Abstract
Studies that have previously examined the relationship between inclination angle and polyethylene wear have shown increased wear of conventional polyethylene with high inclination angles. To date, there have been no long term in vivo studies examining the correlation between cup position and polyethylene wear with highly crosslinked polyethylene.
An institutional arthroplasty database was used to identify patients who had metal-on-highly crosslinked polyethylene primary total hip arthroplasty (THA) using the same component design with a minimum follow up of 10 years ago. A modified RSA examination setup was utilised, recreating standard anteroposterior (AP) and cross-table lateral exams in a single biplane RSA acquisition. Three dimensional head penetration was measured using the centre index method. The same radiographs were used to measure inclination angle and anteversion. Spearman correlation was used to show an association between the parameters of acetabular position and wear rate.
A total of 43 hips were included for analysis in this study. Average follow-up was 12.3 ± 1.2 years. The average linear wear rate was calculated to be 0.066 ± 0.066 mm/year. Inclination angle was not correlated with polyethylene wear rate (p=0.82). Anteversion was also not correlated with polyethylene wear rate (p=0.11). There was no statistical difference between wear rates of hips within Lewinnek's “safe zone” and those outside this “safe zone” (p=0.11). Males had a higher wear rate of 0.094 ± 0.089 mm/year compared to females with a wear rate of 0.046 ± 0.032 mm/year (p=0.045).
At long term follow up of greater than 10 years, highly cross linked polyethylene has very low wear rates. This excellent tribology is independent of acetabular position, but gender did impact wear rates. Due to the low wear rates, follow-up of even longer term is suggested to examine variables affecting wear.