Abstract
Background
The advent of highly cross-linked polyethylene has resulted in improved wear rates and reduced osteolysis with at least intermediate follow-up when compared to conventional polyethylene. However, the role of alternative femoral head bearing materials in decreasing wear is less clear. The purpose of this study was to determine in-vivo polyethylene wear rates across ceramic, Oxinium, and cobalt chrome femoral head articulations.
Methods
A review of our institutional database was performed to identify patients who underwent a total hip arthroplasty using either ceramic or oxidized zirconium (Oxinium) femoral head components on highly cross-linked polyethylene between 2008 and 2011. These patients were then matched on implant type, age, sex and BMI with patients who had a cobalt chrome bearing implant during the same time period. RSA analysis was performed using the center index method to measure femoral head penetration (polyethylene wear). Secondary quality of life outcomes were collected using WOMAC and HHS Scores. Paired analyses were performed to detect differences in wear rate (mm/year) between the cobalt chrome cohorts and their matched ceramic and Oxinium cohorts. Additional independent group comparisons were performed by analysis of variance with the control groups collapsed to determine wear rate differences between all three cohorts.
Results
A total of 75 patients underwent RSA analysis. 20 patients with a ceramic femoral head component and 16 patients with an Oxinium femoral head component along with the same number of matched patients with cobalt chrome femoral head component were included in the analysis. The time in vivo for the Oxinium (5.17 +/− 0.96 years), Oxinium matched cohort (5.13 +/− 0.72 years), ceramic (5.15 +/− 0.76 years) and ceramic matched cohort (5.36 +/− 0.63 years) were comparable. The demographics of all bearing surface cohorts were similar. The paired comparison between the Oxinium and cobalt chrome cohorts (0.32 vs. 0.28 mm/year, p=0.427) and ceramic vs cobalt chrome cohorts (0.28 vs. 0.22 mm/year, p=0.202) did not demonstrate a significant difference in wear rate. The independent groups analysis revealed a significantly higher wear rate of Oxinium (0.33 mm/year) compared to cobalt chrome (0.24 mm/year) (p = 0. 038). There were no differences in HHS and WOMAC scores between the Oxinium and cobalt chrome cohorts (HHS: p = 0.71, WOMAC: p=0.08) or the ceramic and cobalt chrome cohorts (HHS: p=0.15, WOMAC: p =023).
Conclusion
This study presents evidence of a greater wear rate (mm/year) of the Oxinium femoral head component compared to a cobalt chrome femoral head component. This difference was not demonstrated in the ceramic femoral head component. Despite this difference, there were no clinical differences as measured by the HHS and WOMAC. Future research should focus on factors that may contribute to the higher wear rate seen in the Oxinium cohort.
Level of Evidence – Level II
Disclosures - Institutional support provided by Depuy, Stryker, and Smith and Nephew.