through compression molding at 150 °C and 5 MPa for 15 minutes. Mechanical properties were evaluated via the tensile strength experiment (ASTM D638) and dynamic mechanic tests. Wear resistance was measured using the pin on disc (POD) apparatus. Finally, cytotoxicity analysis was conducted based on ISO 10993–5. Results. Dynamic-mechanic analysis demonstrated no difference in flexion modulus and stress for all materials (Table 1). No difference was also verified during cyclical loading experiments (Table 1), which indicates that the drug concentration added to material composition did not affect these properties. POD experiments were proposed to evaluate wear resistance of ibuprofen-loaded UHMWPE samples considering the combination of materials similar to those employed in TJR. Results from POD tests are presented in Table 1. Volumetric wear was close to zero for all samples after 200 thousand cycles. Comprehension of the effect of drug release on mechanical properties is essential to estimate how the material will behave after implantation. Therefore, mechanical properties were assessed after 30 days of ibuprofen release and the results were compared with those obtained in samples as prepared (Table 2). Initial results demonstrated a decrease in elastic modulus in samples prepared with ibuprofen. However, no difference was verified between UHMWPE, UHMWPE 3% IBU and UHMWPE 5% IBU after ibuprofen release. Finally, cell viability of UHMWPE 3% IBU and UHMWPE 5% was found to be superior to 100% (Figure 1). Therefore, both materials can be considered nontoxic. Conclusions. Ibuprofen-loaded UHMWPE did not demonstrate a significant influence on the mechanical and biological behavior of UHMWPE. Dynamic-mechanical tests demonstrated constancy for all samples under analysis. Wear testing resulted in gravimetric wear close to zero, for all tested materials. Mechanical properties conducted after 30 days of ibuprofen release also had a positive outcome. Although presenting a difference in modulus prior and after release tests, modulus and tensile yield stress remained inside acceptable range indicated to UHMWPE used in orthopedic implants. Furthermore, after drug elution UHMWPE 3% IBU and UHMWPE 5% IBU recovered original UHMWPE properties.
Biodegradable metals as orthopaedic implant materials receive substantial scientific and clinical interest. Marketed cardiovascular products confirm good biocompatibility of iron. Solid iron biodegrades slowly in vivo and has got supra-physiological mechanical properties as compared to bone and porous implants can be optimized for specific orthopaedic applications. We used Direct Metal Printing (DMP)3 to additively manufacture (AM) scaffolds of pure iron with fine-tuned bone-mimetic mechanical properties and improved degradation behavior to characterize their biocompatibility under static and dynamic 3D culture conditions using a spectrum of different cell types. Atomized iron powder was used to manufacture scaffolds with a repetitive diamond unit cell design on a ProX DMP 320 (Layerwise/3D Systems, Belgium). Mechanical characterization (Instron machine with a 10kN load cell, ISO 13314: 2011), degradation behavior under static and dynamic conditions (37ºC, 5% CO2 and 20% O2) for up of 28 days, with μCT as well as SEM/energy-dispersive X-ray spectroscopy (EDS) (SEM, JSM-IT100, JEOL) monitoring under in vivo-like conditions. Biocompatibility was comprehensively evaluated using a broader spectrum of human cells according to ISO 10993 guidelines, with topographically identical titanium (Ti-6Al-4V, Ti64) specimen as reference.
Bioactive functional scaffolds are essential for support of cell-based strategies to improve bone regeneration. Adipose-tissue-derived-stromal-cells (ASC) are more accessible multipotent cells with faster proliferation than bone-marrow-derived-stromal-cells (BMSC) having potential to replace BMSC for therapeutic stimulation of bone-defect healing. Their osteogenic potential is, however lower compared to BMSC, a deficit that may be overcome in growth factor-rich orthotopic bone defects with enhanced bone-conductive scaffolds. Objective of this study was to compare the therapeutic potency of human ASC and BMSC for bone regeneration on a novel nanoparticulate β-TCP/collagen-carrier (β-TNC).
The ideal bone substituting biomaterials should possess bone-mimicking mechanical properties; have of porous interconnected structure, and adequate biodegradation behaviour to enable full recovery of bony defects. Direct metal printed porous scaffolds hold potential to satisfy all these requirements and were additively manufactured (AM) from atomized WE43 magnesium alloy powder with grain sizes between 20 and 60 μm. Their micro-structure, mechanical properties, degradation behavior and biocompatibility was then evaluated in vitro. Firstly, post-processing values nicely followed design parameters. Next, Young's moduli were similar to that of trabecular bone (i.e., E = 700–800 MPa) even after 28 days of simulated in vivo-like corrosion by in vitro immersion. Also, a relatively moderate hydrogen evolution, corresponding to a calculated 19.2% of scaffold mass loss, was in good agreement with 20.7% volume reduction as derived from reconstructed μCT images. Finally, only moderate cytotoxicity (i.e., level 0, <25%), even after extensive ISO 10993-conform testing for 72 h using MG-63 cells, was determined using WE43 extracts (2 way ANOVA, post-hoc Tukey's multiple comparisons test; α = 0.05).
Introduction. Ultra-high molecular weight polyethylene (UHMWPE) can provide local sustained delivery of therapeutics. 1,2. For example, it can deliver analgesics to address post-arthroplasty pain. 2. Given that several analgesics, such as bupivacaine (anesthetic) and tolfenamic acid (NSAID), were shown to possess antibacterial activity against Staphylococci, we hypothesize that analgesic-loaded UHMWPE can also yield antimicrobial effects, preventing the development of periprosthetic joint infections. Methods. Bupivacaine and tolfenamic acid were incorporated into UHMWPE via phase-separated compression molding. Drug release from the prepared samples was measured using high-performance liquid chromatography. Antibacterial studies of the obtained materials were conducted against methicillin-sensitive, and methicillin-resistant S. aureus, as well as S. epidermidis. Time-kill curves were obtained to characterize antimicrobial activity against planktonic bacteria. The dynamics of bacterial adhesion were assessed to characterize antibiofilm activity. Scanning electron microscopy (SEM) was used to visualize adherent bacteria. Anticolonizing activity of the tested materials was characterized using the “daughter cell” method as outlined elsewhere. 3.
Introduction. The use of irrigation solution during surgical procedures is a common and effective practice in reduction of bioburden and the risk of subsequent infection. The optimal irrigation solution to accomplish this feat remains unknown. Many surgeons commonly add topical antibiotics to irrigation solutions assuming this has topical effect and eliminates bacteria. The latter reasoning has never been proven. In fact a few prior studies suggest addition of antibiotics to irrigation solution confers no added benefit. Furthermore, this practice adds to cost, has the potential for anaphylactic reactions, and may also contribute to the emergence of antimicrobial resistance. We therefore sought to compare the antimicrobial efficacy and cytotoxicity of irrigation solution containing polymyxin-bacitracin versus other commonly used irrigation solutions. Methods. Using two in vitro breakpoint assays of Staphylococcus aureus (ATCC#25923) and Escherichia coli (ATCC#25922), we examined the efficacy of a panel of irrigation solutions containing topical antibiotics (500,000U/L Polymyxin-Bacitracin 50,000U/L; Vancomycin 1g/L; Gentamicin 80mg/L), as well as commonly used irrigation solutions (Normal saline 0.9%; Povidone-iodine 0.3%; Chlorhexidine 0.05%; Castile soap 0.45%; and Sodium hypochlorite 0.125%) following 1 minute and 3 minutes of exposure. Surviving bacteria were counted in triplicate experiments. Failure to eradicate all bacteria was considered to be “not effective” for that respective solution and exposure time.