Abstract
The leading cause for total hip arthroplasty (THA) revision remains aseptic loosening due to bearing wear. The younger and more active patients currently undergoing arthroplasty present unprecedented demands on THA-bearings. Ceramic-on-ceramic (CoC) bearings have consistently shown the lowest wear rates. The recent advances, especially in alumina CoC bearings, have solved many past problems and produced preferable results in vitro.
Alumina ceramics are extremely hard, scratch resistant, biocompatible, offer a low coefficient of friction, superior lubrication and lower wear rates in comparison to other bearings in THA. The major disadvantage of ceramics used to be fracture. The new generation of alumina ceramics, has reduced the risk of ball fracture to 0.03–0.05%. The risk for liner fracture is even lower.
Assuming an impingement-free component implantation, CoC bearings have major advantages over other bearing combinations. Due to the superior hardness, CoC bearings produce less third body wear and are virtually impervious to damage from instruments during the implantation process.
A complication specific to CoC bearings is squeaking. Squeaking occurs if the friction in the joint articulation is sufficient to excite vibrations to audible magnitudes (due to loss of lubrication). The high range of reported squeaking (0.45% to 10.7%) highlights the importance of correct implant position. If a correct implant position can be guaranteed, then squeaking is rare and without clinical significance.
The improved tribology and presumable resulting implant longevity make CoC the bearing of choice for young and active patients. Especially the alumina matrix (Biolox delta) offers increased burst strength and greater fracture toughness.