Polypropylene (PPE) synthetic mesh is increasingly used in knee arthroplasty surgery to salvage a disrupted extensor mechanism. Despite its clinical success, it is associated with a high rate of periprosthetic joint infection (PJI), which is hypothesized to be caused by bacterial biofilm. The purpose of the current study is to describe the progression of PPE-based biofilm formation over time and to determine if intraoperative antiseptic solutions could be used to effectively remove biofilm when treating PJI. Commercially available knotted monofilament PPE mesh1 was cut into 10mm circular shape, immersed in tryptic soy broth (TSB) with methicillin-sensitive staphylococcus aureus and cultured individually in 48-well plates for 10 days to elucidate the biofilm grown on mesh over time. At every 24 hours, a triplicate of samples was retrieved and biofilm on the mesh was dislodged by sonicating at 52 kHz for 15 minutes and quantified by counting colony-forming units (CFUs) after overnight growth. The biofilm growth was also verified using scanning electron microscopy. The effect of saline and antiseptic solutions was verified by exposing 1) 0.05% chlorohexidine gluconate2, 2) acetic acid-based mixture3, 3) diluted povidone-iodine (0.35%), 4) undiluted povidone-iodine (10%)4, and 5) 1:1 combination of 10% povidone-iodine & 3% hydrogen peroxide on immature and mature biofilms for 3 minutes, created by culturing with bacteria for 24 hours and 72 hours respectively. All experiments were performed in quintuples and repeated. Antiseptic treatments that produced a three-log reduction in CFU counts compared to controls were considered clinically significant.Aim
Method