Abstract
Cemented total hip arthroplasty has become an extremely successful operation with excellent long term results. Although showing decreasing popularity in North America, it always remained a popular choice for the elderly patients in Europe and other parts of the world. Besides optimal component orientation, a proper cementing technique is of major importance to assure longevity of implant fixation. Consequently a meticulous bone bed preparation assures the mechanical interlock between the implant component, cement and the final bone bed.
Cementing the acetabular side should include preservation of the transverse acetabular ligament and clear identification of the medial wall. Medialisation and deepening of the socket are important at reaming, to ensure a containment of the cup. The contact of the cup to cancellous bone should be maximised. Either smaller reamers or 4–6mm anchoring holes can be drilled to the superior sclerosis. Smaller defects can be curettage, while larger ones might require cancellous bone grafting. Of major importance is the thoroughly pulsatile jet lavage with saline to irrigate the cancellous bone bed, to reduce fat and blood lamination. After final irrigation, before cementation, dry sponges are slightly impacted into the cavity, to dry it out. Cementation usually requires 40g of high viscosity bone cement. Immediate pressurisation of the cement into the bone bed should start after a general application time in our institution between 2.5 to 3 minutes after mixing; with either a sterile glove filled with a sponge or designated company specific pressuriser. Sustained pressurisation should be done for 1 minute. The original cup should be 3–4mm smaller than the last reamer, to ensure circumferential cement mantle. Insertion principle includes medialisation first, followed by gradual angulation of the cup. In appropriate position, a balled pressuriser maintains pressure without further moving of the implant, until cement hardening. Remnant cement can be removed with osteotomes, while remaining osteophytes should be flush with implant.
Femoral Side: First the fossa pyriformis should be clearly identified, including the posterolateral entry point of the prosthesis. The femoral neck cut is usually 1.5–2cm above the minor trochanter, based on the preoperative planning and implant type. Opening of the canal is done with an awl or osteotome, followed by any blunt tipped instrument, to follow the intramedullary direction. A box osteotome opens the lateral portion of the femoral neck, gently to preserve as much cancellous bone as possible. Sequential broaching follows carefully and according to the planning, to ensure preservation of 2–3mm cancellous bone for interdigitation. Some systems might require over-broaching by one size. Trialing is done with the broach. Following, irrigation using a long nozzle pulsatile lavage, reduces the chance for fat embolism. A cement restrictor is then placed 1.5–2cm distal to the tip of the stem, to ensure an adequate cement mantle distally. A second complete pulsatile irrigation of the canal follows, to minimise bleeding, followed by a dry sponge. Cement mixing is vacuum based in the meantime, usually 60–80g. We prefer the use of low dose antibiotic laden cement in our set up. Two to three minutes after mixing, the cement is applied rapidly in a retrograde technique with a cement gun, placing the nozzle tip against the cement restrictor. The gun is “pushed” out during the application, rather than being withdrawn from the canal. Proximal pressurisation is first done by thumb, then with a proximal seal for 1 minute. The stem is inserted slowly using steady manual pressure, in the center of the cement mantle, however, should never be impacted. The stem is aligned with the previously defined lateral entry point and is held in position until the cement hardens. The desired outcome is a cement interdigitation into cancellous bone for 2–3mm and an additional mantle of 2mm pure cement.
