Abstract
Ultra-high molecular weight polyethylene (UHMWPE) is the sole polymeric material currently used for weight-bearing surfaces in total joint arthroplasty. However, the wear phenomenon of UHMWPE components in knee and hip prostheses after total joint arthroplasty is one of the major restriction factors on the longevity of these implants. In order to minimize the wear of UHMWPE and to improve the longevity of artificial joints, it is necessary to clarify the factors influencing the wear mechanism of UHMWPE. In the microscopic surface observation of the virgin knee prosthesis with anatomical design, various grades of microscopic surface scratches and defects caused by machining and surface finishing processes during manufacture of the component were observed on the surface of the metallic femoral component [Fig. 1] (C. Cho et al, 2009), although the overall surface were finished at smoother level. It is thought that certain levels of the microscopic surface asperities caused by these surface damages in the metallic femoral component might contribute to increasing and/or accelerating wear of the UHMWPE tibial insert. Therefore, it is necessary to clarify quantitatively the influence of the microscopic surface asperities of the metallic components in virgin artificial joints on the wear of UHMWPE components.
The primary purpose of this study was to investigate the influence of the microscopic surface asperities of the virgin metallic femoral component on the wear of the UHMWPE tibial insert in the virgin knee prosthesis. In this study, the authors focused on the three-dimensional shape of the microscopic surface asperities as a factor influencing the wear mechanism of the UHMWPE tibial insert. The 3D microscopic surface profile measurement of the virgin metallic femoral component using a laser microscope and reproduction of the femoral component surface using 3D CAD software were performed [Fig. 2] in order to produce idealized 3D finite element models of the microscopic surface asperity of the femoral component based on actual measurement data. Elasto-plastic finite element contact analyses between idealized microscopic surface asperities and UHMWPE were also performed in order to investigate the influence of the three-dimensional shape of the microscopic surface asperities of the virgin metallic femoral component on the wear of the UHMWPE tibial insert. The analytical findings of this study suggest that the aspect ratio and shape ratio [Fig. 3] of the microscopic surface asperity of the virgin metallic femoral component have an important influence on increasing and/or accelerating wear of the UHMWPE tibial insert.