Abstract
The Exeter Stem (Howmedica, UK) has been in use for over 35 years. Over the years it has undergone several modifications with the most recent being a highly polished, tapered stem in 1986. The manufacturers quote a rate of 0.0006%. In the current literature there are 16 (or less) instances of fractures of the Orthinox stem.
We present a case of fracture of an Orthinox Exeter Stem 9 years after insertion.
Our patient, BB, presented, aged 62, with symptoms & signs consistent with OA right hip. THR was performed through a lateral approach utilising a trochanteric osteotomy. A size 0 37.5 stem was inserted. Radiographs were very satisfactory. She suffered a post operative DVT/PTE from which she recovered uneventfully. She was independently mobile at 6 month review and was discharged at the 2 year stage pain free.
Aged 71, BB presented to outpatient clinic with a several month history of generalised groin pain. She had a Trendelenberg gait. Considerable pain was experienced on axial compression of the limb. Radiographs revealed a midstem fracture with cement loosening proximally. No trauma was reported. She underwent revision surgery through a posterior approach. Acetabular component was rigidly fixed. This was revised to a pressfit Trident (Zimmer, UK) cup with screws & polyethylene liner. An extended trochanteric osteotomy was used to remove the broken stem. An uncemented Restoration (Stryker, UK) stem was inserted with a 28mm head. Post-operative recovery was unremarkable and at 6 months osteotomy has healed. The stem was sent to Stryker UK Laboratories for analysis. They reported the stem broke in fatigue with the origin on the antero-lateral surface. No material or manufacturing defects seen. Dimensionally correct. Fracture may be due to abnormal bending stresses secondary to proximal loosening and firm distal fixation.
Our case demonstrates a set of circumstances that led to inevitable fatigue and stem fracture. The method of failure should reinforce the radiograph appearances that may cause concern or be acted upon.